- W2004684090 abstract "A porous alumina body was synthesized from anisotropic alumina particles (platelets). The uniaxial pressure in fabricating the green compact body had an influence on the relative density of the alumina body after heating. When green compacts, which had been uniaxially pressed at 1 and 3 MPa, were heated at 1400 °C for 1 h, the relative densities of the resulting alumina bodies were 25.0% and 35.5%, respectively. The compressive strength of compacts that were uniaxially pressed at 1 and 3 MPa were 0.8 and 4.3 MPa, respectively. In an attempt to increase the compressive strength of these porous alumina bodies, aluminum nitrate and magnesium nitrate solution treatments were performed, followed by reheating to 1400 °C for 1 h. When a 0.5 mol/l aluminum nitrate solution was used, the compressive strength of the porous alumina body uniaxially pressed at 1 MPa changed from 0.8 MPa (without solution treatment) to 1.5 MPa. Furthermore, when 0.1 mol/l magnesium nitrate solution was used, the compressive strength of the porous alumina increased to 1.7 MPa. Thus, solution treatment of the porous alumina body had a strong positive effect on its mechanical strength." @default.
- W2004684090 created "2016-06-24" @default.
- W2004684090 creator A5017941349 @default.
- W2004684090 creator A5019538225 @default.
- W2004684090 creator A5022043890 @default.
- W2004684090 creator A5022341389 @default.
- W2004684090 creator A5024786313 @default.
- W2004684090 creator A5051323124 @default.
- W2004684090 date "2010-02-01" @default.
- W2004684090 modified "2023-09-26" @default.
- W2004684090 title "Synthesis and mechanical properties of porous alumina from anisotropic alumina particles" @default.
- W2004684090 cites W1870647091 @default.
- W2004684090 cites W1964219496 @default.
- W2004684090 cites W1981342195 @default.
- W2004684090 cites W1987562431 @default.
- W2004684090 cites W2022177129 @default.
- W2004684090 cites W2027832347 @default.
- W2004684090 cites W2044992865 @default.
- W2004684090 cites W2062355080 @default.
- W2004684090 cites W2080977785 @default.
- W2004684090 cites W2090686237 @default.
- W2004684090 doi "https://doi.org/10.1016/j.jeurceramsoc.2009.09.018" @default.
- W2004684090 hasPublicationYear "2010" @default.
- W2004684090 type Work @default.
- W2004684090 sameAs 2004684090 @default.
- W2004684090 citedByCount "20" @default.
- W2004684090 countsByYear W20046840902013 @default.
- W2004684090 countsByYear W20046840902014 @default.
- W2004684090 countsByYear W20046840902016 @default.
- W2004684090 countsByYear W20046840902017 @default.
- W2004684090 countsByYear W20046840902018 @default.
- W2004684090 countsByYear W20046840902019 @default.
- W2004684090 countsByYear W20046840902020 @default.
- W2004684090 countsByYear W20046840902021 @default.
- W2004684090 countsByYear W20046840902022 @default.
- W2004684090 countsByYear W20046840902023 @default.
- W2004684090 crossrefType "journal-article" @default.
- W2004684090 hasAuthorship W2004684090A5017941349 @default.
- W2004684090 hasAuthorship W2004684090A5019538225 @default.
- W2004684090 hasAuthorship W2004684090A5022043890 @default.
- W2004684090 hasAuthorship W2004684090A5022341389 @default.
- W2004684090 hasAuthorship W2004684090A5024786313 @default.
- W2004684090 hasAuthorship W2004684090A5051323124 @default.
- W2004684090 hasConcept C159985019 @default.
- W2004684090 hasConcept C191897082 @default.
- W2004684090 hasConcept C192562407 @default.
- W2004684090 hasConcept C2780347548 @default.
- W2004684090 hasConcept C30407753 @default.
- W2004684090 hasConcept C513153333 @default.
- W2004684090 hasConcept C543218039 @default.
- W2004684090 hasConcept C6648577 @default.
- W2004684090 hasConcept C82455628 @default.
- W2004684090 hasConcept C87976508 @default.
- W2004684090 hasConceptScore W2004684090C159985019 @default.
- W2004684090 hasConceptScore W2004684090C191897082 @default.
- W2004684090 hasConceptScore W2004684090C192562407 @default.
- W2004684090 hasConceptScore W2004684090C2780347548 @default.
- W2004684090 hasConceptScore W2004684090C30407753 @default.
- W2004684090 hasConceptScore W2004684090C513153333 @default.
- W2004684090 hasConceptScore W2004684090C543218039 @default.
- W2004684090 hasConceptScore W2004684090C6648577 @default.
- W2004684090 hasConceptScore W2004684090C82455628 @default.
- W2004684090 hasConceptScore W2004684090C87976508 @default.
- W2004684090 hasIssue "3" @default.
- W2004684090 hasLocation W20046840901 @default.
- W2004684090 hasOpenAccess W2004684090 @default.
- W2004684090 hasPrimaryLocation W20046840901 @default.
- W2004684090 hasRelatedWork W2036712022 @default.
- W2004684090 hasRelatedWork W2055614860 @default.
- W2004684090 hasRelatedWork W2085037210 @default.
- W2004684090 hasRelatedWork W2121036907 @default.
- W2004684090 hasRelatedWork W2137307547 @default.
- W2004684090 hasRelatedWork W2380293314 @default.
- W2004684090 hasRelatedWork W2897188233 @default.
- W2004684090 hasRelatedWork W2905992715 @default.
- W2004684090 hasRelatedWork W2943188944 @default.
- W2004684090 hasRelatedWork W3082440218 @default.
- W2004684090 hasVolume "30" @default.
- W2004684090 isParatext "false" @default.
- W2004684090 isRetracted "false" @default.
- W2004684090 magId "2004684090" @default.
- W2004684090 workType "article" @default.