- W1991395404 abstract "The effect of bithermal fatigue on the damage production in the directionally solidified nickel-base superalloy IN-6203DS was investigated. The results of bithermal fatigue tests (compression half cycle at low temperatures) and isothermal symmetrical fatigue tests at 850 C showed that the cyclic lifetime of samples from directionally solidified IN-6203DS alloy experienced a drastic lifetime reduction in bithermal fatigue tests, as compared to lifetime in corresponding symmetrical high-temperature fatigue tests. This lifetime reduction was caused by the additional occurrence of internal damage, mainly at grain boundaries normal to the load axis. This damage did not occur during symmetrical tests. 6 refs." @default.
- W1991395404 created "2016-06-24" @default.
- W1991395404 creator A5010251611 @default.
- W1991395404 creator A5071921426 @default.
- W1991395404 date "1992-05-01" @default.
- W1991395404 modified "2023-09-27" @default.
- W1991395404 title "Isothermal and bithermal fatigue of a directionally solidified Ni-based superalloy" @default.
- W1991395404 cites W1997773398 @default.
- W1991395404 cites W2089159232 @default.
- W1991395404 doi "https://doi.org/10.1016/0956-716x(92)90646-v" @default.
- W1991395404 hasPublicationYear "1992" @default.
- W1991395404 type Work @default.
- W1991395404 sameAs 1991395404 @default.
- W1991395404 citedByCount "1" @default.
- W1991395404 crossrefType "journal-article" @default.
- W1991395404 hasAuthorship W1991395404A5010251611 @default.
- W1991395404 hasAuthorship W1991395404A5071921426 @default.
- W1991395404 hasConcept C121332964 @default.
- W1991395404 hasConcept C133347239 @default.
- W1991395404 hasConcept C159985019 @default.
- W1991395404 hasConcept C191897082 @default.
- W1991395404 hasConcept C192562407 @default.
- W1991395404 hasConcept C207055975 @default.
- W1991395404 hasConcept C2780026712 @default.
- W1991395404 hasConcept C71924100 @default.
- W1991395404 hasConcept C97355855 @default.
- W1991395404 hasConceptScore W1991395404C121332964 @default.
- W1991395404 hasConceptScore W1991395404C133347239 @default.
- W1991395404 hasConceptScore W1991395404C159985019 @default.
- W1991395404 hasConceptScore W1991395404C191897082 @default.
- W1991395404 hasConceptScore W1991395404C192562407 @default.
- W1991395404 hasConceptScore W1991395404C207055975 @default.
- W1991395404 hasConceptScore W1991395404C2780026712 @default.
- W1991395404 hasConceptScore W1991395404C71924100 @default.
- W1991395404 hasConceptScore W1991395404C97355855 @default.
- W1991395404 hasLocation W19913954041 @default.
- W1991395404 hasOpenAccess W1991395404 @default.
- W1991395404 hasPrimaryLocation W19913954041 @default.
- W1991395404 hasRelatedWork W1491790056 @default.
- W1991395404 hasRelatedWork W1968229935 @default.
- W1991395404 hasRelatedWork W1979717585 @default.
- W1991395404 hasRelatedWork W1985955539 @default.
- W1991395404 hasRelatedWork W1988724527 @default.
- W1991395404 hasRelatedWork W1989904494 @default.
- W1991395404 hasRelatedWork W2002332851 @default.
- W1991395404 hasRelatedWork W2004238496 @default.
- W1991395404 hasRelatedWork W2021308642 @default.
- W1991395404 hasRelatedWork W2031218193 @default.
- W1991395404 hasRelatedWork W2037113038 @default.
- W1991395404 hasRelatedWork W2051329063 @default.
- W1991395404 hasRelatedWork W2065522404 @default.
- W1991395404 hasRelatedWork W2074451610 @default.
- W1991395404 hasRelatedWork W2091731851 @default.
- W1991395404 hasRelatedWork W2348494037 @default.
- W1991395404 hasRelatedWork W2385473382 @default.
- W1991395404 hasRelatedWork W2387879916 @default.
- W1991395404 hasRelatedWork W2390615777 @default.
- W1991395404 hasRelatedWork W2471162028 @default.
- W1991395404 isParatext "false" @default.
- W1991395404 isRetracted "false" @default.
- W1991395404 magId "1991395404" @default.
- W1991395404 workType "article" @default.