- W2012373556 abstract "A commercial 1Cr-1 Mn steel has been investigated in the temper-embrittled condition in relation to sensitivity to hydrogen stress cracking. The work involved delayed brittle failure tests on smooth steel specimens which were stressed in tension under constant load, while being charged with cathodic hydrogen at a constant current density. Both the relative range of stresses for susceptibility to hydrogen stress crack ing and the overall rate of delayed failure were found to be maximal for specimens which had been tempered at 500 - 550 C, i.e. where grain-boundary impurity segregation and temper embrittlement were also at a maximum. While the intergranular weakness induced by impurity segregation appears to be responsible for lowering the time required to propagate a crack to the critical point for delayed failure, some interaction between hydrogen and impurity elements appears to cause the increase in susceptibility to hydrogen stress cracking." @default.
- W2012373556 created "2016-06-24" @default.
- W2012373556 creator A5008701126 @default.
- W2012373556 creator A5015850442 @default.
- W2012373556 creator A5025951796 @default.
- W2012373556 date "1983-01-01" @default.
- W2012373556 modified "2023-09-23" @default.
- W2012373556 title "Susceptibility to hydrogen-induced delayed failure of temperembrittled, low-alloy steel" @default.
- W2012373556 cites W1990874360 @default.
- W2012373556 cites W2030690236 @default.
- W2012373556 cites W2035168697 @default.
- W2012373556 cites W2594309288 @default.
- W2012373556 doi "https://doi.org/10.1179/030716983803291280" @default.
- W2012373556 hasPublicationYear "1983" @default.
- W2012373556 type Work @default.
- W2012373556 sameAs 2012373556 @default.
- W2012373556 citedByCount "3" @default.
- W2012373556 crossrefType "journal-article" @default.
- W2012373556 hasAuthorship W2012373556A5008701126 @default.
- W2012373556 hasAuthorship W2012373556A5015850442 @default.
- W2012373556 hasAuthorship W2012373556A5025951796 @default.
- W2012373556 hasConcept C112950240 @default.
- W2012373556 hasConcept C136478896 @default.
- W2012373556 hasConcept C138885662 @default.
- W2012373556 hasConcept C142282041 @default.
- W2012373556 hasConcept C147789679 @default.
- W2012373556 hasConcept C159985019 @default.
- W2012373556 hasConcept C17525397 @default.
- W2012373556 hasConcept C178790620 @default.
- W2012373556 hasConcept C184102282 @default.
- W2012373556 hasConcept C185592680 @default.
- W2012373556 hasConcept C186068551 @default.
- W2012373556 hasConcept C191897082 @default.
- W2012373556 hasConcept C192562407 @default.
- W2012373556 hasConcept C205871581 @default.
- W2012373556 hasConcept C20625102 @default.
- W2012373556 hasConcept C21036866 @default.
- W2012373556 hasConcept C2780026712 @default.
- W2012373556 hasConcept C41895202 @default.
- W2012373556 hasConcept C47908070 @default.
- W2012373556 hasConcept C512968161 @default.
- W2012373556 hasConcept C58396970 @default.
- W2012373556 hasConcept C71987851 @default.
- W2012373556 hasConcept C87976508 @default.
- W2012373556 hasConcept C89395315 @default.
- W2012373556 hasConcept C92621854 @default.
- W2012373556 hasConceptScore W2012373556C112950240 @default.
- W2012373556 hasConceptScore W2012373556C136478896 @default.
- W2012373556 hasConceptScore W2012373556C138885662 @default.
- W2012373556 hasConceptScore W2012373556C142282041 @default.
- W2012373556 hasConceptScore W2012373556C147789679 @default.
- W2012373556 hasConceptScore W2012373556C159985019 @default.
- W2012373556 hasConceptScore W2012373556C17525397 @default.
- W2012373556 hasConceptScore W2012373556C178790620 @default.
- W2012373556 hasConceptScore W2012373556C184102282 @default.
- W2012373556 hasConceptScore W2012373556C185592680 @default.
- W2012373556 hasConceptScore W2012373556C186068551 @default.
- W2012373556 hasConceptScore W2012373556C191897082 @default.
- W2012373556 hasConceptScore W2012373556C192562407 @default.
- W2012373556 hasConceptScore W2012373556C205871581 @default.
- W2012373556 hasConceptScore W2012373556C20625102 @default.
- W2012373556 hasConceptScore W2012373556C21036866 @default.
- W2012373556 hasConceptScore W2012373556C2780026712 @default.
- W2012373556 hasConceptScore W2012373556C41895202 @default.
- W2012373556 hasConceptScore W2012373556C47908070 @default.
- W2012373556 hasConceptScore W2012373556C512968161 @default.
- W2012373556 hasConceptScore W2012373556C58396970 @default.
- W2012373556 hasConceptScore W2012373556C71987851 @default.
- W2012373556 hasConceptScore W2012373556C87976508 @default.
- W2012373556 hasConceptScore W2012373556C89395315 @default.
- W2012373556 hasConceptScore W2012373556C92621854 @default.
- W2012373556 hasIssue "1" @default.
- W2012373556 hasLocation W20123735561 @default.
- W2012373556 hasOpenAccess W2012373556 @default.
- W2012373556 hasPrimaryLocation W20123735561 @default.
- W2012373556 hasRelatedWork W1519380744 @default.
- W2012373556 hasRelatedWork W1572428338 @default.
- W2012373556 hasRelatedWork W1600978992 @default.
- W2012373556 hasRelatedWork W1917955032 @default.
- W2012373556 hasRelatedWork W2012373556 @default.
- W2012373556 hasRelatedWork W2021048902 @default.
- W2012373556 hasRelatedWork W235730468 @default.
- W2012373556 hasRelatedWork W2374537797 @default.
- W2012373556 hasRelatedWork W2477718279 @default.
- W2012373556 hasRelatedWork W342344241 @default.
- W2012373556 hasVolume "10" @default.
- W2012373556 isParatext "false" @default.
- W2012373556 isRetracted "false" @default.
- W2012373556 magId "2012373556" @default.
- W2012373556 workType "article" @default.