- W1990202130 abstract "The Mg–8Y–1Er–2Zn (wt.%) alloy with high strength, plasticity and heat-resistance was prepared by the hot extrusion technique and the following aging treatment. The microstructure and mechanical properties were investigated. The results show that long period stacking ordered (LPSO) phase is different from common inermetallics, and the former can be bent by plastic deformation and presents good combination with the Mg matrix. The good mechanical properties of as-extruded alloy are mainly attributed to the lamellar strips with 18R LPSO structure as well as the microstructure refinement. Aging treatment at 220 °C can further improve the strength but not at the expense of plasticity. The ultimate tensile strength (UTS) and elongation to failure (ε) of as-extruded alloy at peak hardness are 390 MPa and 18% at room temperature, and 322 MPa and 30% at 250 °C, respectively. The formation of fine α-Mg recrystallization grains with high number density of 14H LPSO structure is mainly responsible for the superior mechanical properties of extruded alloy after peak-aging." @default.
- W1990202130 created "2016-06-24" @default.
- W1990202130 creator A5011344366 @default.
- W1990202130 creator A5028446319 @default.
- W1990202130 creator A5041408950 @default.
- W1990202130 creator A5062602222 @default.
- W1990202130 creator A5066716873 @default.
- W1990202130 creator A5069041636 @default.
- W1990202130 creator A5074110725 @default.
- W1990202130 date "2014-02-01" @default.
- W1990202130 modified "2023-09-29" @default.
- W1990202130 title "Microstructure and mechanical properties of high-performance Mg–Y–Er–Zn extruded alloy" @default.
- W1990202130 cites W1963923708 @default.
- W1990202130 cites W1973333367 @default.
- W1990202130 cites W1984785241 @default.
- W1990202130 cites W1991866446 @default.
- W1990202130 cites W2003337516 @default.
- W1990202130 cites W2003359530 @default.
- W1990202130 cites W2003747466 @default.
- W1990202130 cites W2005220090 @default.
- W1990202130 cites W2008945759 @default.
- W1990202130 cites W2023925844 @default.
- W1990202130 cites W2032271117 @default.
- W1990202130 cites W2034025024 @default.
- W1990202130 cites W2038528394 @default.
- W1990202130 cites W2055599621 @default.
- W1990202130 cites W2058339778 @default.
- W1990202130 cites W2059593814 @default.
- W1990202130 cites W2062681916 @default.
- W1990202130 cites W2064372727 @default.
- W1990202130 cites W2068048050 @default.
- W1990202130 cites W2072427313 @default.
- W1990202130 cites W2073734867 @default.
- W1990202130 cites W2074577438 @default.
- W1990202130 cites W2080581035 @default.
- W1990202130 cites W2084206766 @default.
- W1990202130 cites W2089565144 @default.
- W1990202130 cites W2110278862 @default.
- W1990202130 cites W2110573545 @default.
- W1990202130 cites W609387768 @default.
- W1990202130 doi "https://doi.org/10.1016/j.matdes.2013.08.048" @default.
- W1990202130 hasPublicationYear "2014" @default.
- W1990202130 type Work @default.
- W1990202130 sameAs 1990202130 @default.
- W1990202130 citedByCount "51" @default.
- W1990202130 countsByYear W19902021302014 @default.
- W1990202130 countsByYear W19902021302015 @default.
- W1990202130 countsByYear W19902021302016 @default.
- W1990202130 countsByYear W19902021302017 @default.
- W1990202130 countsByYear W19902021302018 @default.
- W1990202130 countsByYear W19902021302019 @default.
- W1990202130 countsByYear W19902021302020 @default.
- W1990202130 countsByYear W19902021302021 @default.
- W1990202130 countsByYear W19902021302022 @default.
- W1990202130 countsByYear W19902021302023 @default.
- W1990202130 crossrefType "journal-article" @default.
- W1990202130 hasAuthorship W1990202130A5011344366 @default.
- W1990202130 hasAuthorship W1990202130A5028446319 @default.
- W1990202130 hasAuthorship W1990202130A5041408950 @default.
- W1990202130 hasAuthorship W1990202130A5062602222 @default.
- W1990202130 hasAuthorship W1990202130A5066716873 @default.
- W1990202130 hasAuthorship W1990202130A5069041636 @default.
- W1990202130 hasAuthorship W1990202130A5074110725 @default.
- W1990202130 hasConcept C112950240 @default.
- W1990202130 hasConcept C151730666 @default.
- W1990202130 hasConcept C159985019 @default.
- W1990202130 hasConcept C191897082 @default.
- W1990202130 hasConcept C192562407 @default.
- W1990202130 hasConcept C195702682 @default.
- W1990202130 hasConcept C2778958987 @default.
- W1990202130 hasConcept C2780026712 @default.
- W1990202130 hasConcept C33947775 @default.
- W1990202130 hasConcept C77851909 @default.
- W1990202130 hasConcept C79186407 @default.
- W1990202130 hasConcept C86803240 @default.
- W1990202130 hasConcept C87976508 @default.
- W1990202130 hasConceptScore W1990202130C112950240 @default.
- W1990202130 hasConceptScore W1990202130C151730666 @default.
- W1990202130 hasConceptScore W1990202130C159985019 @default.
- W1990202130 hasConceptScore W1990202130C191897082 @default.
- W1990202130 hasConceptScore W1990202130C192562407 @default.
- W1990202130 hasConceptScore W1990202130C195702682 @default.
- W1990202130 hasConceptScore W1990202130C2778958987 @default.
- W1990202130 hasConceptScore W1990202130C2780026712 @default.
- W1990202130 hasConceptScore W1990202130C33947775 @default.
- W1990202130 hasConceptScore W1990202130C77851909 @default.
- W1990202130 hasConceptScore W1990202130C79186407 @default.
- W1990202130 hasConceptScore W1990202130C86803240 @default.
- W1990202130 hasConceptScore W1990202130C87976508 @default.
- W1990202130 hasFunder F4320321001 @default.
- W1990202130 hasFunder F4320323085 @default.
- W1990202130 hasLocation W19902021301 @default.
- W1990202130 hasOpenAccess W1990202130 @default.
- W1990202130 hasPrimaryLocation W19902021301 @default.
- W1990202130 hasRelatedWork W1975287205 @default.
- W1990202130 hasRelatedWork W1986291781 @default.
- W1990202130 hasRelatedWork W1987487801 @default.
- W1990202130 hasRelatedWork W1988943651 @default.