- W2007717897 abstract "The effects of TiO2–SiO2 sol–gel coating with different firing temperatures (300 °C, 500 °C, and 750 °C) on the cpTi–porcelain bond strength were investigated in the present study. Prior to applying the low-fusing dental titanium porcelain, the phase, surface morphology, surface roughness and static water contact angle of the intermediate layer were evaluated. The cpTi–porcelain bond strength was measured using the three-point flexure test according to ISO 9693 standard. Statistical analyses were made using one-way ANOVA and Dunnett-t test. Significantly higher bond strength of TiO2–SiO2/750 °C (specimens coated with TiO2–SiO2 sol–gel coating and fired at 750 °C for 1 h) when compared to the control group was observed (p < 0.05). No rutile phase was found in all the tested specimens coated with TiO2–SiO2 sol–gel coating. The surface morphology of the intermediate layer was apparently different with different firing temperatures. It was found that the static water contact angle of TiO2–SiO2/750 °C significantly decreased (p < 0.05). However, no markedly different Ra of TiO2–SiO2/500 °C and TiO2–SiO2/750 °C in comparison to that of the control group was observed (p > 0.05). The results show that the TiO2–SiO2 sol–gel coating fired at 750 °C for 1 h can notably improve the cpTi–porcelain bond strength and may be suitable for clinical use." @default.
- W2007717897 created "2016-06-24" @default.
- W2007717897 creator A5009390740 @default.
- W2007717897 creator A5034558455 @default.
- W2007717897 creator A5047435768 @default.
- W2007717897 creator A5060842906 @default.
- W2007717897 creator A5073299519 @default.
- W2007717897 date "2011-04-01" @default.
- W2007717897 modified "2023-09-27" @default.
- W2007717897 title "Effect of TiO2–SiO2 sol–gel coating on the cpTi–porcelain bond strength" @default.
- W2007717897 cites W1978123225 @default.
- W2007717897 cites W1993025738 @default.
- W2007717897 cites W2007844974 @default.
- W2007717897 cites W2039901792 @default.
- W2007717897 cites W2056062976 @default.
- W2007717897 cites W2056213536 @default.
- W2007717897 cites W2062099782 @default.
- W2007717897 cites W2065711312 @default.
- W2007717897 cites W2068713804 @default.
- W2007717897 cites W2146027565 @default.
- W2007717897 cites W2161020201 @default.
- W2007717897 cites W2290963715 @default.
- W2007717897 cites W2332801375 @default.
- W2007717897 cites W2410588174 @default.
- W2007717897 doi "https://doi.org/10.1016/j.matlet.2011.01.024" @default.
- W2007717897 hasPublicationYear "2011" @default.
- W2007717897 type Work @default.
- W2007717897 sameAs 2007717897 @default.
- W2007717897 citedByCount "10" @default.
- W2007717897 countsByYear W20077178972012 @default.
- W2007717897 countsByYear W20077178972013 @default.
- W2007717897 countsByYear W20077178972015 @default.
- W2007717897 countsByYear W20077178972016 @default.
- W2007717897 countsByYear W20077178972021 @default.
- W2007717897 crossrefType "journal-article" @default.
- W2007717897 hasAuthorship W2007717897A5009390740 @default.
- W2007717897 hasAuthorship W2007717897A5034558455 @default.
- W2007717897 hasAuthorship W2007717897A5047435768 @default.
- W2007717897 hasAuthorship W2007717897A5060842906 @default.
- W2007717897 hasAuthorship W2007717897A5073299519 @default.
- W2007717897 hasConcept C107365816 @default.
- W2007717897 hasConcept C127413603 @default.
- W2007717897 hasConcept C159096172 @default.
- W2007717897 hasConcept C159985019 @default.
- W2007717897 hasConcept C171250308 @default.
- W2007717897 hasConcept C178790620 @default.
- W2007717897 hasConcept C185592680 @default.
- W2007717897 hasConcept C192562407 @default.
- W2007717897 hasConcept C2777889555 @default.
- W2007717897 hasConcept C2779227376 @default.
- W2007717897 hasConcept C2781448156 @default.
- W2007717897 hasConcept C38398224 @default.
- W2007717897 hasConcept C42360764 @default.
- W2007717897 hasConcept C44280652 @default.
- W2007717897 hasConcept C6556556 @default.
- W2007717897 hasConcept C68928338 @default.
- W2007717897 hasConcept C71039073 @default.
- W2007717897 hasConceptScore W2007717897C107365816 @default.
- W2007717897 hasConceptScore W2007717897C127413603 @default.
- W2007717897 hasConceptScore W2007717897C159096172 @default.
- W2007717897 hasConceptScore W2007717897C159985019 @default.
- W2007717897 hasConceptScore W2007717897C171250308 @default.
- W2007717897 hasConceptScore W2007717897C178790620 @default.
- W2007717897 hasConceptScore W2007717897C185592680 @default.
- W2007717897 hasConceptScore W2007717897C192562407 @default.
- W2007717897 hasConceptScore W2007717897C2777889555 @default.
- W2007717897 hasConceptScore W2007717897C2779227376 @default.
- W2007717897 hasConceptScore W2007717897C2781448156 @default.
- W2007717897 hasConceptScore W2007717897C38398224 @default.
- W2007717897 hasConceptScore W2007717897C42360764 @default.
- W2007717897 hasConceptScore W2007717897C44280652 @default.
- W2007717897 hasConceptScore W2007717897C6556556 @default.
- W2007717897 hasConceptScore W2007717897C68928338 @default.
- W2007717897 hasConceptScore W2007717897C71039073 @default.
- W2007717897 hasIssue "7" @default.
- W2007717897 hasLocation W20077178971 @default.
- W2007717897 hasOpenAccess W2007717897 @default.
- W2007717897 hasPrimaryLocation W20077178971 @default.
- W2007717897 hasRelatedWork W1147912990 @default.
- W2007717897 hasRelatedWork W218405562 @default.
- W2007717897 hasRelatedWork W2336496291 @default.
- W2007717897 hasRelatedWork W2885824456 @default.
- W2007717897 hasRelatedWork W2950426465 @default.
- W2007717897 hasRelatedWork W3094722505 @default.
- W2007717897 hasRelatedWork W3137195979 @default.
- W2007717897 hasRelatedWork W3141449356 @default.
- W2007717897 hasRelatedWork W4210873755 @default.
- W2007717897 hasRelatedWork W2906742674 @default.
- W2007717897 hasVolume "65" @default.
- W2007717897 isParatext "false" @default.
- W2007717897 isRetracted "false" @default.
- W2007717897 magId "2007717897" @default.
- W2007717897 workType "article" @default.