- W2001650607 abstract "In a previous paper, it was demonstrated that the measurement of cathodic delamination by the Scanning Kelvin Probe can assess the interface stability of poly(vinyl butyral) (PVB) coated steel after field exposure. This technique was utilized to characterize the degradation of the polymer/metal interface in several outdoor climates. In this paper, the effects of environmental factors on the interface degradation were investigated in the laboratory. The mechanisms measured in the field were reproduced to provide input in the development of an appropriate accelerated test for PVB coated steel. The ASTM B117 and G154 standardized tests were investigated individually and sequentially. The interface stability improved after 24 h of ASTM G154 exposure. After 144 h of exposure to ASTM G154 exposure, polymer oxidation took place simultaneously with interface degradation. The condensation phase of the ASTM G154 test was responsible for the interface improvement while the ultraviolet radiation triggered the interface degradation. Pre-exposure to ASTM G154 delayed wet de-adhesion during ASTM B117 exposure. After wet de-adhesion caused by 6 h of ASTM B117, exposure to ASTM G154 for 24 h increased the interface stability. The effects of ultraviolet radiation, relative humidity, temperature and environment on interface degradation were investigated in a special chamber. Humidity was the primary factor found to influence the interface improvement during G154 exposure. A wet/dry salt fog cycle with irradiation by an ultraviolet or filtered xenon arc lamp around room temperature was suggested to reproduce the competition between the interface improvement and the interface degradation that takes place in the field." @default.
- W2001650607 created "2016-06-24" @default.
- W2001650607 creator A5012602129 @default.
- W2001650607 creator A5032235380 @default.
- W2001650607 date "2014-08-01" @default.
- W2001650607 modified "2023-09-23" @default.
- W2001650607 title "Coating and Interface Degradation of Coated steel, Part 2: Accelerated Laboratory Tests" @default.
- W2001650607 cites W1991852723 @default.
- W2001650607 cites W1999740150 @default.
- W2001650607 cites W2025569233 @default.
- W2001650607 cites W2029998511 @default.
- W2001650607 cites W2061478449 @default.
- W2001650607 cites W2063572373 @default.
- W2001650607 cites W2065657110 @default.
- W2001650607 cites W2069373601 @default.
- W2001650607 cites W2075828264 @default.
- W2001650607 cites W2083874738 @default.
- W2001650607 cites W2119996425 @default.
- W2001650607 cites W2149999846 @default.
- W2001650607 cites W2153462635 @default.
- W2001650607 cites W4205107684 @default.
- W2001650607 cites W4255412919 @default.
- W2001650607 doi "https://doi.org/10.1016/j.electacta.2014.05.111" @default.
- W2001650607 hasPublicationYear "2014" @default.
- W2001650607 type Work @default.
- W2001650607 sameAs 2001650607 @default.
- W2001650607 citedByCount "12" @default.
- W2001650607 countsByYear W20016506072014 @default.
- W2001650607 countsByYear W20016506072016 @default.
- W2001650607 countsByYear W20016506072018 @default.
- W2001650607 countsByYear W20016506072019 @default.
- W2001650607 countsByYear W20016506072020 @default.
- W2001650607 countsByYear W20016506072021 @default.
- W2001650607 countsByYear W20016506072022 @default.
- W2001650607 crossrefType "journal-article" @default.
- W2001650607 hasAuthorship W2001650607A5012602129 @default.
- W2001650607 hasAuthorship W2001650607A5032235380 @default.
- W2001650607 hasConcept C118820876 @default.
- W2001650607 hasConcept C119599485 @default.
- W2001650607 hasConcept C121332964 @default.
- W2001650607 hasConcept C127413603 @default.
- W2001650607 hasConcept C151730666 @default.
- W2001650607 hasConcept C153294291 @default.
- W2001650607 hasConcept C158960510 @default.
- W2001650607 hasConcept C159985019 @default.
- W2001650607 hasConcept C192562407 @default.
- W2001650607 hasConcept C2779679103 @default.
- W2001650607 hasConcept C2781448156 @default.
- W2001650607 hasConcept C30239060 @default.
- W2001650607 hasConcept C58097730 @default.
- W2001650607 hasConcept C77928131 @default.
- W2001650607 hasConcept C86803240 @default.
- W2001650607 hasConceptScore W2001650607C118820876 @default.
- W2001650607 hasConceptScore W2001650607C119599485 @default.
- W2001650607 hasConceptScore W2001650607C121332964 @default.
- W2001650607 hasConceptScore W2001650607C127413603 @default.
- W2001650607 hasConceptScore W2001650607C151730666 @default.
- W2001650607 hasConceptScore W2001650607C153294291 @default.
- W2001650607 hasConceptScore W2001650607C158960510 @default.
- W2001650607 hasConceptScore W2001650607C159985019 @default.
- W2001650607 hasConceptScore W2001650607C192562407 @default.
- W2001650607 hasConceptScore W2001650607C2779679103 @default.
- W2001650607 hasConceptScore W2001650607C2781448156 @default.
- W2001650607 hasConceptScore W2001650607C30239060 @default.
- W2001650607 hasConceptScore W2001650607C58097730 @default.
- W2001650607 hasConceptScore W2001650607C77928131 @default.
- W2001650607 hasConceptScore W2001650607C86803240 @default.
- W2001650607 hasLocation W20016506071 @default.
- W2001650607 hasOpenAccess W2001650607 @default.
- W2001650607 hasPrimaryLocation W20016506071 @default.
- W2001650607 hasRelatedWork W2082293200 @default.
- W2001650607 hasRelatedWork W2137307547 @default.
- W2001650607 hasRelatedWork W2380293314 @default.
- W2001650607 hasRelatedWork W2744957166 @default.
- W2001650607 hasRelatedWork W2943188944 @default.
- W2001650607 hasRelatedWork W3008690834 @default.
- W2001650607 hasRelatedWork W3036809288 @default.
- W2001650607 hasRelatedWork W3082440218 @default.
- W2001650607 hasRelatedWork W4242480814 @default.
- W2001650607 hasRelatedWork W4285802202 @default.
- W2001650607 hasVolume "136" @default.
- W2001650607 isParatext "false" @default.
- W2001650607 isRetracted "false" @default.
- W2001650607 magId "2001650607" @default.
- W2001650607 workType "article" @default.