- W1993938659 abstract "The directional solidification of the ternary Al alloy with composition of 2.6 at%Ni, 0.9 at%Y and 96.5 at% Al was carried out under the temperature gradient of 5 K/mm and the droping velocities of 0.5 mm/min, 1 mm/min, 5 mm/min, 10 mm/min, and 25 mm/min. The microstructure of the Al-Ni-Y ternary alloy was also analyzed by X-ray diffraction and optical microscope. The experimental results show that the microstructures of the Al-Ni-Y ternary alloy are consisted of ª-Al 2 , Al 3 Ni and Y 4 Ni 6 Al 23 phase when the alloy was directionally solidified in all directionally solidified rates in the experiments. No primary -Al can be found in the sample with directionally solidified rate of 0.5 mm/min. When the rates higher than 1 mm/min, the primary ª-Al can be observed. The microstructure of the directionally solidified alloy becomes finer and the primary ª-Al is smaller gradually with the increasing of growth velocities when the dropping rate of directional solidification is higher than 5 min/min. Two eutectic structures, Y 4 Ni 6 Al 23 andª-Al eutectic and Al3Ni and ª-Al eutectic, can be found when the dropping rate is higher than 10 mm/min." @default.
- W1993938659 created "2016-06-24" @default.
- W1993938659 creator A5025931224 @default.
- W1993938659 date "2012-08-01" @default.
- W1993938659 modified "2023-09-27" @default.
- W1993938659 title "Effects of Growth Rates on Directionally Solidified Microstructure of Al-Ni-Y Ternary Alloy" @default.
- W1993938659 cites W1986542488 @default.
- W1993938659 cites W1992714126 @default.
- W1993938659 cites W2005360310 @default.
- W1993938659 cites W2011292614 @default.
- W1993938659 cites W2021220340 @default.
- W1993938659 cites W2028667398 @default.
- W1993938659 cites W2050433995 @default.
- W1993938659 cites W2068979445 @default.
- W1993938659 cites W2157743688 @default.
- W1993938659 cites W2280522313 @default.
- W1993938659 doi "https://doi.org/10.4028/www.scientific.net/amr.562-564.477" @default.
- W1993938659 hasPublicationYear "2012" @default.
- W1993938659 type Work @default.
- W1993938659 sameAs 1993938659 @default.
- W1993938659 citedByCount "0" @default.
- W1993938659 crossrefType "journal-article" @default.
- W1993938659 hasAuthorship W1993938659A5025931224 @default.
- W1993938659 hasConcept C159985019 @default.
- W1993938659 hasConcept C178790620 @default.
- W1993938659 hasConcept C18168003 @default.
- W1993938659 hasConcept C185592680 @default.
- W1993938659 hasConcept C191897082 @default.
- W1993938659 hasConcept C192562407 @default.
- W1993938659 hasConcept C199360897 @default.
- W1993938659 hasConcept C26771246 @default.
- W1993938659 hasConcept C2779856285 @default.
- W1993938659 hasConcept C2780026712 @default.
- W1993938659 hasConcept C41008148 @default.
- W1993938659 hasConcept C44280652 @default.
- W1993938659 hasConcept C64452783 @default.
- W1993938659 hasConcept C77017923 @default.
- W1993938659 hasConcept C87976508 @default.
- W1993938659 hasConceptScore W1993938659C159985019 @default.
- W1993938659 hasConceptScore W1993938659C178790620 @default.
- W1993938659 hasConceptScore W1993938659C18168003 @default.
- W1993938659 hasConceptScore W1993938659C185592680 @default.
- W1993938659 hasConceptScore W1993938659C191897082 @default.
- W1993938659 hasConceptScore W1993938659C192562407 @default.
- W1993938659 hasConceptScore W1993938659C199360897 @default.
- W1993938659 hasConceptScore W1993938659C26771246 @default.
- W1993938659 hasConceptScore W1993938659C2779856285 @default.
- W1993938659 hasConceptScore W1993938659C2780026712 @default.
- W1993938659 hasConceptScore W1993938659C41008148 @default.
- W1993938659 hasConceptScore W1993938659C44280652 @default.
- W1993938659 hasConceptScore W1993938659C64452783 @default.
- W1993938659 hasConceptScore W1993938659C77017923 @default.
- W1993938659 hasConceptScore W1993938659C87976508 @default.
- W1993938659 hasLocation W19939386591 @default.
- W1993938659 hasOpenAccess W1993938659 @default.
- W1993938659 hasPrimaryLocation W19939386591 @default.
- W1993938659 hasRelatedWork W1993938659 @default.
- W1993938659 hasRelatedWork W2014792072 @default.
- W1993938659 hasRelatedWork W2026800948 @default.
- W1993938659 hasRelatedWork W2057024573 @default.
- W1993938659 hasRelatedWork W2373097621 @default.
- W1993938659 hasRelatedWork W2375844564 @default.
- W1993938659 hasRelatedWork W2383229841 @default.
- W1993938659 hasRelatedWork W2383471697 @default.
- W1993938659 hasRelatedWork W2383814555 @default.
- W1993938659 hasRelatedWork W2385775974 @default.
- W1993938659 hasVolume "562-564" @default.
- W1993938659 isParatext "false" @default.
- W1993938659 isRetracted "false" @default.
- W1993938659 magId "1993938659" @default.
- W1993938659 workType "article" @default.