• W2008688729 abstract "The coating process was conducted using an inline-type plasma deposition system. Thin and thick films containing SnO2 were prepared from the starting material sintered ITO pellets (0–15 wt% SnO2). The thin film (<0.6 μm thick) showed an amorphous-like structure. The thick film (>1 μm thick) showed a well-ordered crystalline structure. The crystalline and electrical properties of the films were dependent on the deposition temperature and were closely related to the SnO2 contents. Films deposited on substrates at temperatures of 50–180°C comprised a mixture of amorphous and polycrystalline phases and had a hazy appearance because of light scattering at the rough surface. That appearance was not observed in films with 0 wt% SnO2 content, but it was observed with increasing SnO2 content and substrate temperature. In films with thickness greater than 0.6 μm, the hazy appearance was more pronounced than in films with thickness of less than 0.6 μm. Polycrystalline ITO films with a clean and transparent appearance, as well as minimum resistivity of 1.7×10−4 Ω cm, were obtained on substrates at 180 °C (4 wt%, 7.5 wt% SnO2). Transparent and uniform ITO films with sheet resistance of 1.7 Ω/□ were obtained at 2.1 μm thickness at a high deposition rate (ca. 0.5 μm/min)." @default.
• W2008688729 created "2016-06-24" @default.
• W2008688729 creator A5003540412 @default.
• W2008688729 creator A5029627701 @default.
• W2008688729 creator A5073078170 @default.
• W2008688729 date "2012-01-01" @default.
• W2008688729 modified "2023-10-02" @default.
• W2008688729 title "Effects of Substrate Temperature on Properties of Tin-Doped Indium Oxide Films Deposited by Activated Electron Beam Evaporation" @default.
• W2008688729 cites W1974136026 @default.
• W2008688729 cites W1975953624 @default.
• W2008688729 cites W1995920922 @default.
• W2008688729 cites W2068515175 @default.
• W2008688729 doi "https://doi.org/10.4139/sfj.63.173" @default.
• W2008688729 hasPublicationYear "2012" @default.
• W2008688729 type Work @default.
• W2008688729 sameAs 2008688729 @default.
• W2008688729 citedByCount "0" @default.
• W2008688729 crossrefType "journal-article" @default.
• W2008688729 hasAuthorship W2008688729A5003540412 @default.
• W2008688729 hasAuthorship W2008688729A5029627701 @default.
• W2008688729 hasAuthorship W2008688729A5073078170 @default.
• W2008688729 hasBestOaLocation W20086887291 @default.
• W2008688729 hasConcept C111368507 @default.
• W2008688729 hasConcept C113196181 @default.
• W2008688729 hasConcept C119599485 @default.
• W2008688729 hasConcept C121332964 @default.
• W2008688729 hasConcept C127313418 @default.
• W2008688729 hasConcept C127413603 @default.
• W2008688729 hasConcept C137637335 @default.
• W2008688729 hasConcept C151730666 @default.
• W2008688729 hasConcept C159985019 @default.
• W2008688729 hasConcept C171250308 @default.
• W2008688729 hasConcept C185592680 @default.
• W2008688729 hasConcept C19067145 @default.
• W2008688729 hasConcept C191897082 @default.
• W2008688729 hasConcept C192562407 @default.
• W2008688729 hasConcept C2777289219 @default.
• W2008688729 hasConcept C2779227376 @default.
• W2008688729 hasConcept C2816523 @default.
• W2008688729 hasConcept C32737372 @default.
• W2008688729 hasConcept C43617362 @default.
• W2008688729 hasConcept C49040817 @default.
• W2008688729 hasConcept C56052488 @default.
• W2008688729 hasConcept C57863236 @default.
• W2008688729 hasConcept C61441594 @default.
• W2008688729 hasConcept C64297162 @default.
• W2008688729 hasConcept C66825105 @default.
• W2008688729 hasConcept C69990965 @default.
• W2008688729 hasConcept C7770020 @default.
• W2008688729 hasConcept C8010536 @default.
• W2008688729 hasConcept C86803240 @default.
• W2008688729 hasConcept C97355855 @default.
• W2008688729 hasConceptScore W2008688729C111368507 @default.
• W2008688729 hasConceptScore W2008688729C113196181 @default.
• W2008688729 hasConceptScore W2008688729C119599485 @default.
• W2008688729 hasConceptScore W2008688729C121332964 @default.
• W2008688729 hasConceptScore W2008688729C127313418 @default.
• W2008688729 hasConceptScore W2008688729C127413603 @default.
• W2008688729 hasConceptScore W2008688729C137637335 @default.
• W2008688729 hasConceptScore W2008688729C151730666 @default.
• W2008688729 hasConceptScore W2008688729C159985019 @default.
• W2008688729 hasConceptScore W2008688729C171250308 @default.
• W2008688729 hasConceptScore W2008688729C185592680 @default.
• W2008688729 hasConceptScore W2008688729C19067145 @default.
• W2008688729 hasConceptScore W2008688729C191897082 @default.
• W2008688729 hasConceptScore W2008688729C192562407 @default.
• W2008688729 hasConceptScore W2008688729C2777289219 @default.
• W2008688729 hasConceptScore W2008688729C2779227376 @default.
• W2008688729 hasConceptScore W2008688729C2816523 @default.
• W2008688729 hasConceptScore W2008688729C32737372 @default.
• W2008688729 hasConceptScore W2008688729C43617362 @default.
• W2008688729 hasConceptScore W2008688729C49040817 @default.
• W2008688729 hasConceptScore W2008688729C56052488 @default.
• W2008688729 hasConceptScore W2008688729C57863236 @default.
• W2008688729 hasConceptScore W2008688729C61441594 @default.
• W2008688729 hasConceptScore W2008688729C64297162 @default.
• W2008688729 hasConceptScore W2008688729C66825105 @default.
• W2008688729 hasConceptScore W2008688729C69990965 @default.
• W2008688729 hasConceptScore W2008688729C7770020 @default.
• W2008688729 hasConceptScore W2008688729C8010536 @default.
• W2008688729 hasConceptScore W2008688729C86803240 @default.
• W2008688729 hasConceptScore W2008688729C97355855 @default.
• W2008688729 hasIssue "3" @default.
• W2008688729 hasLocation W20086887291 @default.
• W2008688729 hasOpenAccess W2008688729 @default.
• W2008688729 hasPrimaryLocation W20086887291 @default.
• W2008688729 hasRelatedWork W1537274052 @default.
• W2008688729 hasRelatedWork W2006431990 @default.
• W2008688729 hasRelatedWork W2011054106 @default.
• W2008688729 hasRelatedWork W2018480532 @default.
• W2008688729 hasRelatedWork W2150713802 @default.
• W2008688729 hasRelatedWork W2359832175 @default.
• W2008688729 hasRelatedWork W2386027266 @default.
• W2008688729 hasRelatedWork W2323920813 @default.
• W2008688729 hasRelatedWork W2475196915 @default.
• W2008688729 hasRelatedWork W2608951479 @default.
• W2008688729 hasVolume "63" @default.
• W2008688729 isParatext "false" @default.

• next