- W2000363857 endingPage "30" @default.
- W2000363857 startingPage "25" @default.
- W2000363857 abstract "The morphological transition from the A-type to D-type graphite (undercooled graphite) in cast iron has been studied using Fe-3.5%C-2.0%Si-0/0.1%Ti samples. The samples were prepared using a high frequency induction furnace flowing Ar atmosphere using 0.25% steel rods with or without Ti addition. The samples had Ti contents that ranged from 0 to 0.10% at 5 different levels by the addition of sponge titanium. The cooling curves of these melts were measured in a shell mold with an inside diameter of 30mm and 50mm height and in four BN-coated steel cup molds with a volume of 30ml each. The cooling curves were measured by CA thermocouples located at the center. The cooling curves were differentiated to determine the transition points, namely the onset and end points of the eutectic solidification. Three out of the four samples, solidifying in steel molds, were quenched during the eutectic solidification and their macro-structures and micro-structures were observed for the determining the solidification mode. The volume fractions of the D-type graphite area in the samples were measured using 30 microscope images of 50× magnification, and their eutectic temperature was also determined using their cooling curves. The volume fraction of the shell mold samples increased with the Ti addition from 5% to 55%, and if the Ti content was greater than 0.05%, the acceleration occurred with their maximum undercooling, ΔTMAX. The critical undercooling temperature, TA/D, and the critical solidification rate, RA/D, of the A-type to D-type graphite transition were determined by comparing the volume fractions to the solidification time. The ΔTMAX and TA/D values increased with the Ti addition. This is the main reason why the Ti addition accelerates the D-type graphite increase." @default.
- W2000363857 created "2016-06-24" @default.
- W2000363857 creator A5042920714 @default.
- W2000363857 creator A5083575775 @default.
- W2000363857 date "2010-12-01" @default.
- W2000363857 modified "2023-09-26" @default.
- W2000363857 title "Influence of Ti on Graphite Morphological Transition in Flake Graphite Cast Iron" @default.
- W2000363857 cites W2056791470 @default.
- W2000363857 cites W2507336872 @default.
- W2000363857 cites W2608916220 @default.
- W2000363857 doi "https://doi.org/10.4028/www.scientific.net/kem.457.25" @default.
- W2000363857 hasPublicationYear "2010" @default.
- W2000363857 type Work @default.
- W2000363857 sameAs 2000363857 @default.
- W2000363857 citedByCount "8" @default.
- W2000363857 countsByYear W20003638572013 @default.
- W2000363857 countsByYear W20003638572014 @default.
- W2000363857 countsByYear W20003638572015 @default.
- W2000363857 countsByYear W20003638572016 @default.
- W2000363857 countsByYear W20003638572018 @default.
- W2000363857 countsByYear W20003638572021 @default.
- W2000363857 crossrefType "journal-article" @default.
- W2000363857 hasAuthorship W2000363857A5042920714 @default.
- W2000363857 hasAuthorship W2000363857A5083575775 @default.
- W2000363857 hasConcept C112964491 @default.
- W2000363857 hasConcept C113196181 @default.
- W2000363857 hasConcept C121332964 @default.
- W2000363857 hasConcept C142724271 @default.
- W2000363857 hasConcept C159985019 @default.
- W2000363857 hasConcept C162184086 @default.
- W2000363857 hasConcept C168068576 @default.
- W2000363857 hasConcept C18168003 @default.
- W2000363857 hasConcept C185592680 @default.
- W2000363857 hasConcept C191897082 @default.
- W2000363857 hasConcept C192562407 @default.
- W2000363857 hasConcept C204787440 @default.
- W2000363857 hasConcept C20556612 @default.
- W2000363857 hasConcept C2776735967 @default.
- W2000363857 hasConcept C2779698641 @default.
- W2000363857 hasConcept C2780566776 @default.
- W2000363857 hasConcept C43617362 @default.
- W2000363857 hasConcept C506065880 @default.
- W2000363857 hasConcept C65590680 @default.
- W2000363857 hasConcept C71924100 @default.
- W2000363857 hasConcept C87976508 @default.
- W2000363857 hasConcept C90086362 @default.
- W2000363857 hasConcept C97355855 @default.
- W2000363857 hasConceptScore W2000363857C112964491 @default.
- W2000363857 hasConceptScore W2000363857C113196181 @default.
- W2000363857 hasConceptScore W2000363857C121332964 @default.
- W2000363857 hasConceptScore W2000363857C142724271 @default.
- W2000363857 hasConceptScore W2000363857C159985019 @default.
- W2000363857 hasConceptScore W2000363857C162184086 @default.
- W2000363857 hasConceptScore W2000363857C168068576 @default.
- W2000363857 hasConceptScore W2000363857C18168003 @default.
- W2000363857 hasConceptScore W2000363857C185592680 @default.
- W2000363857 hasConceptScore W2000363857C191897082 @default.
- W2000363857 hasConceptScore W2000363857C192562407 @default.
- W2000363857 hasConceptScore W2000363857C204787440 @default.
- W2000363857 hasConceptScore W2000363857C20556612 @default.
- W2000363857 hasConceptScore W2000363857C2776735967 @default.
- W2000363857 hasConceptScore W2000363857C2779698641 @default.
- W2000363857 hasConceptScore W2000363857C2780566776 @default.
- W2000363857 hasConceptScore W2000363857C43617362 @default.
- W2000363857 hasConceptScore W2000363857C506065880 @default.
- W2000363857 hasConceptScore W2000363857C65590680 @default.
- W2000363857 hasConceptScore W2000363857C71924100 @default.
- W2000363857 hasConceptScore W2000363857C87976508 @default.
- W2000363857 hasConceptScore W2000363857C90086362 @default.
- W2000363857 hasConceptScore W2000363857C97355855 @default.
- W2000363857 hasLocation W20003638571 @default.
- W2000363857 hasOpenAccess W2000363857 @default.
- W2000363857 hasPrimaryLocation W20003638571 @default.
- W2000363857 hasRelatedWork W1983614295 @default.
- W2000363857 hasRelatedWork W2000363857 @default.
- W2000363857 hasRelatedWork W2076911605 @default.
- W2000363857 hasRelatedWork W2324008243 @default.
- W2000363857 hasRelatedWork W2378555518 @default.
- W2000363857 hasRelatedWork W247207938 @default.
- W2000363857 hasRelatedWork W2507336872 @default.
- W2000363857 hasRelatedWork W2966432970 @default.
- W2000363857 hasRelatedWork W3148965194 @default.
- W2000363857 hasRelatedWork W2041010856 @default.
- W2000363857 hasVolume "457" @default.
- W2000363857 isParatext "false" @default.
- W2000363857 isRetracted "false" @default.
- W2000363857 magId "2000363857" @default.
- W2000363857 workType "article" @default.