• W2009777728 abstract "Different crystallization process concerning N doping was shown in this study. In the crystalline phase of Sb-rich, Te-free GeSb alloy, only Sb crystalline phase was observed as hexagonal phase and Ge crystalline phase was not shown yet in our annealing condition which is 400 °C for 20 min with a ramp rate of 10 K/min. Moreover, as increasing the N doping contents, overall crystallinity was suppressed and the lattice parameters were increased slightly from 4.274 Å to 4.285 Å for ‘a’ parameter and from 11.360 Å to 11.496 Å for ‘c’ parameter. It needs 50 nano-seconds and 15 mW minimum to crystallize GeSb alloy via laser irradiation. The Avrami coefficients were 0.76635 for an un-doped GeSb alloy and 0.37607 in average for N doped GeSb alloys. These Avrami coefficients mean that the crystallization process is growth dominant for un-doped GeSb alloy and nucleation dominant for N doped GeSb alloy. However, our Avrami coefficient values are different to typical values as from ∼1 to 4 because of our experimental condition that is not conducted throughout an isothermal condition. Sheet resistivity difference between amorphous and crystalline phase was more than three orders and the final sheet resistivity of crystalline phase was increased with increasing N doping contents. The phase transition temperatures defined via differentiating the sheet resistivity curve using spline fuction was 315 °C for un-doped GeSb alloy and increased to 350 °C for N-doped GeSb alloy." @default.
• W2009777728 created "2016-06-24" @default.
• W2009777728 creator A5013694438 @default.
• W2009777728 creator A5028589992 @default.
• W2009777728 creator A5067660680 @default.
• W2009777728 creator A5070512930 @default.
• W2009777728 date "2011-05-01" @default.
• W2009777728 modified "2023-10-05" @default.
• W2009777728 title "Considerable changes in crystallization process delivered by N doping in Te-free, Sb-rich GeSb binary alloy" @default.
• W2009777728 cites W150281289 @default.
• W2009777728 cites W1532321282 @default.
• W2009777728 cites W1679750219 @default.
• W2009777728 cites W1983433508 @default.
• W2009777728 cites W1985602161 @default.
• W2009777728 cites W1986706057 @default.
• W2009777728 cites W1996796719 @default.
• W2009777728 cites W2018514694 @default.
• W2009777728 cites W2051220390 @default.
• W2009777728 cites W2055878952 @default.
• W2009777728 cites W2212619124 @default.
• W2009777728 cites W284135608 @default.
• W2009777728 doi "https://doi.org/10.1016/j.cap.2011.03.047" @default.
• W2009777728 hasPublicationYear "2011" @default.
• W2009777728 type Work @default.
• W2009777728 sameAs 2009777728 @default.
• W2009777728 citedByCount "8" @default.
• W2009777728 countsByYear W20097777282012 @default.
• W2009777728 countsByYear W20097777282015 @default.
• W2009777728 countsByYear W20097777282016 @default.
• W2009777728 countsByYear W20097777282017 @default.
• W2009777728 countsByYear W20097777282019 @default.
• W2009777728 countsByYear W20097777282020 @default.
• W2009777728 crossrefType "journal-article" @default.
• W2009777728 hasAuthorship W2009777728A5013694438 @default.
• W2009777728 hasAuthorship W2009777728A5028589992 @default.
• W2009777728 hasAuthorship W2009777728A5067660680 @default.
• W2009777728 hasAuthorship W2009777728A5070512930 @default.
• W2009777728 hasConcept C113196181 @default.
• W2009777728 hasConcept C119599485 @default.
• W2009777728 hasConcept C121332964 @default.
• W2009777728 hasConcept C127413603 @default.
• W2009777728 hasConcept C159985019 @default.
• W2009777728 hasConcept C178790620 @default.
• W2009777728 hasConcept C185592680 @default.
• W2009777728 hasConcept C191897082 @default.
• W2009777728 hasConcept C192562407 @default.
• W2009777728 hasConcept C203036418 @default.
• W2009777728 hasConcept C2777855556 @default.
• W2009777728 hasConcept C2780026712 @default.
• W2009777728 hasConcept C43617362 @default.
• W2009777728 hasConcept C44280652 @default.
• W2009777728 hasConcept C46275449 @default.
• W2009777728 hasConcept C49040817 @default.
• W2009777728 hasConcept C56052488 @default.
• W2009777728 hasConcept C57863236 @default.
• W2009777728 hasConcept C61048295 @default.
• W2009777728 hasConcept C69990965 @default.
• W2009777728 hasConcept C8010536 @default.
• W2009777728 hasConcept C97355855 @default.
• W2009777728 hasConceptScore W2009777728C113196181 @default.
• W2009777728 hasConceptScore W2009777728C119599485 @default.
• W2009777728 hasConceptScore W2009777728C121332964 @default.
• W2009777728 hasConceptScore W2009777728C127413603 @default.
• W2009777728 hasConceptScore W2009777728C159985019 @default.
• W2009777728 hasConceptScore W2009777728C178790620 @default.
• W2009777728 hasConceptScore W2009777728C185592680 @default.
• W2009777728 hasConceptScore W2009777728C191897082 @default.
• W2009777728 hasConceptScore W2009777728C192562407 @default.
• W2009777728 hasConceptScore W2009777728C203036418 @default.
• W2009777728 hasConceptScore W2009777728C2777855556 @default.
• W2009777728 hasConceptScore W2009777728C2780026712 @default.
• W2009777728 hasConceptScore W2009777728C43617362 @default.
• W2009777728 hasConceptScore W2009777728C44280652 @default.
• W2009777728 hasConceptScore W2009777728C46275449 @default.
• W2009777728 hasConceptScore W2009777728C49040817 @default.
• W2009777728 hasConceptScore W2009777728C56052488 @default.
• W2009777728 hasConceptScore W2009777728C57863236 @default.
• W2009777728 hasConceptScore W2009777728C61048295 @default.
• W2009777728 hasConceptScore W2009777728C69990965 @default.
• W2009777728 hasConceptScore W2009777728C8010536 @default.
• W2009777728 hasConceptScore W2009777728C97355855 @default.
• W2009777728 hasIssue "3" @default.
• W2009777728 hasLocation W20097777281 @default.
• W2009777728 hasOpenAccess W2009777728 @default.
• W2009777728 hasPrimaryLocation W20097777281 @default.
• W2009777728 hasRelatedWork W1479734495 @default.
• W2009777728 hasRelatedWork W1982532620 @default.
• W2009777728 hasRelatedWork W1985270458 @default.
• W2009777728 hasRelatedWork W2022161832 @default.
• W2009777728 hasRelatedWork W2026326345 @default.
• W2009777728 hasRelatedWork W2029389590 @default.
• W2009777728 hasRelatedWork W2058619810 @default.
• W2009777728 hasRelatedWork W2152820317 @default.
• W2009777728 hasRelatedWork W2153672889 @default.
• W2009777728 hasRelatedWork W2359891209 @default.
• W2009777728 hasVolume "11" @default.
• W2009777728 isParatext "false" @default.
• W2009777728 isRetracted "false" @default.

• next