- W2000388299 abstract "Zirconium implantation-induced amorphization has been investigated with Rutherford back scattering spectrometry along a channeling direction (RBS-C) using 2 MeV He+. Ion implantation was carried out at the energy of 175 keV, with fluences of 2×1015 to 2×1016 Zr+/cm2 at room temperatures. The critical amorphization fluence at room temperature was determined as ∼1.5×1016 Zr+/cm2 corresponding to ∼ 40 dpa; ∼2.7% peak Zr-concentration) which is a lower damage energy than that reported for implantation with ions of similar mass and energy. The effect of post implantation of oxygen into a pre-implanted sample (with zirconium) was investigated. The RBS results show that oxygen implantation in a crystalline sample increases the damage only slightly and slightly broadens the Zr profile. For the fluences above thresh-old for amorphization, post implantation by oxygen has very little effect on the residual damage or on the Zr distribution. The presence of both F and F+ centers were indicated by optical absorption (OA) measurements. The OA spectra show the concentration of F and F+ centers increases with increasing fluence with some changes resulting from oxygen implantation of a pre-zirconium-implanted sapphire. This alters the relative concentrations of F and F+ centers. The F-type center concentrations for the samples were calculated using Smakula's equation. Photoluminescence (PL) at an excitation of 255 nm confirms the presence of both F and F+ centers with emission peaks at about 420 and 325 nm respectively. The PL spectra suggest that oxygen implantation decrease the concentration of the both species, consistent with the OA results (© 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim)" @default.
- W2000388299 created "2016-06-24" @default.
- W2000388299 creator A5014556096 @default.
- W2000388299 creator A5066677047 @default.
- W2000388299 creator A5075876633 @default.
- W2000388299 creator A5091288880 @default.
- W2000388299 date "2012-12-18" @default.
- W2000388299 modified "2023-10-18" @default.
- W2000388299 title "The defect structure of sapphire produced by implantation of Zr and Zr plus O: threshold fluence for amorphization and optical properties" @default.
- W2000388299 doi "https://doi.org/10.1002/pssc.201200392" @default.
- W2000388299 hasPublicationYear "2012" @default.
- W2000388299 type Work @default.
- W2000388299 sameAs 2000388299 @default.
- W2000388299 citedByCount "3" @default.
- W2000388299 countsByYear W20003882992013 @default.
- W2000388299 countsByYear W20003882992014 @default.
- W2000388299 countsByYear W20003882992018 @default.
- W2000388299 crossrefType "journal-article" @default.
- W2000388299 hasAuthorship W2000388299A5014556096 @default.
- W2000388299 hasAuthorship W2000388299A5066677047 @default.
- W2000388299 hasAuthorship W2000388299A5075876633 @default.
- W2000388299 hasAuthorship W2000388299A5091288880 @default.
- W2000388299 hasConcept C113196181 @default.
- W2000388299 hasConcept C120665830 @default.
- W2000388299 hasConcept C121332964 @default.
- W2000388299 hasConcept C145148216 @default.
- W2000388299 hasConcept C171250308 @default.
- W2000388299 hasConcept C178790620 @default.
- W2000388299 hasConcept C185592680 @default.
- W2000388299 hasConcept C19067145 @default.
- W2000388299 hasConcept C191897082 @default.
- W2000388299 hasConcept C192562407 @default.
- W2000388299 hasConcept C22078206 @default.
- W2000388299 hasConcept C2780064504 @default.
- W2000388299 hasConcept C2780547777 @default.
- W2000388299 hasConcept C41823505 @default.
- W2000388299 hasConcept C43617362 @default.
- W2000388299 hasConcept C49040817 @default.
- W2000388299 hasConcept C520434653 @default.
- W2000388299 hasConcept C534791751 @default.
- W2000388299 hasConcept C540031477 @default.
- W2000388299 hasConcept C85080765 @default.
- W2000388299 hasConceptScore W2000388299C113196181 @default.
- W2000388299 hasConceptScore W2000388299C120665830 @default.
- W2000388299 hasConceptScore W2000388299C121332964 @default.
- W2000388299 hasConceptScore W2000388299C145148216 @default.
- W2000388299 hasConceptScore W2000388299C171250308 @default.
- W2000388299 hasConceptScore W2000388299C178790620 @default.
- W2000388299 hasConceptScore W2000388299C185592680 @default.
- W2000388299 hasConceptScore W2000388299C19067145 @default.
- W2000388299 hasConceptScore W2000388299C191897082 @default.
- W2000388299 hasConceptScore W2000388299C192562407 @default.
- W2000388299 hasConceptScore W2000388299C22078206 @default.
- W2000388299 hasConceptScore W2000388299C2780064504 @default.
- W2000388299 hasConceptScore W2000388299C2780547777 @default.
- W2000388299 hasConceptScore W2000388299C41823505 @default.
- W2000388299 hasConceptScore W2000388299C43617362 @default.
- W2000388299 hasConceptScore W2000388299C49040817 @default.
- W2000388299 hasConceptScore W2000388299C520434653 @default.
- W2000388299 hasConceptScore W2000388299C534791751 @default.
- W2000388299 hasConceptScore W2000388299C540031477 @default.
- W2000388299 hasConceptScore W2000388299C85080765 @default.
- W2000388299 hasIssue "2" @default.
- W2000388299 hasLocation W20003882991 @default.
- W2000388299 hasOpenAccess W2000388299 @default.
- W2000388299 hasPrimaryLocation W20003882991 @default.
- W2000388299 hasRelatedWork W1984315097 @default.
- W2000388299 hasRelatedWork W1985873695 @default.
- W2000388299 hasRelatedWork W1992037396 @default.
- W2000388299 hasRelatedWork W1992351272 @default.
- W2000388299 hasRelatedWork W2000388299 @default.
- W2000388299 hasRelatedWork W2030882861 @default.
- W2000388299 hasRelatedWork W2037515270 @default.
- W2000388299 hasRelatedWork W2048867833 @default.
- W2000388299 hasRelatedWork W2082553217 @default.
- W2000388299 hasRelatedWork W861034006 @default.
- W2000388299 hasVolume "10" @default.
- W2000388299 isParatext "false" @default.
- W2000388299 isRetracted "false" @default.
- W2000388299 magId "2000388299" @default.
- W2000388299 workType "article" @default.