- W2013608618 abstract "Abstract The effects of different substrates (CMSX-4 and IN738LC) on cyclic oxidation behavior of two thermal barrier coatings (TBCs) were investigated in this study. Cyclic oxidation test was conducted at a peak temperature of 1080 °C with 30 min hold time. The TBC systems tested consisted of two nickel-base superalloy substrates (CMSX-4 and IN738LC), a platinum aluminide bond coat and two types of 8YSZ top coat (vertical cracks (VC) and columnar structure). Samples with CMSX-4 substrate showed greater cyclic oxidation lifetimes than that with IN738LC, and VC YSZ on CMSX-4 offered longer cyclic life than those with columnar structure. After the oxidation test, the samples were analyzed using a scanning electron microscope (SEM) and an X-Ray diffractometer. The failure location of all TBC systems examined was found to be in the vicinity of TGO, consistent with past research of similar coating systems. Alumina and spinels (CS) were detected on all spalled surfaces although the amount of each phase differs from sample to sample. Ta-rich oxide was found on spalled coating surfaces with CMSX-4 substrate while islands of YSZ on the exposed TGO surface of samples with IN738LC substrate. It is believed that alloy composition, TGO rumpling and stresses induced by TGO growth and coefficient of thermal expansion (CTE) mismatch between different layers all contributed to the reduced cycles to failure of TBC systems with IN738LC substrate." @default.
- W2013608618 created "2016-06-24" @default.
- W2013608618 creator A5031290487 @default.
- W2013608618 creator A5033263947 @default.
- W2013608618 creator A5058924447 @default.
- W2013608618 creator A5090360201 @default.
- W2013608618 date "2014-11-01" @default.
- W2013608618 modified "2023-09-26" @default.
- W2013608618 title "Effects of substrate material and TBC structure on the cyclic oxidation resistance of TBC systems" @default.
- W2013608618 cites W186390596 @default.
- W2013608618 cites W1964458642 @default.
- W2013608618 cites W1980754319 @default.
- W2013608618 cites W1987601245 @default.
- W2013608618 cites W1988455667 @default.
- W2013608618 cites W1993609138 @default.
- W2013608618 cites W2000991874 @default.
- W2013608618 cites W2001231786 @default.
- W2013608618 cites W2006744700 @default.
- W2013608618 cites W2011079205 @default.
- W2013608618 cites W2013380859 @default.
- W2013608618 cites W2016578413 @default.
- W2013608618 cites W2017456319 @default.
- W2013608618 cites W2020319174 @default.
- W2013608618 cites W2038270033 @default.
- W2013608618 cites W2039927208 @default.
- W2013608618 cites W2045323460 @default.
- W2013608618 cites W2049160016 @default.
- W2013608618 cites W2050515541 @default.
- W2013608618 cites W2050896265 @default.
- W2013608618 cites W2052194193 @default.
- W2013608618 cites W2052616915 @default.
- W2013608618 cites W2056480551 @default.
- W2013608618 cites W2061296290 @default.
- W2013608618 cites W2064458873 @default.
- W2013608618 cites W2074627324 @default.
- W2013608618 cites W2074941664 @default.
- W2013608618 cites W2075777359 @default.
- W2013608618 cites W2077315870 @default.
- W2013608618 cites W2079936618 @default.
- W2013608618 cites W2084867605 @default.
- W2013608618 cites W2093594019 @default.
- W2013608618 cites W2141134472 @default.
- W2013608618 cites W2149974092 @default.
- W2013608618 cites W2152236287 @default.
- W2013608618 cites W2160677850 @default.
- W2013608618 cites W2165522162 @default.
- W2013608618 doi "https://doi.org/10.1016/j.surfcoat.2014.10.004" @default.
- W2013608618 hasPublicationYear "2014" @default.
- W2013608618 type Work @default.
- W2013608618 sameAs 2013608618 @default.
- W2013608618 citedByCount "10" @default.
- W2013608618 countsByYear W20136086182018 @default.
- W2013608618 countsByYear W20136086182019 @default.
- W2013608618 countsByYear W20136086182020 @default.
- W2013608618 countsByYear W20136086182021 @default.
- W2013608618 countsByYear W20136086182023 @default.
- W2013608618 crossrefType "journal-article" @default.
- W2013608618 hasAuthorship W2013608618A5031290487 @default.
- W2013608618 hasAuthorship W2013608618A5033263947 @default.
- W2013608618 hasAuthorship W2013608618A5058924447 @default.
- W2013608618 hasAuthorship W2013608618A5090360201 @default.
- W2013608618 hasConcept C111368507 @default.
- W2013608618 hasConcept C127313418 @default.
- W2013608618 hasConcept C159985019 @default.
- W2013608618 hasConcept C191897082 @default.
- W2013608618 hasConcept C192562407 @default.
- W2013608618 hasConcept C2777289219 @default.
- W2013608618 hasConceptScore W2013608618C111368507 @default.
- W2013608618 hasConceptScore W2013608618C127313418 @default.
- W2013608618 hasConceptScore W2013608618C159985019 @default.
- W2013608618 hasConceptScore W2013608618C191897082 @default.
- W2013608618 hasConceptScore W2013608618C192562407 @default.
- W2013608618 hasConceptScore W2013608618C2777289219 @default.
- W2013608618 hasFunder F4320334593 @default.
- W2013608618 hasLocation W20136086181 @default.
- W2013608618 hasOpenAccess W2013608618 @default.
- W2013608618 hasPrimaryLocation W20136086181 @default.
- W2013608618 hasRelatedWork W1994103032 @default.
- W2013608618 hasRelatedWork W2011052271 @default.
- W2013608618 hasRelatedWork W2014315543 @default.
- W2013608618 hasRelatedWork W2030075758 @default.
- W2013608618 hasRelatedWork W2082293200 @default.
- W2013608618 hasRelatedWork W2366754381 @default.
- W2013608618 hasRelatedWork W2380293314 @default.
- W2013608618 hasRelatedWork W2886057184 @default.
- W2013608618 hasRelatedWork W2943188944 @default.
- W2013608618 hasRelatedWork W4285802202 @default.
- W2013608618 hasVolume "258" @default.
- W2013608618 isParatext "false" @default.
- W2013608618 isRetracted "false" @default.
- W2013608618 magId "2013608618" @default.
- W2013608618 workType "article" @default.