• W1992382839 abstract "Dislocation motion at low temperatures in pure and hydrogen free Nb is investigated after deformations at 77 K, RT, or 420 K by an internal friction technique at about 600 Hz. The α-peak in hydrogen free (Pd coated) Nb specimens after deformation at 77 K and warm up to RT is observed as a very broad peak at around 60 K. Ageing at 420 K causes the preferential suppression of the higher temperature part of the α-peak and reveals the α1-peak at around 40 K. This suppression is probably associated with dislocation pinning by C, N, or O impurities. The subtraction of this α1- peak from the virgin α-peak gives the α2-peak at around 60 K. On the other hand, deformation at RT (or 420 K) always causes an absorption of hydrogen into the specimen and gives rise to the small α1-peak and the large hydrogen cold work (HCW) peak. During ageing at 420 K (hydrogen degassing treatment) of this specimen, the HCW peak is suppressed starting from the higher temperature side and finally disappeared and the α1-peak grows up at about 40 K. These results and also the activation volume of 5b3 or less determined for the α1-peak and about 30b3 for the α2-peak suggest that the α1- and the α2-peaks are associated with the kink diffusion process in screw dislocations and the kink pair formation process on non-screw dislocations, respectively. The activation parameters determined for these peaks are E ≈ 70 meV and τ0 ≈ 1.0 × 10−12 s for the α1-peak and E ≈ 75 meV and τ0 ≈ 3 × 10−11 s for the α2 peak, respectively. Bei tiefen Temperaturen wird in reinem und wasserstofffreiem Nb die Versetzungsbewegung nach Deformation bei 77 K, RT oder 420 K mittels Messung der inneren Reibung bei 600 Hz untersucht. Das α-Maximum in wasserstofffreien (Pd-bedeckten) Nb-Proben nach Deformation bei 77 K und Erwärmung auf RT wird als sehr breites Maximum bei etwa 60 K beobachtet. Temperung bei 420 K verursacht die bevorzugte Unterdrückung des höheren Temperaturanteils des α-Maximums und ergibt ein α1-Maximum bei etwa 40 K. Diese Unterdrückung ist wahrscheinlich verknüpft mit einer Versetzungsverankerung durch C-, N- oder O-Störstellen. Die Substraktion dieses α1-Maximums vom jungfräulichen α-Maximum ergibt das α2-Maximum bei etwa 60 K. Andererseits verursacht eine Deformation bei RT (oder 420 K) eine Absorption von Wasserstoff in der Probe und gibt Anlaß zu dem kleinen, α1-Maximum und dem großen Cold Work Wasserstoff (HCW)-Maximum. Während der Temperung bei 420 K (Wasserstoffentgasungsbehandlung) dieser Probe wird das HCW-Maximum unterdrückt, beginnend auf der Hochtemperaturseite, und verschwindet schließlich, während das α1-Maximum erneut bei etwa 40 K wächst. Diese Ergebnisse sowie das Aktivierungsvolumen von 5b3 oder kleiner, für das α1-Maximum und etwa 30b3 für das α2-Maximum weisen darauf hin, daß die α1- und α2-Maxima verknüpft sind mit einem Kinkdiffusionsprozeß der Schraubenversetzungen bzw. einem Kinkpaarbildungsprozeß der Nicht-Schraubenversetzungen. Die für diese Maxima bestimmten Aktivierungsparameter sind E ≈ 70 meV und τ0 ≈ 1,0 × 10−12 s, für das α1- Maximum bzw. E ≈ 75 meV und τ0 ≈ 3 × 10−11 s für das α2-Maximum." @default.
• W1992382839 created "2016-06-24" @default.
• W1992382839 creator A5017563178 @default.
• W1992382839 creator A5056671820 @default.
• W1992382839 creator A5084351447 @default.
• W1992382839 date "1987-11-16" @default.
• W1992382839 modified "2023-09-26" @default.
• W1992382839 title "Low-temperature dislocation internal friction in hydrogen-free niobium" @default.
• W1992382839 cites W1965452309 @default.
• W1992382839 cites W1968555189 @default.
• W1992382839 cites W1984647614 @default.
• W1992382839 cites W1986180940 @default.
• W1992382839 cites W1993154113 @default.
• W1992382839 cites W2014613677 @default.
• W1992382839 cites W2015572869 @default.
• W1992382839 cites W2020688324 @default.
