- W2000773318 abstract "ZrB 2 -Cu composite is a new electrical contact materials in the integration of high conductivity, high wear resistance and good mechanical strength. In this paper, ZrB 2 -Cu composites were prepared by hot-pressing sintering at 800~900 °C under a pressure of 20 MPa.The densification of ZrB 2 -Cu composites was improved by the addition of nickel using an electroless metal plating technique. X-ray diffraction and scan electron microscopy were used to analyze the phase and microstructure of ZrB 2 -Cu composites. The results showed that ZrB 2 -Cu composites with 60 vol % Cu which was sintered at 900 °C had a higher relative density, highest flexural strength of 381 MPa and higher hardness of 2.16 GPa(HV). ZrB 2 -Cu composites with 50 vol % Cu which was sintered at 900 °C had higher flexural strength of 297 MPa and the highest hardness of 2.66 GPa." @default.
- W2000773318 created "2016-06-24" @default.
- W2000773318 creator A5015060674 @default.
- W2000773318 creator A5019348338 @default.
- W2000773318 creator A5053161407 @default.
- W2000773318 creator A5065037360 @default.
- W2000773318 creator A5066491158 @default.
- W2000773318 creator A5072547549 @default.
- W2000773318 creator A5078786255 @default.
- W2000773318 creator A5082121435 @default.
- W2000773318 creator A5085296032 @default.
- W2000773318 date "2014-03-01" @default.
- W2000773318 modified "2023-09-27" @default.
- W2000773318 title "Processing and Properties of ZrB<sub>2</sub>-Cu Composites Sintered by Hot-Pressing Sintering" @default.
- W2000773318 cites W1605646627 @default.
- W2000773318 cites W1997748031 @default.
- W2000773318 cites W2000576158 @default.
- W2000773318 cites W2003921363 @default.
- W2000773318 cites W2003969448 @default.
- W2000773318 cites W2006323391 @default.
- W2000773318 cites W2020222101 @default.
- W2000773318 cites W2021714042 @default.
- W2000773318 cites W2042647297 @default.
- W2000773318 cites W2048207270 @default.
- W2000773318 cites W2088527807 @default.
- W2000773318 cites W2090277028 @default.
- W2000773318 cites W2135986023 @default.
- W2000773318 doi "https://doi.org/10.4028/www.scientific.net/kem.602-603.447" @default.
- W2000773318 hasPublicationYear "2014" @default.
- W2000773318 type Work @default.
- W2000773318 sameAs 2000773318 @default.
- W2000773318 citedByCount "2" @default.
- W2000773318 countsByYear W20007733182019 @default.
- W2000773318 countsByYear W20007733182020 @default.
- W2000773318 crossrefType "journal-article" @default.
- W2000773318 hasAuthorship W2000773318A5015060674 @default.
- W2000773318 hasAuthorship W2000773318A5019348338 @default.
- W2000773318 hasAuthorship W2000773318A5053161407 @default.
- W2000773318 hasAuthorship W2000773318A5065037360 @default.
- W2000773318 hasAuthorship W2000773318A5066491158 @default.
- W2000773318 hasAuthorship W2000773318A5072547549 @default.
- W2000773318 hasAuthorship W2000773318A5078786255 @default.
- W2000773318 hasAuthorship W2000773318A5082121435 @default.
- W2000773318 hasAuthorship W2000773318A5085296032 @default.
- W2000773318 hasConcept C104779481 @default.
- W2000773318 hasConcept C159985019 @default.
- W2000773318 hasConcept C178405089 @default.
- W2000773318 hasConcept C191897082 @default.
- W2000773318 hasConcept C192562407 @default.
- W2000773318 hasConcept C26771246 @default.
- W2000773318 hasConcept C2776578615 @default.
- W2000773318 hasConcept C2777581544 @default.
- W2000773318 hasConcept C504270822 @default.
- W2000773318 hasConcept C82455628 @default.
- W2000773318 hasConcept C87976508 @default.
- W2000773318 hasConceptScore W2000773318C104779481 @default.
- W2000773318 hasConceptScore W2000773318C159985019 @default.
- W2000773318 hasConceptScore W2000773318C178405089 @default.
- W2000773318 hasConceptScore W2000773318C191897082 @default.
- W2000773318 hasConceptScore W2000773318C192562407 @default.
- W2000773318 hasConceptScore W2000773318C26771246 @default.
- W2000773318 hasConceptScore W2000773318C2776578615 @default.
- W2000773318 hasConceptScore W2000773318C2777581544 @default.
- W2000773318 hasConceptScore W2000773318C504270822 @default.
- W2000773318 hasConceptScore W2000773318C82455628 @default.
- W2000773318 hasConceptScore W2000773318C87976508 @default.
- W2000773318 hasLocation W20007733181 @default.
- W2000773318 hasOpenAccess W2000773318 @default.
- W2000773318 hasPrimaryLocation W20007733181 @default.
- W2000773318 hasRelatedWork W1539994931 @default.
- W2000773318 hasRelatedWork W1881464162 @default.
- W2000773318 hasRelatedWork W1964172946 @default.
- W2000773318 hasRelatedWork W1992300008 @default.
- W2000773318 hasRelatedWork W2026896546 @default.
- W2000773318 hasRelatedWork W2034939499 @default.
- W2000773318 hasRelatedWork W2036143556 @default.
- W2000773318 hasRelatedWork W2037673641 @default.
- W2000773318 hasRelatedWork W2042576283 @default.
- W2000773318 hasRelatedWork W2078503657 @default.
- W2000773318 hasRelatedWork W2079646566 @default.
- W2000773318 hasRelatedWork W2246198057 @default.
- W2000773318 hasRelatedWork W2393520902 @default.
- W2000773318 hasRelatedWork W2540066325 @default.
- W2000773318 hasRelatedWork W2562268712 @default.
- W2000773318 hasRelatedWork W2572606550 @default.
- W2000773318 hasRelatedWork W2908274695 @default.
- W2000773318 hasRelatedWork W3025531648 @default.
- W2000773318 hasRelatedWork W318029349 @default.
- W2000773318 hasRelatedWork W3204708717 @default.
- W2000773318 isParatext "false" @default.
- W2000773318 isRetracted "false" @default.
- W2000773318 magId "2000773318" @default.
- W2000773318 workType "article" @default.