- W2005765718 abstract "This is the second in a series of papers in which the thermal degradation of ethylene-vinyl acetate (EVA) and ethylene-butyl acrylate (EBA) copolymers are compared. The EBA samples contain 0.8, 1.6, and 5.4 mol % butyl acrylate (BA), respectively, and the EVA samples 1.2 and 6.7 mol % vinyl acetate (VA). The samples were heated in nitrogen in a tubular oven at 285, 333, 350, 370 and 390°C for 6–120 min. The samples were analyzed with IR, NMR, gravimetry, and titration of carboxylic groups. The EVA samples were rapidly degraded by deacetylation, which was complete after about 30 min at 333°C. A linear relation between the loss of acetate groups and the formation of trans double bonds was found. A small amount of keto groups and traces of lactones were also observed. The data confirm the previously proposed mechanisms for deacetylation and the formation of acetaldehyde. A mechanism for lactone formation is suggested. The deacetylation rate is increasing with the VA content, presumably because of an increased amount of block sequences and an enhanced acid catalytic effect. The acrylate sidegroups are much more stable than the acetate groups, and are similar in stability to the main hydrocarbon chain. The BA decomposition results in carboxylic and anhydride groups. Decarboxylation also occur and increases with the thermal treatment. In LDPE and EBA the increase in unsaturation is small and mainly due to vinyl end groups formed via β-cleavage or disproportionation. In EVA the formation of vinyl end groups is suppressed." @default.
- W2005765718 created "2016-06-24" @default.
- W2005765718 creator A5007092192 @default.
- W2005765718 creator A5037034168 @default.
- W2005765718 date "1991-11-05" @default.
- W2005765718 modified "2023-10-03" @default.
- W2005765718 title "Thermal degradation of EVA and EBA—A comparison. II. Changes in unsaturation and side group structure" @default.
- W2005765718 doi "https://doi.org/10.1002/app.1991.070430918" @default.
- W2005765718 hasPublicationYear "1991" @default.
- W2005765718 type Work @default.
- W2005765718 sameAs 2005765718 @default.
- W2005765718 citedByCount "39" @default.
- W2005765718 countsByYear W20057657182012 @default.
- W2005765718 countsByYear W20057657182015 @default.
- W2005765718 countsByYear W20057657182016 @default.
- W2005765718 countsByYear W20057657182017 @default.
- W2005765718 countsByYear W20057657182020 @default.
- W2005765718 countsByYear W20057657182022 @default.
- W2005765718 crossrefType "journal-article" @default.
- W2005765718 hasAuthorship W2005765718A5007092192 @default.
- W2005765718 hasAuthorship W2005765718A5037034168 @default.
- W2005765718 hasConcept C15920480 @default.
- W2005765718 hasConcept C161790260 @default.
- W2005765718 hasConcept C178790620 @default.
- W2005765718 hasConcept C185592680 @default.
- W2005765718 hasConcept C188027245 @default.
- W2005765718 hasConcept C201268389 @default.
- W2005765718 hasConcept C2776093513 @default.
- W2005765718 hasConcept C2778597550 @default.
- W2005765718 hasConcept C2779989194 @default.
- W2005765718 hasConcept C2780076828 @default.
- W2005765718 hasConcept C521977710 @default.
- W2005765718 hasConcept C59061564 @default.
- W2005765718 hasConceptScore W2005765718C15920480 @default.
- W2005765718 hasConceptScore W2005765718C161790260 @default.
- W2005765718 hasConceptScore W2005765718C178790620 @default.
- W2005765718 hasConceptScore W2005765718C185592680 @default.
- W2005765718 hasConceptScore W2005765718C188027245 @default.
- W2005765718 hasConceptScore W2005765718C201268389 @default.
- W2005765718 hasConceptScore W2005765718C2776093513 @default.
- W2005765718 hasConceptScore W2005765718C2778597550 @default.
- W2005765718 hasConceptScore W2005765718C2779989194 @default.
- W2005765718 hasConceptScore W2005765718C2780076828 @default.
- W2005765718 hasConceptScore W2005765718C521977710 @default.
- W2005765718 hasConceptScore W2005765718C59061564 @default.
- W2005765718 hasIssue "9" @default.
- W2005765718 hasLocation W20057657181 @default.
- W2005765718 hasOpenAccess W2005765718 @default.
- W2005765718 hasPrimaryLocation W20057657181 @default.
- W2005765718 hasRelatedWork W1980529305 @default.
- W2005765718 hasRelatedWork W2001857553 @default.
- W2005765718 hasRelatedWork W2014114831 @default.
- W2005765718 hasRelatedWork W2026017645 @default.
- W2005765718 hasRelatedWork W2033464724 @default.
- W2005765718 hasRelatedWork W2101257968 @default.
- W2005765718 hasRelatedWork W2348314287 @default.
- W2005765718 hasRelatedWork W2361129114 @default.
- W2005765718 hasRelatedWork W2373865258 @default.
- W2005765718 hasRelatedWork W4312106221 @default.
- W2005765718 hasVolume "43" @default.
- W2005765718 isParatext "false" @default.
- W2005765718 isRetracted "false" @default.
- W2005765718 magId "2005765718" @default.
- W2005765718 workType "article" @default.