• W1992382839 cites W2033290861 @default.
• W1992382839 cites W2034866290 @default.
• W1992382839 cites W2035143654 @default.
• W1992382839 cites W2055499189 @default.
• W1992382839 cites W2095070575 @default.
• W1992382839 cites W2098256998 @default.
• W1992382839 cites W2143268801 @default.
• W1992382839 cites W941798707 @default.
• W1992382839 cites W2072908557 @default.
• W1992382839 doi "https://doi.org/10.1002/pssa.2211040134" @default.
• W1992382839 hasPublicationYear "1987" @default.
• W1992382839 type Work @default.
• W1992382839 sameAs 1992382839 @default.
• W1992382839 citedByCount "10" @default.
• W1992382839 countsByYear W19923828392019 @default.
• W1992382839 crossrefType "journal-article" @default.
• W1992382839 hasAuthorship W1992382839A5017563178 @default.
• W1992382839 hasAuthorship W1992382839A5056671820 @default.
• W1992382839 hasAuthorship W1992382839A5084351447 @default.
• W1992382839 hasConcept C113196181 @default.
• W1992382839 hasConcept C121332964 @default.
• W1992382839 hasConcept C159122135 @default.
• W1992382839 hasConcept C159985019 @default.
• W1992382839 hasConcept C178790620 @default.
• W1992382839 hasConcept C185592680 @default.
• W1992382839 hasConcept C191897082 @default.
• W1992382839 hasConcept C192562407 @default.
• W1992382839 hasConcept C204366326 @default.
• W1992382839 hasConcept C26873012 @default.
• W1992382839 hasConcept C2985158122 @default.
• W1992382839 hasConcept C43617362 @default.
• W1992382839 hasConcept C507968137 @default.
• W1992382839 hasConcept C512968161 @default.
• W1992382839 hasConcept C69357855 @default.
• W1992382839 hasConcept C71987851 @default.
• W1992382839 hasConcept C8010536 @default.
• W1992382839 hasConcept C97355855 @default.
• W1992382839 hasConceptScore W1992382839C113196181 @default.
• W1992382839 hasConceptScore W1992382839C121332964 @default.
• W1992382839 hasConceptScore W1992382839C159122135 @default.
• W1992382839 hasConceptScore W1992382839C159985019 @default.
• W1992382839 hasConceptScore W1992382839C178790620 @default.
• W1992382839 hasConceptScore W1992382839C185592680 @default.
• W1992382839 hasConceptScore W1992382839C191897082 @default.
• W1992382839 hasConceptScore W1992382839C192562407 @default.
• W1992382839 hasConceptScore W1992382839C204366326 @default.
• W1992382839 hasConceptScore W1992382839C26873012 @default.
• W1992382839 hasConceptScore W1992382839C2985158122 @default.
• W1992382839 hasConceptScore W1992382839C43617362 @default.
• W1992382839 hasConceptScore W1992382839C507968137 @default.
• W1992382839 hasConceptScore W1992382839C512968161 @default.
• W1992382839 hasConceptScore W1992382839C69357855 @default.
• W1992382839 hasConceptScore W1992382839C71987851 @default.
• W1992382839 hasConceptScore W1992382839C8010536 @default.
• W1992382839 hasConceptScore W1992382839C97355855 @default.
• W1992382839 hasIssue "1" @default.
• W1992382839 hasLocation W19923828391 @default.
• W1992382839 hasOpenAccess W1992382839 @default.
• W1992382839 hasPrimaryLocation W19923828391 @default.
• W1992382839 hasRelatedWork W1992382839 @default.
• W1992382839 hasRelatedWork W1992662866 @default.
• W1992382839 hasRelatedWork W2009623648 @default.
• W1992382839 hasRelatedWork W2038058640 @default.
• W1992382839 hasRelatedWork W2183232989 @default.
• W1992382839 hasRelatedWork W2806773088 @default.
• W1992382839 hasRelatedWork W3183248983 @default.
• W1992382839 hasRelatedWork W4283391832 @default.
• W1992382839 hasRelatedWork W4313423027 @default.
• W1992382839 hasRelatedWork W95672946 @default.
• W1992382839 hasVolume "104" @default.
• W1992382839 isParatext "false" @default.
• W1992382839 isRetracted "false" @default.
• W1992382839 magId "1992382839" @default.
• W1992382839 workType "article" @default.