- W2000451489 abstract "The effect of the presence of rust on steel on its further corrosion during outdoor and laboratory exposure to SO2 has been examined. More aggressive initial conditions favour the formation of non-protective, loose rust which-flakes off from the metal surface and increases the subsequent yearly corrosion values. The initial rust present increases the rate of attack during the first 2–3 months, but there is then a general falling off of the corrosion rate with time. SO2-contaminated rust is able to promote corrosion on clean (rust-free) steel, but the amount of corrosion is not dependent on the amount of SO2 adsorbed by the rust. The order of severity of attack on steel by different electrolytes differs from that caused by rust produced by the same electrolytes. Rust contaminated with FeSO4 or FeCl3 enhances the rusting of steel, whereas rust converters (such as phosphates) have beneficial effects. In the further rusting in SO2 of prerusted steel specimens it was found that the duration.of the pre-rusting period determines the subsequent rate of rusting, but the ‘age’ of the rust, rather than its thickness, determines its protective effect. In interrupted SO2 exposure, in which the pre-rusted specimens were first exposed to SO2 and then to humid SO2-free air, it was found that a temperature (18°e) and humidity (50% R.H.) which are too low to initiate the formation of incipient reaction product (FeSO4, 4H2O) on clean metal, allow sufficient formation of these products on rusted specimens to enable rusting to continue in moist SO2-free air." @default.
- W2000451489 created "2016-06-24" @default.
- W2000451489 creator A5031173480 @default.
- W2000451489 creator A5043406867 @default.
- W2000451489 date "1973-09-01" @default.
- W2000451489 modified "2023-10-18" @default.
- W2000451489 title "Behaviour of Rust and Rusted Steel Surfaces" @default.
- W2000451489 cites W1998729125 @default.
- W2000451489 cites W2009847481 @default.
- W2000451489 cites W2035249943 @default.
- W2000451489 cites W2046132502 @default.
- W2000451489 cites W2157451914 @default.
- W2000451489 cites W4255121003 @default.
- W2000451489 doi "https://doi.org/10.1179/000705973798321883" @default.
- W2000451489 hasPublicationYear "1973" @default.
- W2000451489 type Work @default.
- W2000451489 sameAs 2000451489 @default.
- W2000451489 citedByCount "1" @default.
- W2000451489 crossrefType "journal-article" @default.
- W2000451489 hasAuthorship W2000451489A5031173480 @default.
- W2000451489 hasAuthorship W2000451489A5043406867 @default.
- W2000451489 hasConcept C121332964 @default.
- W2000451489 hasConcept C158960510 @default.
- W2000451489 hasConcept C191897082 @default.
- W2000451489 hasConcept C192562407 @default.
- W2000451489 hasConcept C197781089 @default.
- W2000451489 hasConcept C199360897 @default.
- W2000451489 hasConcept C20625102 @default.
- W2000451489 hasConcept C41008148 @default.
- W2000451489 hasConcept C544153396 @default.
- W2000451489 hasConcept C97355855 @default.
- W2000451489 hasConceptScore W2000451489C121332964 @default.
- W2000451489 hasConceptScore W2000451489C158960510 @default.
- W2000451489 hasConceptScore W2000451489C191897082 @default.
- W2000451489 hasConceptScore W2000451489C192562407 @default.
- W2000451489 hasConceptScore W2000451489C197781089 @default.
- W2000451489 hasConceptScore W2000451489C199360897 @default.
- W2000451489 hasConceptScore W2000451489C20625102 @default.
- W2000451489 hasConceptScore W2000451489C41008148 @default.
- W2000451489 hasConceptScore W2000451489C544153396 @default.
- W2000451489 hasConceptScore W2000451489C97355855 @default.
- W2000451489 hasIssue "5" @default.
- W2000451489 hasLocation W20004514891 @default.
- W2000451489 hasOpenAccess W2000451489 @default.
- W2000451489 hasPrimaryLocation W20004514891 @default.
- W2000451489 hasRelatedWork W1965708370 @default.
- W2000451489 hasRelatedWork W2062074601 @default.
- W2000451489 hasRelatedWork W2242289565 @default.
- W2000451489 hasRelatedWork W2323764994 @default.
- W2000451489 hasRelatedWork W2356411619 @default.
- W2000451489 hasRelatedWork W2374666697 @default.
- W2000451489 hasRelatedWork W2389386261 @default.
- W2000451489 hasRelatedWork W2393708124 @default.
- W2000451489 hasRelatedWork W3097783663 @default.
- W2000451489 hasRelatedWork W4234468012 @default.
- W2000451489 hasVolume "8" @default.
- W2000451489 isParatext "false" @default.
- W2000451489 isRetracted "false" @default.
- W2000451489 magId "2000451489" @default.
- W2000451489 workType "article" @default.