- W2000552828 abstract "An Ag-Pd thick-film conductor for aluminum nitride (AlN) ceramics was developed. The conductor showed adhesion strength and reliability almost comparable to those of commercial conductors for alumina ceramics. The influence of physical properties of the lead oxide glass frit on conductor performance was studied, and the most suitable glass was selected for the frit material. The softening point of frit glass has the largest effect on conductor performance; this temperature should be approximately 500 degrees C. If the softening point was either too high or too low, compared to the sintering temperature of the conducting metals, poor adhesion strength resulted. Use of glass with too high a softening point caused poor wettability but resistance to erosion by Pb-Sn solder, while it resulted in good wettability but poor erosion resistance when the softening point was too low. Additionally, Cr-, Ti, and Zr-oxides were identified as wettability-promoting agents. The molten glass did not penetrate into the AlN ceramics; rather, it remained on the surface. This behavior differed from that in the case of alumina ceramics, for which the molten glass penetrated along the grain boundaries.< <ETX xmlns:mml=http://www.w3.org/1998/Math/MathML xmlns:xlink=http://www.w3.org/1999/xlink>></ETX>" @default.
- W2000552828 created "2016-06-24" @default.
- W2000552828 creator A5013392433 @default.
- W2000552828 creator A5019649050 @default.
- W2000552828 creator A5019761718 @default.
- W2000552828 creator A5034409116 @default.
- W2000552828 date "1990-06-01" @default.
- W2000552828 modified "2023-09-25" @default.
- W2000552828 title "Ag-Pd thick film conductor for AlN ceramics" @default.
- W2000552828 cites W1976120114 @default.
- W2000552828 cites W1998857049 @default.
- W2000552828 cites W2070221684 @default.
- W2000552828 cites W2118411166 @default.
- W2000552828 cites W2170541220 @default.
- W2000552828 doi "https://doi.org/10.1109/33.56162" @default.
- W2000552828 hasPublicationYear "1990" @default.
- W2000552828 type Work @default.
- W2000552828 sameAs 2000552828 @default.
- W2000552828 citedByCount "16" @default.
- W2000552828 crossrefType "journal-article" @default.
- W2000552828 hasAuthorship W2000552828A5013392433 @default.
- W2000552828 hasAuthorship W2000552828A5019649050 @default.
- W2000552828 hasAuthorship W2000552828A5019761718 @default.
- W2000552828 hasAuthorship W2000552828A5034409116 @default.
- W2000552828 hasConcept C126989708 @default.
- W2000552828 hasConcept C134132462 @default.
- W2000552828 hasConcept C134514944 @default.
- W2000552828 hasConcept C13530604 @default.
- W2000552828 hasConcept C159985019 @default.
- W2000552828 hasConcept C191897082 @default.
- W2000552828 hasConcept C192562407 @default.
- W2000552828 hasConcept C2777581544 @default.
- W2000552828 hasConcept C2781098093 @default.
- W2000552828 hasConcept C68930688 @default.
- W2000552828 hasConceptScore W2000552828C126989708 @default.
- W2000552828 hasConceptScore W2000552828C134132462 @default.
- W2000552828 hasConceptScore W2000552828C134514944 @default.
- W2000552828 hasConceptScore W2000552828C13530604 @default.
- W2000552828 hasConceptScore W2000552828C159985019 @default.
- W2000552828 hasConceptScore W2000552828C191897082 @default.
- W2000552828 hasConceptScore W2000552828C192562407 @default.
- W2000552828 hasConceptScore W2000552828C2777581544 @default.
- W2000552828 hasConceptScore W2000552828C2781098093 @default.
- W2000552828 hasConceptScore W2000552828C68930688 @default.
- W2000552828 hasIssue "2" @default.
- W2000552828 hasLocation W20005528281 @default.
- W2000552828 hasOpenAccess W2000552828 @default.
- W2000552828 hasPrimaryLocation W20005528281 @default.
- W2000552828 hasRelatedWork W1967284073 @default.
- W2000552828 hasRelatedWork W2000552828 @default.
- W2000552828 hasRelatedWork W2026802036 @default.
- W2000552828 hasRelatedWork W2067716691 @default.
- W2000552828 hasRelatedWork W2110008131 @default.
- W2000552828 hasRelatedWork W2357980851 @default.
- W2000552828 hasRelatedWork W2367728600 @default.
- W2000552828 hasRelatedWork W2371076247 @default.
- W2000552828 hasRelatedWork W2371355397 @default.
- W2000552828 hasRelatedWork W2505031575 @default.
- W2000552828 hasVolume "13" @default.
- W2000552828 isParatext "false" @default.
- W2000552828 isRetracted "false" @default.
- W2000552828 magId "2000552828" @default.
- W2000552828 workType "article" @default.