• W2013056335 abstract "The effect of boron segregation on recrystallization was investigated in two Nb and two Nb-free steels. The results indicate that the addition of B to a Nb steel retards the recrystallization of austenite after high temperature deformation to a significant degree. By contrast, the effect of B when added alone is not of commercial importance. At deformation temperatures above 950°C, the influence of boron is mainly due to grain boundary segregation and solute drag; below 900°C, the retardation results from the precipitation of Nb carbonitride. During isothermal holding, there are two types of non-equilibrium segregation on boundaries. Strain-induced segregation occurs on the original boundaries; it increases and attains a maximum rapidly, then decreases and disappears after 60 s of holding at 1000°C. A second type of non-equilibrium segregation occurs on newly formed boundaries during recrystallization. It develops quickly as the new boundaries are formed and begin to move, and can persist until grain impingement occurs and the motion is halted. The enhanced effect of B in the presence of Nb is attributed to the formation of (Nb, B) complexes, which appear to increase the solute drag force and decrease the boundary velocity. On étudie l'effet de la ségrégation du bore sur la recristallisation dans deux aciers au niobium et dans deux aciers sans niobium. Les résultats montrent que l'addition de bore à un acier au niobium retarde d'une manière significative la recristallisation de l'austénite après une déformation à haute température. Par contre, l'effet du bore lorsqu'il est ajouté seul ne présente pas d'importance commerciale. A des températures de déformation supérieures à 950°C, l'influence du bore est principalement due à la ségrégation aux joints de grains et au traînage du soluté; au dessous de 950°C, le retard provient de la précipitation de carbonitrures de niobium. Pendant le maintien isotherme, il y a deux types de ségrégation hors d'équilibre sur les joints. La ségrégation induite par déformation se produit sur les joints originels; elle augmente et atteint un maximum rapidement, puis décroît et disparaît aprés un maintien de 60s à 1000°C. Un second type de ségrégation hors d'équilibre se produit sur les joints nouvellement formés pendant la recristallisation. Il se développe rapidement lorsque les nouveaux joints sont formés et commencement à se déplacer, et il peut persister jusqu'à ce que les grains se rencontrent et que le mouvement s'arrête. Le renforcement de l'effet du bore en présence de niobium est attribué à la formation de complexes (Nb, B) qui semblent augmenter la force de traînage du soluté et diminuer la vitesse de migration des joints. Der Einfluβ der Borsegregation auf die Rekristallisation wird an zwei Stahlsorten, mit und ohne Nb-Gehalt, untersucht. Die Ergebnisse zeigen, daβ die Zugabe von Bor zu einem Nb-haltigen Stahl die Rekristallisation des Austenits nach einer Hochtemperaturverformung beträchtlich verzögert. Dagegen ist die Zugabe von Bor ohne Nb ohne kommerziellen Vorteil. Bei Verformungstemperaturen oberhalb von 950°C beruht der Einfluβ des Bors überwiegend auf der Segregation an Korngrenzen und einer entsprechenden Reibung; unterhalb von 900°C rührt die Verzögerung von der Ausscheidung von Nb-Karbonitrid her. Während der isothermen Lagerung treten zwei Arten von Nichtgleichgewichtssegregation an Korngrenzen auf. Spannungsinduzierte Segregation findet an ursprünglichen Korngrenzen statt; sie nimmt zu und erreicht rasch ein Maximum, nimmt dann ab und verschwindet nach 60 s bei 1000°C. Die zweite art findet an neu während der Rekristallisation gebildeten Korngrenzen statt. Diese Segregation entwickelt sich rasch, wenn sich die neuen Korngrenzen formen und zu bewegen beginnen, und kann dauren, bis Korngrenzen aufeinandertreffen und stoppen. Der verstärkte Effekt im Beisein von Nb wird der Bildung von (Nb, B)-Komplexen zugeschrieben, welche die Reibungsspannung zu vergröβern und damit die Korngrenzgeschwindigkeit zu verringern scheinen." @default.
• W2013056335 created "2016-06-24" @default.
• W2013056335 creator A5024902299 @default.
• W2013056335 creator A5058841196 @default.
• W2013056335 creator A5063976933 @default.
• W2013056335 creator A5084875553 @default.
• W2013056335 date "1991-10-01" @default.
• W2013056335 modified "2023-10-14" @default.
• W2013056335 title "The non-equilibrium segregation of boron during the recrystalization of Nb-treated HSLA steels" @default.
• W2013056335 cites W1966514997 @default.
• W2013056335 cites W1967899194 @default.
• W2013056335 cites W1971868225 @default.
• W2013056335 cites W1982638814 @default.
• W2013056335 cites W1985129490 @default.
• W2013056335 cites W1987732601 @default.
• W2013056335 cites W1989520734 @default.
