- W1989175549 abstract "Abstract In this study, microstructure evolution at intermetallic interfaces in SnAgCu solder joints of an area array component was investigated at various stages of a thermal cycling test. Failure modes of solder joints were analyzed to determine the effects of process conditions on crack propagation. Lead-free printed-circuit-board (PCB) assemblies were carried out using different foot print designs on PCBs, solder paste deposition volume and reflow profiles. Lead-free SnAgCu plastic-ball-grid-array (PBGA) components were assembled onto PCBs using SnAgCu solder paste. The assembled boards were subjected to the thermal cycling test (−40 °C/+125 °C), and crack initiation and crack propagation during the test were studied. Microstructure analysis and measurements of interface intermetallic growth were conducted using samples after 0, 1000, 2000 and 3000 thermal cycles. Failures were not found before 5700 thermal cycles and the characteristic lives of all solder joints produced using different process and design parameters were more than 7200 thermal cycles, indicating robust solder joints produced with a wide process window. In addition, the intermetallic interfaces were found to have Sn–Ni–Cu. The solder joints consisted of two Ag–Sn compounds exhibiting unique structures of Sn-rich and Ag-rich compounds. A crystalline star-shaped structure of Sn–Ni–Cu–P was also observed in a solder joint. The intermetallic thicknesses were less than 3 μm. The intermetallics growth was about 10% after 3000 thermal cycles. However, these compounds did not affect the reliability of the solder joints. Furthermore, findings in this study were compared with those in previous studies, and the comparison proved the validity of this study." @default.
- W1989175549 created "2016-06-24" @default.
- W1989175549 creator A5008606329 @default.
- W1989175549 creator A5056599169 @default.
- W1989175549 creator A5072928191 @default.
- W1989175549 date "2006-02-01" @default.
- W1989175549 modified "2023-09-26" @default.
- W1989175549 title "Effects of process conditions on reliability, microstructure evolution and failure modes of SnAgCu solder joints" @default.
- W1989175549 cites W1986159450 @default.
- W1989175549 cites W1994986915 @default.
- W1989175549 cites W2007253222 @default.
- W1989175549 cites W2010001525 @default.
- W1989175549 cites W2020426419 @default.
- W1989175549 cites W2036900792 @default.
- W1989175549 cites W2042789821 @default.
- W1989175549 cites W2053811404 @default.
- W1989175549 cites W2055019056 @default.
- W1989175549 cites W2062086178 @default.
- W1989175549 cites W2088314224 @default.
- W1989175549 cites W2097719765 @default.
- W1989175549 cites W2113394070 @default.
- W1989175549 doi "https://doi.org/10.1016/j.microrel.2005.05.005" @default.
- W1989175549 hasPublicationYear "2006" @default.
- W1989175549 type Work @default.
- W1989175549 sameAs 1989175549 @default.
- W1989175549 citedByCount "37" @default.
- W1989175549 countsByYear W19891755492012 @default.
- W1989175549 countsByYear W19891755492014 @default.
- W1989175549 countsByYear W19891755492015 @default.
- W1989175549 countsByYear W19891755492017 @default.
- W1989175549 countsByYear W19891755492020 @default.
- W1989175549 countsByYear W19891755492021 @default.
- W1989175549 countsByYear W19891755492022 @default.
- W1989175549 countsByYear W19891755492023 @default.
- W1989175549 crossrefType "journal-article" @default.
- W1989175549 hasAuthorship W1989175549A5008606329 @default.
- W1989175549 hasAuthorship W1989175549A5056599169 @default.
- W1989175549 hasAuthorship W1989175549A5072928191 @default.
- W1989175549 hasConcept C111919701 @default.
- W1989175549 hasConcept C121332964 @default.
- W1989175549 hasConcept C127413603 @default.
- W1989175549 hasConcept C159985019 @default.
- W1989175549 hasConcept C163258240 @default.
- W1989175549 hasConcept C191897082 @default.
- W1989175549 hasConcept C192562407 @default.
- W1989175549 hasConcept C200601418 @default.
- W1989175549 hasConcept C41008148 @default.
- W1989175549 hasConcept C43214815 @default.
- W1989175549 hasConcept C50296614 @default.
- W1989175549 hasConcept C66938386 @default.
- W1989175549 hasConcept C77595967 @default.
- W1989175549 hasConcept C87976508 @default.
- W1989175549 hasConcept C97355855 @default.
- W1989175549 hasConcept C98045186 @default.
- W1989175549 hasConceptScore W1989175549C111919701 @default.
- W1989175549 hasConceptScore W1989175549C121332964 @default.
- W1989175549 hasConceptScore W1989175549C127413603 @default.
- W1989175549 hasConceptScore W1989175549C159985019 @default.
- W1989175549 hasConceptScore W1989175549C163258240 @default.
- W1989175549 hasConceptScore W1989175549C191897082 @default.
- W1989175549 hasConceptScore W1989175549C192562407 @default.
- W1989175549 hasConceptScore W1989175549C200601418 @default.
- W1989175549 hasConceptScore W1989175549C41008148 @default.
- W1989175549 hasConceptScore W1989175549C43214815 @default.
- W1989175549 hasConceptScore W1989175549C50296614 @default.
- W1989175549 hasConceptScore W1989175549C66938386 @default.
- W1989175549 hasConceptScore W1989175549C77595967 @default.
- W1989175549 hasConceptScore W1989175549C87976508 @default.
- W1989175549 hasConceptScore W1989175549C97355855 @default.
- W1989175549 hasConceptScore W1989175549C98045186 @default.
- W1989175549 hasIssue "2-4" @default.
- W1989175549 hasLocation W19891755491 @default.
- W1989175549 hasOpenAccess W1989175549 @default.
- W1989175549 hasPrimaryLocation W19891755491 @default.
- W1989175549 hasRelatedWork W150843855 @default.
- W1989175549 hasRelatedWork W1967565480 @default.
- W1989175549 hasRelatedWork W2011794728 @default.
- W1989175549 hasRelatedWork W2020660716 @default.
- W1989175549 hasRelatedWork W2046292958 @default.
- W1989175549 hasRelatedWork W2351679394 @default.
- W1989175549 hasRelatedWork W2771611885 @default.
- W1989175549 hasRelatedWork W2997894178 @default.
- W1989175549 hasRelatedWork W3157307459 @default.
- W1989175549 hasRelatedWork W4283821095 @default.
- W1989175549 hasVolume "46" @default.
- W1989175549 isParatext "false" @default.
- W1989175549 isRetracted "false" @default.
- W1989175549 magId "1989175549" @default.
- W1989175549 workType "article" @default.