• W1987177509 abstract "Al2O3/Ni nano composites were prepared from NiAl2O4 spinel by in situ reaction sintering method. The starting materials of Al2O3–NiO powder were synthesized by thermal decomposition of precipitates prepared from aluminum sulfate and nickel sulfate. The specific surface area of the Al2O3–NiO powder was >36 m2/g. The Al2O3/Ni composites were obtained by firing the starting material buried in a carbon bed at 1500 °C for 1 h. The resulting Al2O3/Ni composites have relative densities >96% (0–40 mol% Ni). Nickel grains dispersed homogeneously in the microstructure, accounting for 10% of within the grains and 90% at grain boundaries. The average particle size of the former nickel grains was 150 nm while that of the latter grains was 300 nm. The maximum three-point bending strength was 408 MPa at 10 mol% Ni sample and the maximum fracture toughness was 9.9 MPa m1/2 at 40 mol% Ni sample. The Vickers hardness decreased slightly with increasing Ni content and this change is in good agreement with individual mixture rule." @default.
• W1987177509 created "2016-06-24" @default.
• W1987177509 creator A5030213215 @default.
• W1987177509 creator A5037413611 @default.
• W1987177509 creator A5054075534 @default.
• W1987177509 creator A5068667478 @default.
• W1987177509 creator A5072950026 @default.
• W1987177509 creator A5089202025 @default.
• W1987177509 date "2007-09-01" @default.
• W1987177509 modified "2023-10-16" @default.
• W1987177509 title "Preparation and properties of Al2O3/Ni composite from NiAl2O4 spinel by in situ reaction sintering method" @default.
• W1987177509 cites W1970799826 @default.
• W1987177509 cites W1975560238 @default.
• W1987177509 cites W1981854827 @default.
• W1987177509 cites W1988552983 @default.
• W1987177509 cites W2007114089 @default.
• W1987177509 cites W2017653664 @default.
• W1987177509 cites W2028227817 @default.
• W1987177509 cites W2029129551 @default.
• W1987177509 cites W2035425818 @default.
• W1987177509 cites W2040830093 @default.
• W1987177509 cites W2046658745 @default.
• W1987177509 cites W2052648260 @default.
• W1987177509 cites W2081453467 @default.
• W1987177509 cites W2326340304 @default.
• W1987177509 doi "https://doi.org/10.1016/j.ceramint.2006.03.027" @default.
• W1987177509 hasPublicationYear "2007" @default.
• W1987177509 type Work @default.
• W1987177509 sameAs 1987177509 @default.
• W1987177509 citedByCount "26" @default.
• W1987177509 countsByYear W19871775092013 @default.
• W1987177509 countsByYear W19871775092014 @default.
• W1987177509 countsByYear W19871775092015 @default.
• W1987177509 countsByYear W19871775092020 @default.
• W1987177509 countsByYear W19871775092021 @default.
• W1987177509 countsByYear W19871775092022 @default.
• W1987177509 countsByYear W19871775092023 @default.
• W1987177509 crossrefType "journal-article" @default.
• W1987177509 hasAuthorship W1987177509A5030213215 @default.
• W1987177509 hasAuthorship W1987177509A5037413611 @default.
• W1987177509 hasAuthorship W1987177509A5054075534 @default.
• W1987177509 hasAuthorship W1987177509A5068667478 @default.
• W1987177509 hasAuthorship W1987177509A5072950026 @default.
• W1987177509 hasAuthorship W1987177509A5089202025 @default.
• W1987177509 hasConcept C104779481 @default.
• W1987177509 hasConcept C127413603 @default.
• W1987177509 hasConcept C133392424 @default.
• W1987177509 hasConcept C159985019 @default.
• W1987177509 hasConcept C161790260 @default.
• W1987177509 hasConcept C185592680 @default.
• W1987177509 hasConcept C187530423 @default.
• W1987177509 hasConcept C191897082 @default.
• W1987177509 hasConcept C192191005 @default.
• W1987177509 hasConcept C192562407 @default.
• W1987177509 hasConcept C2776230739 @default.
• W1987177509 hasConcept C2777581544 @default.
• W1987177509 hasConcept C42360764 @default.
• W1987177509 hasConcept C504270822 @default.
• W1987177509 hasConcept C55493867 @default.
• W1987177509 hasConcept C74575197 @default.
• W1987177509 hasConcept C82455628 @default.
• W1987177509 hasConcept C87976508 @default.
• W1987177509 hasConcept C97549433 @default.
• W1987177509 hasConceptScore W1987177509C104779481 @default.
• W1987177509 hasConceptScore W1987177509C127413603 @default.
• W1987177509 hasConceptScore W1987177509C133392424 @default.
• W1987177509 hasConceptScore W1987177509C159985019 @default.
• W1987177509 hasConceptScore W1987177509C161790260 @default.
• W1987177509 hasConceptScore W1987177509C185592680 @default.
• W1987177509 hasConceptScore W1987177509C187530423 @default.
• W1987177509 hasConceptScore W1987177509C191897082 @default.
• W1987177509 hasConceptScore W1987177509C192191005 @default.
• W1987177509 hasConceptScore W1987177509C192562407 @default.
• W1987177509 hasConceptScore W1987177509C2776230739 @default.
• W1987177509 hasConceptScore W1987177509C2777581544 @default.
• W1987177509 hasConceptScore W1987177509C42360764 @default.
• W1987177509 hasConceptScore W1987177509C504270822 @default.
• W1987177509 hasConceptScore W1987177509C55493867 @default.
• W1987177509 hasConceptScore W1987177509C74575197 @default.
• W1987177509 hasConceptScore W1987177509C82455628 @default.
• W1987177509 hasConceptScore W1987177509C87976508 @default.
• W1987177509 hasConceptScore W1987177509C97549433 @default.
• W1987177509 hasIssue "7" @default.
• W1987177509 hasLocation W19871775091 @default.
• W1987177509 hasOpenAccess W1987177509 @default.
• W1987177509 hasPrimaryLocation W19871775091 @default.
• W1987177509 hasRelatedWork W2042576283 @default.
• W1987177509 hasRelatedWork W2370800422 @default.
• W1987177509 hasRelatedWork W2902107089 @default.
• W1987177509 hasRelatedWork W3005262979 @default.
• W1987177509 hasRelatedWork W3015701583 @default.
• W1987177509 hasRelatedWork W3082170855 @default.
• W1987177509 hasRelatedWork W3135953374 @default.
• W1987177509 hasRelatedWork W3202399420 @default.
• W1987177509 hasRelatedWork W4236317703 @default.
• W1987177509 hasRelatedWork W4385190314 @default.
• W1987177509 hasVolume "33" @default.
• W1987177509 isParatext "false" @default.

• next