- W2010296974 abstract "The objective of this work is to investigate the tribological behavior between WC-Co cemented carbide and austenitic stainless steel under repeated rotation sliding. Influences of cobalt content of commercial grade cemented tungsten carbide on friction coefficient and material transfer phenomena have been explored. Three grades of commercial WC-Co cemented carbide with similar medium WC grain size were employed; WC-12Co, WC-14Co and WC-19Co. The average grain size were ranges between 0.85-1.1 μm and the hardness of about 86-88 HRA have been given by the material maker. The composition analysis and the average grain size of tungsten carbide have been rechecked. Furthermore, the carbide grain size distribution was recorded and the fracture toughness was calculated for each WC-Co grade. The experiments were carried out using ball on disk test. The ball was made from SUS304 grade and the disk was fabricated by 3 grades of WC-Co cemented carbide. The friction coefficient was measured under dry sliding. The characteristics of contact surfaces were explored on the ball as well as on the disk after tests to reveal the presence of a metallic transfer on the WC-Co cemented carbide disk and the wear scar on the ball. The measurement results of wear volume on the stainless steel ball disclosed that maximum wear rate was found from the stainless steel ball rub against WC-19Co tool material." @default.
- W2010296974 created "2016-06-24" @default.
- W2010296974 creator A5001324070 @default.
- W2010296974 creator A5033226584 @default.
- W2010296974 date "2014-06-01" @default.
- W2010296974 modified "2023-10-16" @default.
- W2010296974 title "Influences of Cobalt Content on the Physical and Tribological Properties of Cemented Tungsten Carbide Used in Sheet Metal Forming Application" @default.
- W2010296974 cites W2020107003 @default.
- W2010296974 cites W2023609619 @default.
- W2010296974 cites W2025818078 @default.
- W2010296974 cites W2036760211 @default.
- W2010296974 cites W2043897804 @default.
- W2010296974 cites W2070406914 @default.
- W2010296974 cites W2070449025 @default.
- W2010296974 cites W2085290768 @default.
- W2010296974 cites W2155250935 @default.
- W2010296974 cites W2162730831 @default.
- W2010296974 cites W4240409138 @default.
- W2010296974 doi "https://doi.org/10.4028/www.scientific.net/amr.966-967.80" @default.
- W2010296974 hasPublicationYear "2014" @default.
- W2010296974 type Work @default.
- W2010296974 sameAs 2010296974 @default.
- W2010296974 citedByCount "0" @default.
- W2010296974 crossrefType "journal-article" @default.
- W2010296974 hasAuthorship W2010296974A5001324070 @default.
- W2010296974 hasAuthorship W2010296974A5033226584 @default.
- W2010296974 hasConcept C122041747 @default.
- W2010296974 hasConcept C134306372 @default.
- W2010296974 hasConcept C159985019 @default.
- W2010296974 hasConcept C167310744 @default.
- W2010296974 hasConcept C191897082 @default.
- W2010296974 hasConcept C192191005 @default.
- W2010296974 hasConcept C192562407 @default.
- W2010296974 hasConcept C2779715934 @default.
- W2010296974 hasConcept C2781422231 @default.
- W2010296974 hasConcept C2987692278 @default.
- W2010296974 hasConcept C3017962496 @default.
- W2010296974 hasConcept C33923547 @default.
- W2010296974 hasConcept C5335593 @default.
- W2010296974 hasConceptScore W2010296974C122041747 @default.
- W2010296974 hasConceptScore W2010296974C134306372 @default.
- W2010296974 hasConceptScore W2010296974C159985019 @default.
- W2010296974 hasConceptScore W2010296974C167310744 @default.
- W2010296974 hasConceptScore W2010296974C191897082 @default.
- W2010296974 hasConceptScore W2010296974C192191005 @default.
- W2010296974 hasConceptScore W2010296974C192562407 @default.
- W2010296974 hasConceptScore W2010296974C2779715934 @default.
- W2010296974 hasConceptScore W2010296974C2781422231 @default.
- W2010296974 hasConceptScore W2010296974C2987692278 @default.
- W2010296974 hasConceptScore W2010296974C3017962496 @default.
- W2010296974 hasConceptScore W2010296974C33923547 @default.
- W2010296974 hasConceptScore W2010296974C5335593 @default.
- W2010296974 hasLocation W20102969741 @default.
- W2010296974 hasOpenAccess W2010296974 @default.
- W2010296974 hasPrimaryLocation W20102969741 @default.
- W2010296974 hasRelatedWork W1974711915 @default.
- W2010296974 hasRelatedWork W1978918981 @default.
- W2010296974 hasRelatedWork W2010296974 @default.
- W2010296974 hasRelatedWork W2069738921 @default.
- W2010296974 hasRelatedWork W2074243585 @default.
- W2010296974 hasRelatedWork W2083747326 @default.
- W2010296974 hasRelatedWork W2349525105 @default.
- W2010296974 hasRelatedWork W2379875209 @default.
- W2010296974 hasRelatedWork W2756478405 @default.
- W2010296974 hasRelatedWork W2963302329 @default.
- W2010296974 hasVolume "966-967" @default.
- W2010296974 isParatext "false" @default.
- W2010296974 isRetracted "false" @default.
- W2010296974 magId "2010296974" @default.
- W2010296974 workType "article" @default.