- W2013541590 abstract "To make use of metals with improved conductivity like Ag, AgPd, Au or Cu for metallization pastes in ceramic multilayer technology, Low-Temperature Co-fired Ceramics (LTCC) are densified at temperatures below 900°C. The densification mechanism can be attributed to viscous sintering in combination with the crystallization of the glass matrix. Lifetime prediction and extension of the application range to elevated temperatures strongly depend on the transition range of the remaining amorphous phase as well as on the final crystallization products. Due to the fact that multilayer ceramics based on LTCCs are gaining increasing interest in the manufacturing of highly integrated devices for microelectronic and sensor applications, there is the need to establish a better understanding of their mechanical and electrical behaviour in the elevated temperature regime. In this study, four commercial LTCC substrate materials in addition to a test product in the sintered state, namely DP 951, DP 943, both from DuPont, CT 800 and AHT-01, both from Heraeus, and GC from CeramTec were investigated in respect to the temperature dependence of their mechanical and electrical properties up to temperatures of 950 °C. Mechanical characterization included three-point bending tests on single layer substrates. Furthermore, the surface resistivity as a function of temperature up to 500°C was determined under vacuum for DP 951. Next, these results were correlated to the composition of the glasses, determined by inductively coupled plasma (ICP) analysis, as well as the crystallization products apparent in the composites, which were determined by XRD of the sintered substrates and in-situ HT-XRD for DP 951. Results gained from these investigations of the commercial LTCC products were compared to measurements carried out on glass-ceramic composites developed in-house exhibiting improved electrical behaviour and good temperature stability." @default.
- W2013541590 created "2016-06-24" @default.
- W2013541590 creator A5004235901 @default.
- W2013541590 creator A5004759165 @default.
- W2013541590 creator A5017133878 @default.
- W2013541590 creator A5056561370 @default.
- W2013541590 creator A5074689407 @default.
- W2013541590 date "2009-05-20" @default.
- W2013541590 modified "2023-09-25" @default.
- W2013541590 title "Electrical and mechanical characterization of low temperature co-fired ceramics for high temperature sensor applications" @default.
- W2013541590 cites W112656829 @default.
- W2013541590 cites W1520982623 @default.
- W2013541590 cites W1530958485 @default.
- W2013541590 cites W1964472476 @default.
- W2013541590 cites W1968942585 @default.
- W2013541590 cites W2030906177 @default.
- W2013541590 cites W2114441747 @default.
- W2013541590 cites W2136586541 @default.
- W2013541590 cites W2144295036 @default.
- W2013541590 cites W2159197093 @default.
- W2013541590 cites W2495725524 @default.
- W2013541590 cites W642411338 @default.
- W2013541590 cites W2479879239 @default.
- W2013541590 doi "https://doi.org/10.1117/12.822665" @default.
- W2013541590 hasPublicationYear "2009" @default.
- W2013541590 type Work @default.
- W2013541590 sameAs 2013541590 @default.
- W2013541590 citedByCount "1" @default.
- W2013541590 countsByYear W20135415902022 @default.
- W2013541590 crossrefType "proceedings-article" @default.
- W2013541590 hasAuthorship W2013541590A5004235901 @default.
- W2013541590 hasAuthorship W2013541590A5004759165 @default.
- W2013541590 hasAuthorship W2013541590A5017133878 @default.
- W2013541590 hasAuthorship W2013541590A5056561370 @default.
- W2013541590 hasAuthorship W2013541590A5074689407 @default.
- W2013541590 hasConcept C121332964 @default.
- W2013541590 hasConcept C134132462 @default.
- W2013541590 hasConcept C159985019 @default.
- W2013541590 hasConcept C171250308 @default.
- W2013541590 hasConcept C192562407 @default.
- W2013541590 hasConcept C2780841128 @default.
- W2013541590 hasConcept C49040817 @default.
- W2013541590 hasConcept C72293138 @default.
- W2013541590 hasConcept C97355855 @default.
- W2013541590 hasConceptScore W2013541590C121332964 @default.
- W2013541590 hasConceptScore W2013541590C134132462 @default.
- W2013541590 hasConceptScore W2013541590C159985019 @default.
- W2013541590 hasConceptScore W2013541590C171250308 @default.
- W2013541590 hasConceptScore W2013541590C192562407 @default.
- W2013541590 hasConceptScore W2013541590C2780841128 @default.
- W2013541590 hasConceptScore W2013541590C49040817 @default.
- W2013541590 hasConceptScore W2013541590C72293138 @default.
- W2013541590 hasConceptScore W2013541590C97355855 @default.
- W2013541590 hasLocation W20135415901 @default.
- W2013541590 hasOpenAccess W2013541590 @default.
- W2013541590 hasPrimaryLocation W20135415901 @default.
- W2013541590 hasRelatedWork W1985469821 @default.
- W2013541590 hasRelatedWork W2062108412 @default.
- W2013541590 hasRelatedWork W2082293200 @default.
- W2013541590 hasRelatedWork W2084463405 @default.
- W2013541590 hasRelatedWork W2281145519 @default.
- W2013541590 hasRelatedWork W2366934632 @default.
- W2013541590 hasRelatedWork W2380293314 @default.
- W2013541590 hasRelatedWork W2943188944 @default.
- W2013541590 hasRelatedWork W4285802202 @default.
- W2013541590 hasRelatedWork W4305082739 @default.
- W2013541590 isParatext "false" @default.
- W2013541590 isRetracted "false" @default.
- W2013541590 magId "2013541590" @default.
- W2013541590 workType "article" @default.