- W2000867897 abstract "Two main types of fiberboards were produced using lauan (Shorea spp.) fibers with an isocyanate resin as the binder; fiberboard with a flat, homogeneous (homoprofile), and typical U-shaped (conventional) density profile along the board thickness. The processing parameters included manipulation of mat moisture content distribution, press closing speed, and hot pressing method. The results are summarized as follows: (1) A larger variation was observed in the peak density (PD) and core density (CD) of fiberboards at 0.5g/cm3 mean density (MD) level than in those at 0.7 g/cm3. Generally, PD showed a greater variation than CD, irrespective of MD level. (2) Boards produced using two-step hot pressing recorded substantially higher PD with reduced CD. (3) Multiple regression analysis showed that CD and PD could be calculated based on the other profile defining factors, and a rough estimation for peak distance and gradient factor was possible. (4) Based on static bending, conventional fiberboard had a higher modulus of rupture (MOR) than the homo-profile board but a similar modulus of elasticity (MOE). (5) At 0.5 g/cm3 the MOR and dynamic MOE of fiberboard increased by up to 67% and 62%, respectively, when the PD increased from 0.5 to 1.07 g/cm3. Similarly, an increase of PD from 0.7 to 1.1 g/cm3 resulted in corresponding increases of 55% and 34% in the MOR and dynamic MOE of 0.7 g/cm3 boards. (6) The internal bond strength and screw withdrawal resistance were almost entirely dependent on the CD and MD, respectively. (7) Homo-profile fiberboards registered higher thickness swelling and water absorption than conventional fiberboards throughout the dry/wet conditioning cycle." @default.
- W2000867897 created "2016-06-24" @default.
- W2000867897 creator A5011427197 @default.
- W2000867897 creator A5041886510 @default.
- W2000867897 creator A5046225712 @default.
- W2000867897 creator A5050350398 @default.
- W2000867897 creator A5053204257 @default.
- W2000867897 date "2000-06-01" @default.
- W2000867897 modified "2023-09-25" @default.
- W2000867897 title "Formation of the density profile and its effects on the properties of fiberboard" @default.
- W2000867897 cites W2056766479 @default.
- W2000867897 cites W2167741093 @default.
- W2000867897 cites W3198565243 @default.
- W2000867897 doi "https://doi.org/10.1007/bf00776450" @default.
- W2000867897 hasPublicationYear "2000" @default.
- W2000867897 type Work @default.
- W2000867897 sameAs 2000867897 @default.
- W2000867897 citedByCount "39" @default.
- W2000867897 countsByYear W20008678972012 @default.
- W2000867897 countsByYear W20008678972013 @default.
- W2000867897 countsByYear W20008678972014 @default.
- W2000867897 countsByYear W20008678972015 @default.
- W2000867897 countsByYear W20008678972016 @default.
- W2000867897 countsByYear W20008678972018 @default.
- W2000867897 countsByYear W20008678972020 @default.
- W2000867897 countsByYear W20008678972021 @default.
- W2000867897 countsByYear W20008678972022 @default.
- W2000867897 countsByYear W20008678972023 @default.
- W2000867897 crossrefType "journal-article" @default.
- W2000867897 hasAuthorship W2000867897A5011427197 @default.
- W2000867897 hasAuthorship W2000867897A5041886510 @default.
- W2000867897 hasAuthorship W2000867897A5046225712 @default.
- W2000867897 hasAuthorship W2000867897A5050350398 @default.
- W2000867897 hasAuthorship W2000867897A5053204257 @default.
- W2000867897 hasBestOaLocation W20008678971 @default.
- W2000867897 hasConcept C114614502 @default.
- W2000867897 hasConcept C159985019 @default.
- W2000867897 hasConcept C176864760 @default.
- W2000867897 hasConcept C178405089 @default.
- W2000867897 hasConcept C192562407 @default.
- W2000867897 hasConcept C196029304 @default.
- W2000867897 hasConcept C2776177134 @default.
- W2000867897 hasConcept C2993236451 @default.
- W2000867897 hasConcept C33923547 @default.
- W2000867897 hasConcept C66882249 @default.
- W2000867897 hasConcept C93021684 @default.
- W2000867897 hasConceptScore W2000867897C114614502 @default.
- W2000867897 hasConceptScore W2000867897C159985019 @default.
- W2000867897 hasConceptScore W2000867897C176864760 @default.
- W2000867897 hasConceptScore W2000867897C178405089 @default.
- W2000867897 hasConceptScore W2000867897C192562407 @default.
- W2000867897 hasConceptScore W2000867897C196029304 @default.
- W2000867897 hasConceptScore W2000867897C2776177134 @default.
- W2000867897 hasConceptScore W2000867897C2993236451 @default.
- W2000867897 hasConceptScore W2000867897C33923547 @default.
- W2000867897 hasConceptScore W2000867897C66882249 @default.
- W2000867897 hasConceptScore W2000867897C93021684 @default.
- W2000867897 hasIssue "3" @default.
- W2000867897 hasLocation W20008678971 @default.
- W2000867897 hasOpenAccess W2000867897 @default.
- W2000867897 hasPrimaryLocation W20008678971 @default.
- W2000867897 hasRelatedWork W2009845471 @default.
- W2000867897 hasRelatedWork W2025687592 @default.
- W2000867897 hasRelatedWork W2360688981 @default.
- W2000867897 hasRelatedWork W2371089163 @default.
- W2000867897 hasRelatedWork W2387542655 @default.
- W2000867897 hasRelatedWork W2471105796 @default.
- W2000867897 hasRelatedWork W2789571739 @default.
- W2000867897 hasRelatedWork W2944045227 @default.
- W2000867897 hasRelatedWork W3003882707 @default.
- W2000867897 hasRelatedWork W2560560155 @default.
- W2000867897 hasVolume "46" @default.
- W2000867897 isParatext "false" @default.
- W2000867897 isRetracted "false" @default.
- W2000867897 magId "2000867897" @default.
- W2000867897 workType "article" @default.