- W2014457598 abstract "Nanocrystalline TiN coating was deposited by means of the cathodic arc method on stainless steels types X6CrNiTi18-10 and X39Cr13. Both steels were subjected to thermal treatment in order to obtain substrates of different hardness: 1.7 GPa, 2.8 GPa and 4.6 GPa. The TiN coating was 3.7 μm thick. The TiN coating has strong (1 1 1) crystallographic orientation and fine crystalline structure of δ-TiN phase. The TiN coating is characterized by high hardness (25.4 GPa) and good adhesion. The adhesion increases with the substrate hardness. The evaluation of TiN coating resistance to cavitation erosion is based on the investigation performed in a cavitation tunnel with a slot cavitator and tap water as a medium. The estimated cavitation resistance parameters of coating were the incubation period of damage and the total mass loss after the whole test. It has been confirmed that the incubation periods of the coated steels were from 2 to 4 times longer than that of the uncoated steels. The mass losses of the coated steels decrease approximately 2.5 times in comparison with the uncoated steels. The scanning microscope analysis indicates that the damage of TiN coating is mainly due to its delamination. The character of the coating and substrate damage in multiple locations indicates that the hard coating micro-particles torn off during the cavitation bubbles implosion hit against the coating and the revealed areas of substrate. As a result, the coating and especially the substrate of relatively low hardness beside cavitation erosion are subject to solid particle erosion with the hard torn off micro-particles of coating." @default.
- W2014457598 created "2016-06-24" @default.
- W2014457598 creator A5070586262 @default.
- W2014457598 creator A5086321848 @default.
- W2014457598 date "2007-09-01" @default.
- W2014457598 modified "2023-10-16" @default.
- W2014457598 title "Influence of the substrate hardness on the cavitation erosion resistance of TiN coating" @default.
- W2014457598 cites W2001153595 @default.
- W2014457598 cites W2006662428 @default.
- W2014457598 cites W2013865786 @default.
- W2014457598 cites W2016688762 @default.
- W2014457598 cites W2033988895 @default.
- W2014457598 cites W2050263081 @default.
- W2014457598 cites W2058962715 @default.
- W2014457598 cites W2077855696 @default.
- W2014457598 cites W2079243663 @default.
- W2014457598 cites W2086933933 @default.
- W2014457598 cites W2087095817 @default.
- W2014457598 cites W2087309823 @default.
- W2014457598 doi "https://doi.org/10.1016/j.wear.2007.02.003" @default.
- W2014457598 hasPublicationYear "2007" @default.
- W2014457598 type Work @default.
- W2014457598 sameAs 2014457598 @default.
- W2014457598 citedByCount "64" @default.
- W2014457598 countsByYear W20144575982012 @default.
- W2014457598 countsByYear W20144575982013 @default.
- W2014457598 countsByYear W20144575982014 @default.
- W2014457598 countsByYear W20144575982015 @default.
- W2014457598 countsByYear W20144575982016 @default.
- W2014457598 countsByYear W20144575982017 @default.
- W2014457598 countsByYear W20144575982018 @default.
- W2014457598 countsByYear W20144575982019 @default.
- W2014457598 countsByYear W20144575982020 @default.
- W2014457598 countsByYear W20144575982021 @default.
- W2014457598 countsByYear W20144575982022 @default.
- W2014457598 countsByYear W20144575982023 @default.
- W2014457598 crossrefType "journal-article" @default.
- W2014457598 hasAuthorship W2014457598A5070586262 @default.
- W2014457598 hasAuthorship W2014457598A5086321848 @default.
- W2014457598 hasConcept C111368507 @default.
- W2014457598 hasConcept C121332964 @default.
- W2014457598 hasConcept C127313418 @default.
- W2014457598 hasConcept C147789679 @default.
- W2014457598 hasConcept C159985019 @default.
- W2014457598 hasConcept C17525397 @default.
- W2014457598 hasConcept C185592680 @default.
- W2014457598 hasConcept C191897082 @default.
- W2014457598 hasConcept C192562407 @default.
- W2014457598 hasConcept C205871581 @default.
- W2014457598 hasConcept C207057113 @default.
- W2014457598 hasConcept C2777289219 @default.
- W2014457598 hasConcept C2781448156 @default.
- W2014457598 hasConcept C525849907 @default.
- W2014457598 hasConcept C57879066 @default.
- W2014457598 hasConcept C89395315 @default.
- W2014457598 hasConceptScore W2014457598C111368507 @default.
- W2014457598 hasConceptScore W2014457598C121332964 @default.
- W2014457598 hasConceptScore W2014457598C127313418 @default.
- W2014457598 hasConceptScore W2014457598C147789679 @default.
- W2014457598 hasConceptScore W2014457598C159985019 @default.
- W2014457598 hasConceptScore W2014457598C17525397 @default.
- W2014457598 hasConceptScore W2014457598C185592680 @default.
- W2014457598 hasConceptScore W2014457598C191897082 @default.
- W2014457598 hasConceptScore W2014457598C192562407 @default.
- W2014457598 hasConceptScore W2014457598C205871581 @default.
- W2014457598 hasConceptScore W2014457598C207057113 @default.
- W2014457598 hasConceptScore W2014457598C2777289219 @default.
- W2014457598 hasConceptScore W2014457598C2781448156 @default.
- W2014457598 hasConceptScore W2014457598C525849907 @default.
- W2014457598 hasConceptScore W2014457598C57879066 @default.
- W2014457598 hasConceptScore W2014457598C89395315 @default.
- W2014457598 hasIssue "1-6" @default.
- W2014457598 hasLocation W20144575981 @default.
- W2014457598 hasOpenAccess W2014457598 @default.
- W2014457598 hasPrimaryLocation W20144575981 @default.
- W2014457598 hasRelatedWork W1984055990 @default.
- W2014457598 hasRelatedWork W1991793670 @default.
- W2014457598 hasRelatedWork W2092136578 @default.
- W2014457598 hasRelatedWork W2360748184 @default.
- W2014457598 hasRelatedWork W2363148876 @default.
- W2014457598 hasRelatedWork W2380293314 @default.
- W2014457598 hasRelatedWork W2386678136 @default.
- W2014457598 hasRelatedWork W3082440218 @default.
- W2014457598 hasRelatedWork W3201544005 @default.
- W2014457598 hasRelatedWork W4225379450 @default.
- W2014457598 hasVolume "263" @default.
- W2014457598 isParatext "false" @default.
- W2014457598 isRetracted "false" @default.
- W2014457598 magId "2014457598" @default.
- W2014457598 workType "article" @default.