- W2014098319 abstract "Aerosol-assisted metallo-organic CVD (MOCVD) method (spray pyrolysis) has been employed to deposit thin films of solid electrolyte onto dense (NiO + YDC) substrates in our laboratory. The β-diketonate precursors Ce(tmhd)4 and Y(tmhd)3 were chosen as the source materials for deposition of yttria-doped ceria (YDC) thin films in the temperature range 500–700°C. Scanning electron microscopy (SEM) observation revealed the YDC films to have uniform and nanometric grains, with thickness ranging from 0.18 to 1.2 μm with different deposition times. X-ray diffraction (XRD) analyses showed that the films possessed a single phase with a fluorite cubic structure. X-ray photoelectron spectroscopy (XPS) showed that the elemental ratio Y/Ce of the film was close to that of the mixed solution precursor at a deposition temperature 600°C. After being reduced in an H2 atmosphere at 600°C for 10 h, the (NiO + YDC) substrate was converted into Ni + YDC. The YDC thin film was found to be N2 leak tight up to the pressure of 0.65 MPa. AC impedance analyses showed that the ionic conductivity of YDC thin film on (Ni + YDC) substrate was slightly less than that of YDC prepared by sintering, but higher than that of yttria-stabilized zirconia (YSZ). These results suggest that the YDC thin film obtained by aerosol-assisted MOCVD is a potential solid electrolyte alternative to YSZ, at intermediate operating temperatures, for solid oxide fuel cell (SOFC) applications." @default.
- W2014098319 created "2016-06-24" @default.
- W2014098319 creator A5002201967 @default.
- W2014098319 creator A5036016266 @default.
- W2014098319 creator A5057765244 @default.
- W2014098319 creator A5073738793 @default.
- W2014098319 creator A5085787693 @default.
- W2014098319 date "2000-11-01" @default.
- W2014098319 modified "2023-10-18" @default.
- W2014098319 title "Aerosol-assisted MOCVD deposition of YDC thin films on (NiO + YDC) substrates" @default.
- W2014098319 cites W1971200136 @default.
- W2014098319 cites W1971917372 @default.
- W2014098319 cites W1991380893 @default.
- W2014098319 cites W1999578410 @default.
- W2014098319 cites W2005643745 @default.
- W2014098319 cites W2025021122 @default.
- W2014098319 cites W2060104283 @default.
- W2014098319 cites W2148888953 @default.
- W2014098319 doi "https://doi.org/10.1016/s0025-5408(00)00449-9" @default.
- W2014098319 hasPublicationYear "2000" @default.
- W2014098319 type Work @default.
- W2014098319 sameAs 2014098319 @default.
- W2014098319 citedByCount "28" @default.
- W2014098319 countsByYear W20140983192012 @default.
- W2014098319 countsByYear W20140983192013 @default.
- W2014098319 countsByYear W20140983192015 @default.
- W2014098319 countsByYear W20140983192016 @default.
- W2014098319 countsByYear W20140983192020 @default.
- W2014098319 crossrefType "journal-article" @default.
- W2014098319 hasAuthorship W2014098319A5002201967 @default.
- W2014098319 hasAuthorship W2014098319A5036016266 @default.
- W2014098319 hasAuthorship W2014098319A5057765244 @default.
- W2014098319 hasAuthorship W2014098319A5073738793 @default.
- W2014098319 hasAuthorship W2014098319A5085787693 @default.
- W2014098319 hasConcept C110738630 @default.
- W2014098319 hasConcept C111368507 @default.
- W2014098319 hasConcept C113196181 @default.
- W2014098319 hasConcept C123609680 @default.
- W2014098319 hasConcept C127313418 @default.
- W2014098319 hasConcept C127413603 @default.
- W2014098319 hasConcept C134132462 @default.
- W2014098319 hasConcept C159985019 @default.
- W2014098319 hasConcept C161790260 @default.
- W2014098319 hasConcept C171250308 @default.
- W2014098319 hasConcept C175665537 @default.
- W2014098319 hasConcept C175708663 @default.
- W2014098319 hasConcept C178790620 @default.
- W2014098319 hasConcept C185592680 @default.
- W2014098319 hasConcept C19067145 @default.
- W2014098319 hasConcept C192562407 @default.
- W2014098319 hasConcept C26771246 @default.
- W2014098319 hasConcept C2777289219 @default.
- W2014098319 hasConcept C2779227376 @default.
- W2014098319 hasConcept C42360764 @default.
- W2014098319 hasConcept C74575197 @default.
- W2014098319 hasConcept C96410337 @default.
- W2014098319 hasConceptScore W2014098319C110738630 @default.
- W2014098319 hasConceptScore W2014098319C111368507 @default.
- W2014098319 hasConceptScore W2014098319C113196181 @default.
- W2014098319 hasConceptScore W2014098319C123609680 @default.
- W2014098319 hasConceptScore W2014098319C127313418 @default.
- W2014098319 hasConceptScore W2014098319C127413603 @default.
- W2014098319 hasConceptScore W2014098319C134132462 @default.
- W2014098319 hasConceptScore W2014098319C159985019 @default.
- W2014098319 hasConceptScore W2014098319C161790260 @default.
- W2014098319 hasConceptScore W2014098319C171250308 @default.
- W2014098319 hasConceptScore W2014098319C175665537 @default.
- W2014098319 hasConceptScore W2014098319C175708663 @default.
- W2014098319 hasConceptScore W2014098319C178790620 @default.
- W2014098319 hasConceptScore W2014098319C185592680 @default.
- W2014098319 hasConceptScore W2014098319C19067145 @default.
- W2014098319 hasConceptScore W2014098319C192562407 @default.
- W2014098319 hasConceptScore W2014098319C26771246 @default.
- W2014098319 hasConceptScore W2014098319C2777289219 @default.
- W2014098319 hasConceptScore W2014098319C2779227376 @default.
- W2014098319 hasConceptScore W2014098319C42360764 @default.
- W2014098319 hasConceptScore W2014098319C74575197 @default.
- W2014098319 hasConceptScore W2014098319C96410337 @default.
- W2014098319 hasIssue "14-15" @default.
- W2014098319 hasLocation W20140983191 @default.
- W2014098319 hasOpenAccess W2014098319 @default.
- W2014098319 hasPrimaryLocation W20140983191 @default.
- W2014098319 hasRelatedWork W1990574691 @default.
- W2014098319 hasRelatedWork W1993162244 @default.
- W2014098319 hasRelatedWork W2008815603 @default.
- W2014098319 hasRelatedWork W2394155613 @default.
- W2014098319 hasRelatedWork W2538112308 @default.
- W2014098319 hasRelatedWork W2790297317 @default.
- W2014098319 hasRelatedWork W2997596721 @default.
- W2014098319 hasRelatedWork W4230902934 @default.
- W2014098319 hasRelatedWork W4367334242 @default.
- W2014098319 hasRelatedWork W2584279877 @default.
- W2014098319 hasVolume "35" @default.
- W2014098319 isParatext "false" @default.
- W2014098319 isRetracted "false" @default.
- W2014098319 magId "2014098319" @default.
- W2014098319 workType "article" @default.