- W2007362272 abstract "The significance of the formation of thick oxide scales during exposure of Cr steels in steam-containing environments on the service life of components is discussed. The quantitative effects of the loss of load-bearing cross-section on the creep rupture life are presented. For tubes of 6 mm wall thickness, the reduction in rupture life due to material loss will be significant after comparatively short exposure times of 10 000 h at 600 °C. Potentially much more damaging is, however, the thermal insulation effect of the porous, thick oxide scales, which leads to overheating of heat transfer tubes. The higher metal temperatures will then lead to early failure by creep. The scale present after 10 000 h exposure in steam may be sufficient to cause a temperature increase of 50 K which will reduce the rupture time for a constant stress by a factor of 30. Oxide scale spalling can also lead to overheating due to the restriction of the flow inside tubes. The design should ensure that spalled oxide cannot accumulate inside the tubes." @default.
- W2007362272 created "2016-06-24" @default.
- W2007362272 creator A5087276005 @default.
- W2007362272 creator A5090041375 @default.
- W2007362272 date "2007-01-01" @default.
- W2007362272 modified "2023-09-26" @default.
- W2007362272 title "Implications of steam oxidation for the service life of high-strength martensitic steel components in high-temperature plant" @default.
- W2007362272 cites W2012307525 @default.
- W2007362272 cites W2053224068 @default.
- W2007362272 cites W2057285972 @default.
- W2007362272 cites W287590353 @default.
- W2007362272 doi "https://doi.org/10.1016/j.ijpvp.2006.09.008" @default.
- W2007362272 hasPublicationYear "2007" @default.
- W2007362272 type Work @default.
- W2007362272 sameAs 2007362272 @default.
- W2007362272 citedByCount "71" @default.
- W2007362272 countsByYear W20073622722012 @default.
- W2007362272 countsByYear W20073622722013 @default.
- W2007362272 countsByYear W20073622722014 @default.
- W2007362272 countsByYear W20073622722015 @default.
- W2007362272 countsByYear W20073622722016 @default.
- W2007362272 countsByYear W20073622722017 @default.
- W2007362272 countsByYear W20073622722018 @default.
- W2007362272 countsByYear W20073622722019 @default.
- W2007362272 countsByYear W20073622722020 @default.
- W2007362272 countsByYear W20073622722021 @default.
- W2007362272 countsByYear W20073622722022 @default.
- W2007362272 countsByYear W20073622722023 @default.
- W2007362272 crossrefType "journal-article" @default.
- W2007362272 hasAuthorship W2007362272A5087276005 @default.
- W2007362272 hasAuthorship W2007362272A5090041375 @default.
- W2007362272 hasConcept C103208741 @default.
- W2007362272 hasConcept C116915560 @default.
- W2007362272 hasConcept C127413603 @default.
- W2007362272 hasConcept C144133560 @default.
- W2007362272 hasConcept C159985019 @default.
- W2007362272 hasConcept C162853370 @default.
- W2007362272 hasConcept C18747287 @default.
- W2007362272 hasConcept C191897082 @default.
- W2007362272 hasConcept C192562407 @default.
- W2007362272 hasConcept C2780378061 @default.
- W2007362272 hasConcept C77595967 @default.
- W2007362272 hasConcept C87976508 @default.
- W2007362272 hasConceptScore W2007362272C103208741 @default.
- W2007362272 hasConceptScore W2007362272C116915560 @default.
- W2007362272 hasConceptScore W2007362272C127413603 @default.
- W2007362272 hasConceptScore W2007362272C144133560 @default.
- W2007362272 hasConceptScore W2007362272C159985019 @default.
- W2007362272 hasConceptScore W2007362272C162853370 @default.
- W2007362272 hasConceptScore W2007362272C18747287 @default.
- W2007362272 hasConceptScore W2007362272C191897082 @default.
- W2007362272 hasConceptScore W2007362272C192562407 @default.
- W2007362272 hasConceptScore W2007362272C2780378061 @default.
- W2007362272 hasConceptScore W2007362272C77595967 @default.
- W2007362272 hasConceptScore W2007362272C87976508 @default.
- W2007362272 hasIssue "1-2" @default.
- W2007362272 hasLocation W20073622721 @default.
- W2007362272 hasOpenAccess W2007362272 @default.
- W2007362272 hasPrimaryLocation W20073622721 @default.
- W2007362272 hasRelatedWork W2009381456 @default.
- W2007362272 hasRelatedWork W2014319677 @default.
- W2007362272 hasRelatedWork W2021423027 @default.
- W2007362272 hasRelatedWork W2034761211 @default.
- W2007362272 hasRelatedWork W2247050986 @default.
- W2007362272 hasRelatedWork W2369745116 @default.
- W2007362272 hasRelatedWork W2388183869 @default.
- W2007362272 hasRelatedWork W4313829337 @default.
- W2007362272 hasRelatedWork W814686861 @default.
- W2007362272 hasRelatedWork W2626967714 @default.
- W2007362272 hasVolume "84" @default.
- W2007362272 isParatext "false" @default.
- W2007362272 isRetracted "false" @default.
- W2007362272 magId "2007362272" @default.
- W2007362272 workType "article" @default.