- W2000598742 abstract "In-doped NiO films with indium concentrations ranging from 0 to 30.3 at. % were deposited on glass substrates to investigate corresponding structural, optical, and electrical property variations. The x-ray diffraction patterns show that all films display only NiO peaks. When In atoms were added to NiO films, the NiO peaks shifted to lower angles, indicating that the lattice parameters of the films increased due to the larger In ions substituting for the smaller Ni ions. An electrical resistivity (ρ) too high to be measured occurred when the indium concentration in the NiO film was less than 15.6 at. %. The ρ value dropped significantly to 0.06 Ω·cm as the indium concentration increased to 26.9 at. %. Upon further raising the In to 30.3 at. %, the ρ value decreased further to 0.01 Ω·cm. All the In-doped NiO films showed n-type conduction. The transmittance of undoped NiO film is as high as 96%. On raising the indium concentration to 15.6, 19.9, 26.9, and 30.3 at. %, the transmittances decreased further to 68%, 62%, 57%, and 47%, respectively. Introducing higher In concentrations improved the films’ thermal stability of electrical resistivity." @default.
- W2000598742 created "2016-06-24" @default.
- W2000598742 creator A5000275104 @default.
- W2000598742 creator A5026709814 @default.
- W2000598742 creator A5057758904 @default.
- W2000598742 creator A5061320453 @default.
- W2000598742 creator A5080836379 @default.
- W2000598742 creator A5081762612 @default.
- W2000598742 date "2014-02-18" @default.
- W2000598742 modified "2023-10-17" @default.
- W2000598742 title "Structural, optical, and electrical properties of NiO-In composite films deposited by radio frequency cosputtering" @default.
- W2000598742 cites W1985127914 @default.
- W2000598742 cites W1998518565 @default.
- W2000598742 cites W1998834859 @default.
- W2000598742 cites W2020375306 @default.
- W2000598742 cites W2021268452 @default.
- W2000598742 cites W2024096267 @default.
- W2000598742 cites W2053792843 @default.
- W2000598742 cites W2070897505 @default.
- W2000598742 cites W2318383382 @default.
- W2000598742 doi "https://doi.org/10.1116/1.4865808" @default.
- W2000598742 hasPublicationYear "2014" @default.
- W2000598742 type Work @default.
- W2000598742 sameAs 2000598742 @default.
- W2000598742 citedByCount "0" @default.
- W2000598742 crossrefType "journal-article" @default.
- W2000598742 hasAuthorship W2000598742A5000275104 @default.
- W2000598742 hasAuthorship W2000598742A5026709814 @default.
- W2000598742 hasAuthorship W2000598742A5057758904 @default.
- W2000598742 hasAuthorship W2000598742A5061320453 @default.
- W2000598742 hasAuthorship W2000598742A5080836379 @default.
- W2000598742 hasAuthorship W2000598742A5081762612 @default.
- W2000598742 hasConcept C113196181 @default.
- W2000598742 hasConcept C121332964 @default.
- W2000598742 hasConcept C145148216 @default.
- W2000598742 hasConcept C150493377 @default.
- W2000598742 hasConcept C161790260 @default.
- W2000598742 hasConcept C178790620 @default.
- W2000598742 hasConcept C185592680 @default.
- W2000598742 hasConcept C192562407 @default.
- W2000598742 hasConcept C43617362 @default.
- W2000598742 hasConcept C49040817 @default.
- W2000598742 hasConcept C543292547 @default.
- W2000598742 hasConcept C55493867 @default.
- W2000598742 hasConcept C57863236 @default.
- W2000598742 hasConcept C59061564 @default.
- W2000598742 hasConcept C62520636 @default.
- W2000598742 hasConcept C69990965 @default.
- W2000598742 hasConcept C74575197 @default.
- W2000598742 hasConceptScore W2000598742C113196181 @default.
- W2000598742 hasConceptScore W2000598742C121332964 @default.
- W2000598742 hasConceptScore W2000598742C145148216 @default.
- W2000598742 hasConceptScore W2000598742C150493377 @default.
- W2000598742 hasConceptScore W2000598742C161790260 @default.
- W2000598742 hasConceptScore W2000598742C178790620 @default.
- W2000598742 hasConceptScore W2000598742C185592680 @default.
- W2000598742 hasConceptScore W2000598742C192562407 @default.
- W2000598742 hasConceptScore W2000598742C43617362 @default.
- W2000598742 hasConceptScore W2000598742C49040817 @default.
- W2000598742 hasConceptScore W2000598742C543292547 @default.
- W2000598742 hasConceptScore W2000598742C55493867 @default.
- W2000598742 hasConceptScore W2000598742C57863236 @default.
- W2000598742 hasConceptScore W2000598742C59061564 @default.
- W2000598742 hasConceptScore W2000598742C62520636 @default.
- W2000598742 hasConceptScore W2000598742C69990965 @default.
- W2000598742 hasConceptScore W2000598742C74575197 @default.
- W2000598742 hasIssue "2" @default.
- W2000598742 hasLocation W20005987421 @default.
- W2000598742 hasOpenAccess W2000598742 @default.
- W2000598742 hasPrimaryLocation W20005987421 @default.
- W2000598742 hasRelatedWork W2050581041 @default.
- W2000598742 hasRelatedWork W2068086501 @default.
- W2000598742 hasRelatedWork W2187648595 @default.
- W2000598742 hasRelatedWork W2338073499 @default.
- W2000598742 hasRelatedWork W2600077805 @default.
- W2000598742 hasRelatedWork W2923388388 @default.
- W2000598742 hasRelatedWork W3109494280 @default.
- W2000598742 hasRelatedWork W4312244319 @default.
- W2000598742 hasRelatedWork W2132364722 @default.
- W2000598742 hasRelatedWork W2619132286 @default.
- W2000598742 hasVolume "32" @default.
- W2000598742 isParatext "false" @default.
- W2000598742 isRetracted "false" @default.
- W2000598742 magId "2000598742" @default.
- W2000598742 workType "article" @default.