- W2009884182 abstract "A series of CrSiCN coatings with various Si concentrations were deposited on Si(100) wafers, and the influence of Si content on the microstructure, mechanical property and crack resistance of the coatings was investigated by XRD, Raman spectroscopy and nanoindentation. After introducing (CH3)3SiH into precursor from 5 sccm to 30 sccm, the Si concentration increased from 0.97 at.% to 7.00 at.% with gradually increasing formation of amorphous SiCx and SiNx. Under low Si concentration (0.97–3.40 at.%) condition, solid solution effect and formation of nc-Cr(C,N)/a-SiNx(a-SiCx) architecture caused an increase in hardness from 18.1 GPa to 21.3 GPa. In contrast, at high Si concentration (5.35–7.00 at.%), larger grain separation, which resulted from the increase of a-SiNx(a-SiCx), led to a drop of hardness to a low range of 13.0–13.6 GPa and a decrease in compressive stress from 4.74 GPa to 2.78 GPa. As a result, superior elasticity and high compressive stress prevented the CrSiCN (Si < 3.40 at.%) coatings from radial crack, whereas the CrSiCN (Si ≥ 3.40 at.%) coatings confronted. However, after unloading, unbalance of high compressive stress (4.74 and 4.83 GPa) in CrCN and CrSiCN (0.97 at.%) coatings initiated cracks parallel to the indenter edge. On account of favorable H/E, H3/E2 and compressive stress, the CrSiCN coating with 2.05 at.% Si presented the best mechanical property and crack resistance." @default.
- W2009884182 created "2016-06-24" @default.
- W2009884182 creator A5025212044 @default.
- W2009884182 creator A5031356139 @default.
- W2009884182 creator A5042061954 @default.
- W2009884182 creator A5065673386 @default.
- W2009884182 creator A5076585197 @default.
- W2009884182 creator A5079556570 @default.
- W2009884182 date "2015-06-01" @default.
- W2009884182 modified "2023-09-27" @default.
- W2009884182 title "Evaluation of crack resistance of CrSiCN coatings as a function of Si concentration via nanoindentation" @default.
- W2009884182 cites W1963669399 @default.
- W2009884182 cites W1963850614 @default.
- W2009884182 cites W1966725671 @default.
- W2009884182 cites W1967073636 @default.
- W2009884182 cites W1971111028 @default.
- W2009884182 cites W1972035635 @default.
- W2009884182 cites W1972895988 @default.
- W2009884182 cites W1974845795 @default.
- W2009884182 cites W1978696931 @default.
- W2009884182 cites W1980138575 @default.
- W2009884182 cites W1984858971 @default.
- W2009884182 cites W1991354304 @default.
- W2009884182 cites W1991897258 @default.
- W2009884182 cites W1992237602 @default.
- W2009884182 cites W1996412801 @default.
- W2009884182 cites W1996737647 @default.
- W2009884182 cites W1999666331 @default.
- W2009884182 cites W2006453586 @default.
- W2009884182 cites W2008499869 @default.
- W2009884182 cites W2008856576 @default.
- W2009884182 cites W2012453317 @default.
- W2009884182 cites W2014298271 @default.
- W2009884182 cites W2017904437 @default.
- W2009884182 cites W2020952194 @default.
- W2009884182 cites W2021439688 @default.
- W2009884182 cites W2024894587 @default.
- W2009884182 cites W2027243386 @default.
- W2009884182 cites W2028208869 @default.
- W2009884182 cites W2033549315 @default.
- W2009884182 cites W2034409180 @default.
- W2009884182 cites W2034517149 @default.
- W2009884182 cites W2035174442 @default.
- W2009884182 cites W2039524459 @default.
- W2009884182 cites W2044538258 @default.
- W2009884182 cites W2054275753 @default.
- W2009884182 cites W2058638690 @default.
- W2009884182 cites W2059062190 @default.
- W2009884182 cites W2062241396 @default.
- W2009884182 cites W2065045667 @default.
- W2009884182 cites W2066874036 @default.
- W2009884182 cites W2074270391 @default.
- W2009884182 cites W2074817624 @default.
- W2009884182 cites W2075499302 @default.
- W2009884182 cites W2079506543 @default.
- W2009884182 cites W2081096636 @default.
- W2009884182 cites W2082795760 @default.
- W2009884182 cites W2083074590 @default.
- W2009884182 cites W2088820124 @default.
- W2009884182 cites W2090345656 @default.
- W2009884182 cites W2092899756 @default.
- W2009884182 cites W2107898214 @default.
- W2009884182 cites W38289613 @default.
- W2009884182 doi "https://doi.org/10.1016/j.surfcoat.2015.04.001" @default.
- W2009884182 hasPublicationYear "2015" @default.
- W2009884182 type Work @default.
- W2009884182 sameAs 2009884182 @default.
- W2009884182 citedByCount "24" @default.
- W2009884182 countsByYear W20098841822015 @default.
- W2009884182 countsByYear W20098841822016 @default.
- W2009884182 countsByYear W20098841822017 @default.
- W2009884182 countsByYear W20098841822018 @default.
- W2009884182 countsByYear W20098841822019 @default.
- W2009884182 countsByYear W20098841822020 @default.
- W2009884182 countsByYear W20098841822021 @default.
- W2009884182 countsByYear W20098841822022 @default.
- W2009884182 countsByYear W20098841822023 @default.
- W2009884182 crossrefType "journal-article" @default.
- W2009884182 hasAuthorship W2009884182A5025212044 @default.
- W2009884182 hasAuthorship W2009884182A5031356139 @default.
- W2009884182 hasAuthorship W2009884182A5042061954 @default.
- W2009884182 hasAuthorship W2009884182A5065673386 @default.
- W2009884182 hasAuthorship W2009884182A5076585197 @default.
- W2009884182 hasAuthorship W2009884182A5079556570 @default.
- W2009884182 hasConcept C120665830 @default.
- W2009884182 hasConcept C121332964 @default.
- W2009884182 hasConcept C159985019 @default.
- W2009884182 hasConcept C160671074 @default.
- W2009884182 hasConcept C171250308 @default.
- W2009884182 hasConcept C185592680 @default.
- W2009884182 hasConcept C192562407 @default.
- W2009884182 hasConcept C2781448156 @default.
- W2009884182 hasConcept C30407753 @default.
- W2009884182 hasConcept C40003534 @default.
- W2009884182 hasConcept C49326732 @default.
- W2009884182 hasConcept C56052488 @default.
- W2009884182 hasConcept C8010536 @default.
- W2009884182 hasConcept C87976508 @default.