• W2005079377 abstract "Fatigue properties of bainitic 100Cr6 (SAE 52100, JIS SUJ2) steel are investigated in the high cycle and very high cycle fatigue (VHCF) regime. Fully reversed tension–compression fatigue tests are performed with ultrasonic fatigue testing equipment. Specimens are grinded which leads to surface compression stresses and increased surface roughness. About 1/3 of the specimens failed after crack initiation at interior Al2O3− or TiN-inclusions and 2/3 failed after surface crack initiation at scratches or cavities. When inclusions are considered as cracks, failures can occur at minimum stress intensity range of 2.8 MPa m1/2, and maximum stress intensity range without failure is 3.3 MPa m1/2. Facets are visible close to the inclusion in some specimens, and the stress intensity range at the border of the facet is approximately 4.5 MPa m1/2. Murakami’s model can well predict the endurance limit at 109 cycles for internal failures considering the area of the inclusion in the evaluation. Surface fatigue crack initiation can lead to failure above 108 cycles. When scratches are considered as cracks, minimum stress intensity range of 2.5 MPa m1/2 can propagate surface cracks to failure. Fracture mechanics approach showed several similarities to literature results of the same material tested in tempered martensite condition." @default.
• W2005079377 created "2016-06-24" @default.
• W2005079377 creator A5001160134 @default.
• W2005079377 creator A5031431089 @default.
• W2005079377 creator A5032652204 @default.
• W2005079377 creator A5040543245 @default.
• W2005079377 creator A5044220483 @default.
• W2005079377 creator A5070872174 @default.
• W2005079377 date "2009-02-01" @default.
• W2005079377 modified "2023-10-18" @default.
• W2005079377 title "Very high cycle fatigue properties of bainitic high carbon–chromium steel" @default.
• W2005079377 cites W103769932 @default.
• W2005079377 cites W1535659778 @default.
• W2005079377 cites W1977789213 @default.
• W2005079377 cites W1977840992 @default.
• W2005079377 cites W1984716245 @default.
• W2005079377 cites W1984905865 @default.
• W2005079377 cites W1988421830 @default.
• W2005079377 cites W2000914789 @default.
• W2005079377 cites W2015211316 @default.
• W2005079377 cites W2019055674 @default.
• W2005079377 cites W2032351011 @default.
• W2005079377 cites W2034845912 @default.
• W2005079377 cites W2036130541 @default.
• W2005079377 cites W2044183219 @default.
• W2005079377 cites W2044780784 @default.
• W2005079377 cites W2044933282 @default.
• W2005079377 cites W2047860270 @default.
• W2005079377 cites W2049439236 @default.
• W2005079377 cites W2077728731 @default.
• W2005079377 cites W2093128091 @default.
• W2005079377 cites W2094104349 @default.
• W2005079377 cites W2094984431 @default.
• W2005079377 cites W2122899804 @default.
• W2005079377 cites W2127402552 @default.
• W2005079377 cites W2129120933 @default.
• W2005079377 cites W2139483581 @default.
• W2005079377 cites W2148016987 @default.
• W2005079377 cites W2171108863 @default.
• W2005079377 cites W2981224554 @default.
• W2005079377 cites W3049191061 @default.
• W2005079377 cites W2505814459 @default.
• W2005079377 doi "https://doi.org/10.1016/j.ijfatigue.2008.09.001" @default.
• W2005079377 hasPublicationYear "2009" @default.
• W2005079377 type Work @default.
• W2005079377 sameAs 2005079377 @default.
• W2005079377 citedByCount "114" @default.
• W2005079377 countsByYear W20050793772012 @default.
• W2005079377 countsByYear W20050793772013 @default.
• W2005079377 countsByYear W20050793772014 @default.
• W2005079377 countsByYear W20050793772015 @default.
• W2005079377 countsByYear W20050793772016 @default.
• W2005079377 countsByYear W20050793772017 @default.
• W2005079377 countsByYear W20050793772018 @default.
• W2005079377 countsByYear W20050793772019 @default.
• W2005079377 countsByYear W20050793772020 @default.
• W2005079377 countsByYear W20050793772021 @default.
• W2005079377 countsByYear W20050793772022 @default.
• W2005079377 countsByYear W20050793772023 @default.
• W2005079377 crossrefType "journal-article" @default.
• W2005079377 hasAuthorship W2005079377A5001160134 @default.
• W2005079377 hasAuthorship W2005079377A5031431089 @default.
• W2005079377 hasAuthorship W2005079377A5032652204 @default.
• W2005079377 hasAuthorship W2005079377A5040543245 @default.
• W2005079377 hasAuthorship W2005079377A5044220483 @default.
• W2005079377 hasAuthorship W2005079377A5070872174 @default.
• W2005079377 hasConcept C107365816 @default.
• W2005079377 hasConcept C121332964 @default.
• W2005079377 hasConcept C131850400 @default.
• W2005079377 hasConcept C138885662 @default.
• W2005079377 hasConcept C159985019 @default.
• W2005079377 hasConcept C180016635 @default.
• W2005079377 hasConcept C18747287 @default.
• W2005079377 hasConcept C191897082 @default.
• W2005079377 hasConcept C192562407 @default.
• W2005079377 hasConcept C21036866 @default.
• W2005079377 hasConcept C28539199 @default.
• W2005079377 hasConcept C2985278600 @default.
• W2005079377 hasConcept C41895202 @default.
• W2005079377 hasConcept C54303661 @default.
• W2005079377 hasConcept C59085676 @default.
• W2005079377 hasConcept C62520636 @default.
• W2005079377 hasConcept C87976508 @default.
• W2005079377 hasConcept C93038891 @default.
• W2005079377 hasConceptScore W2005079377C107365816 @default.
• W2005079377 hasConceptScore W2005079377C121332964 @default.
• W2005079377 hasConceptScore W2005079377C131850400 @default.
• W2005079377 hasConceptScore W2005079377C138885662 @default.
• W2005079377 hasConceptScore W2005079377C159985019 @default.
• W2005079377 hasConceptScore W2005079377C180016635 @default.
• W2005079377 hasConceptScore W2005079377C18747287 @default.
• W2005079377 hasConceptScore W2005079377C191897082 @default.
• W2005079377 hasConceptScore W2005079377C192562407 @default.
• W2005079377 hasConceptScore W2005079377C21036866 @default.
• W2005079377 hasConceptScore W2005079377C28539199 @default.
• W2005079377 hasConceptScore W2005079377C2985278600 @default.
• W2005079377 hasConceptScore W2005079377C41895202 @default.
• W2005079377 hasConceptScore W2005079377C54303661 @default.

• next