- W2010594865 abstract "The adhesive strength and fractured microstructure of aluminum nitride (AlN) substrate metallized with resistor thick-films followed by firing at 850 oC have been investigated via a pull-out rupture test loaded in tension. The AlN substrate used includes the as-received form and an oxidized form that was thermally treated at 1450 oC prior to the metallization. The thick-film paste includes both the as-received form (which is an RuO2-based resistor) and a mixture of the paste with varying fractions of submicrometer alumina powder (5–20 wt.%) for comparison purposes. When the as-received AlN is used as the substrate, rupture strength decreases monotonically from 1.2 to ∼0.1 MPa as the alumina loading (in the film) increased from 0 to 20 wt.%. The strength, however, remains relatively constant (∼0.5 MPa) for the pre-oxidized AlN case, i.e. the adhesion is found insensitive to the change of alumina loading. This strength dependency has been compared with their fractured microstructure and the possible fracture mechanism that caused the failure is discussed." @default.
- W2010594865 created "2016-06-24" @default.
- W2010594865 creator A5043937943 @default.
- W2010594865 creator A5057441996 @default.
- W2010594865 creator A5076640209 @default.
- W2010594865 date "2002-01-01" @default.
- W2010594865 modified "2023-10-17" @default.
- W2010594865 title "Interfacial adhesion and microstructure of thick film metallized aluminum nitride substrates" @default.
- W2010594865 cites W165393292 @default.
- W2010594865 cites W1819828827 @default.
- W2010594865 cites W1988065036 @default.
- W2010594865 cites W2000552828 @default.
- W2010594865 cites W2037026046 @default.
- W2010594865 cites W2040380198 @default.
- W2010594865 cites W2056577111 @default.
- W2010594865 cites W2067680055 @default.
- W2010594865 cites W2068689387 @default.
- W2010594865 cites W2086811096 @default.
- W2010594865 cites W2134741400 @default.
- W2010594865 cites W2170301593 @default.
- W2010594865 cites W2179965569 @default.
- W2010594865 cites W325138863 @default.
- W2010594865 cites W190306484 @default.
- W2010594865 doi "https://doi.org/10.1016/s0272-8842(01)00053-0" @default.
- W2010594865 hasPublicationYear "2002" @default.
- W2010594865 type Work @default.
- W2010594865 sameAs 2010594865 @default.
- W2010594865 citedByCount "8" @default.
- W2010594865 countsByYear W20105948652015 @default.
- W2010594865 countsByYear W20105948652016 @default.
- W2010594865 countsByYear W20105948652020 @default.
- W2010594865 countsByYear W20105948652021 @default.
- W2010594865 crossrefType "journal-article" @default.
- W2010594865 hasAuthorship W2010594865A5043937943 @default.
- W2010594865 hasAuthorship W2010594865A5057441996 @default.
- W2010594865 hasAuthorship W2010594865A5076640209 @default.
- W2010594865 hasConcept C111368507 @default.
- W2010594865 hasConcept C127313418 @default.
- W2010594865 hasConcept C159985019 @default.
- W2010594865 hasConcept C192562407 @default.
- W2010594865 hasConcept C194760766 @default.
- W2010594865 hasConcept C2777289219 @default.
- W2010594865 hasConcept C2779227376 @default.
- W2010594865 hasConcept C2780162792 @default.
- W2010594865 hasConcept C513153333 @default.
- W2010594865 hasConcept C68928338 @default.
- W2010594865 hasConcept C84416704 @default.
- W2010594865 hasConcept C87976508 @default.
- W2010594865 hasConceptScore W2010594865C111368507 @default.
- W2010594865 hasConceptScore W2010594865C127313418 @default.
- W2010594865 hasConceptScore W2010594865C159985019 @default.
- W2010594865 hasConceptScore W2010594865C192562407 @default.
- W2010594865 hasConceptScore W2010594865C194760766 @default.
- W2010594865 hasConceptScore W2010594865C2777289219 @default.
- W2010594865 hasConceptScore W2010594865C2779227376 @default.
- W2010594865 hasConceptScore W2010594865C2780162792 @default.
- W2010594865 hasConceptScore W2010594865C513153333 @default.
- W2010594865 hasConceptScore W2010594865C68928338 @default.
- W2010594865 hasConceptScore W2010594865C84416704 @default.
- W2010594865 hasConceptScore W2010594865C87976508 @default.
- W2010594865 hasIssue "1" @default.
- W2010594865 hasLocation W20105948651 @default.
- W2010594865 hasOpenAccess W2010594865 @default.
- W2010594865 hasPrimaryLocation W20105948651 @default.
- W2010594865 hasRelatedWork W2001692255 @default.
- W2010594865 hasRelatedWork W2024908392 @default.
- W2010594865 hasRelatedWork W2049250247 @default.
- W2010594865 hasRelatedWork W2088502706 @default.
- W2010594865 hasRelatedWork W2091129523 @default.
- W2010594865 hasRelatedWork W2138393670 @default.
- W2010594865 hasRelatedWork W2351556892 @default.
- W2010594865 hasRelatedWork W2657397208 @default.
- W2010594865 hasRelatedWork W4298168385 @default.
- W2010594865 hasRelatedWork W883757858 @default.
- W2010594865 hasVolume "28" @default.
- W2010594865 isParatext "false" @default.
- W2010594865 isRetracted "false" @default.
- W2010594865 magId "2010594865" @default.
- W2010594865 workType "article" @default.