• W2013056335 cites W1994314167 @default.
• W2013056335 cites W1995982133 @default.
• W2013056335 cites W2008419076 @default.
• W2013056335 cites W2009925593 @default.
• W2013056335 cites W2011206512 @default.
• W2013056335 cites W2016924980 @default.
• W2013056335 cites W2021443456 @default.
• W2013056335 cites W2022194226 @default.
• W2013056335 cites W2047883767 @default.
• W2013056335 cites W2057619734 @default.
• W2013056335 cites W2075301115 @default.
• W2013056335 cites W2082353512 @default.
• W2013056335 cites W2082566478 @default.
• W2013056335 cites W2083674334 @default.
• W2013056335 cites W2551720166 @default.
• W2013056335 cites W4237262305 @default.
• W2013056335 cites W4253691359 @default.
• W2013056335 doi "https://doi.org/10.1016/0956-7151(91)90012-p" @default.
• W2013056335 hasPublicationYear "1991" @default.
• W2013056335 type Work @default.
• W2013056335 sameAs 2013056335 @default.
• W2013056335 citedByCount "68" @default.
• W2013056335 countsByYear W20130563352012 @default.
• W2013056335 countsByYear W20130563352013 @default.
• W2013056335 countsByYear W20130563352015 @default.
• W2013056335 countsByYear W20130563352016 @default.
• W2013056335 countsByYear W20130563352017 @default.
• W2013056335 countsByYear W20130563352018 @default.
• W2013056335 countsByYear W20130563352019 @default.
• W2013056335 countsByYear W20130563352020 @default.
• W2013056335 countsByYear W20130563352021 @default.
• W2013056335 countsByYear W20130563352022 @default.
• W2013056335 countsByYear W20130563352023 @default.
• W2013056335 crossrefType "journal-article" @default.
• W2013056335 hasAuthorship W2013056335A5024902299 @default.
• W2013056335 hasAuthorship W2013056335A5058841196 @default.
• W2013056335 hasAuthorship W2013056335A5063976933 @default.
• W2013056335 hasAuthorship W2013056335A5084875553 @default.
• W2013056335 hasConcept C121332964 @default.
• W2013056335 hasConcept C12487841 @default.
• W2013056335 hasConcept C133347239 @default.
• W2013056335 hasConcept C151730666 @default.
• W2013056335 hasConcept C178790620 @default.
• W2013056335 hasConcept C185592680 @default.
• W2013056335 hasConcept C191897082 @default.
• W2013056335 hasConcept C192562407 @default.
• W2013056335 hasConcept C195702682 @default.
• W2013056335 hasConcept C47908070 @default.
• W2013056335 hasConcept C501308230 @default.
• W2013056335 hasConcept C507968137 @default.
• W2013056335 hasConcept C61048295 @default.
• W2013056335 hasConcept C8010536 @default.
• W2013056335 hasConcept C86803240 @default.
• W2013056335 hasConcept C87976508 @default.
• W2013056335 hasConcept C96288455 @default.
• W2013056335 hasConcept C97355855 @default.
• W2013056335 hasConceptScore W2013056335C121332964 @default.
• W2013056335 hasConceptScore W2013056335C12487841 @default.
• W2013056335 hasConceptScore W2013056335C133347239 @default.
• W2013056335 hasConceptScore W2013056335C151730666 @default.
• W2013056335 hasConceptScore W2013056335C178790620 @default.
• W2013056335 hasConceptScore W2013056335C185592680 @default.
• W2013056335 hasConceptScore W2013056335C191897082 @default.
• W2013056335 hasConceptScore W2013056335C192562407 @default.
• W2013056335 hasConceptScore W2013056335C195702682 @default.
• W2013056335 hasConceptScore W2013056335C47908070 @default.
• W2013056335 hasConceptScore W2013056335C501308230 @default.
• W2013056335 hasConceptScore W2013056335C507968137 @default.
• W2013056335 hasConceptScore W2013056335C61048295 @default.
• W2013056335 hasConceptScore W2013056335C8010536 @default.
• W2013056335 hasConceptScore W2013056335C86803240 @default.
• W2013056335 hasConceptScore W2013056335C87976508 @default.
• W2013056335 hasConceptScore W2013056335C96288455 @default.
• W2013056335 hasConceptScore W2013056335C97355855 @default.
• W2013056335 hasIssue "10" @default.
• W2013056335 hasLocation W20130563351 @default.
• W2013056335 hasOpenAccess W2013056335 @default.
• W2013056335 hasPrimaryLocation W20130563351 @default.
• W2013056335 hasRelatedWork W1569065267 @default.
• W2013056335 hasRelatedWork W2007495929 @default.
• W2013056335 hasRelatedWork W2071816729 @default.
• W2013056335 hasRelatedWork W2100353769 @default.

• next