- W2015505535 abstract "The effects of aging of a Ni-rich Ni-Ta-Cr alloy on the microstructure (using optical and scanning electron microscopy) and hardness are presented. In the solution-annealed condition (1280°C, 4 h) the microstructure consisted of a face-centered cubic matrix and about 10% of a Ni3Ta type phase, which contained some Cr; the hardness was about 530 DPH. No change in the microstructure nor significant change in hardness occurred upon aging at 600°C for 1,000 h. Aging from 700 to 1000°C produced a significant decrease in hardness, to about 330 DPH after 1000 h. A lamellar product formed, usually initiating at the secondary particles present in the solution-annealed condition. At longer times and higher temperatures, a coarser lamellar product formed. The results of qualitative EDS analysis of the phases are reported." @default.
- W2015505535 created "2016-06-24" @default.
- W2015505535 creator A5073055640 @default.
- W2015505535 creator A5080611881 @default.
- W2015505535 date "1989-05-01" @default.
- W2015505535 modified "2023-09-23" @default.
- W2015505535 title "Microstructures of a Ni-9.6 at.% Ta-16.6 at.% Cr alloy after aging up to 1000 hours from 600 to 1,000°C" @default.
- W2015505535 cites W2026136279 @default.
- W2015505535 cites W2081503768 @default.
- W2015505535 doi "https://doi.org/10.1016/0026-0800(89)90001-3" @default.
- W2015505535 hasPublicationYear "1989" @default.
- W2015505535 type Work @default.
- W2015505535 sameAs 2015505535 @default.
- W2015505535 citedByCount "0" @default.
- W2015505535 crossrefType "journal-article" @default.
- W2015505535 hasAuthorship W2015505535A5073055640 @default.
- W2015505535 hasAuthorship W2015505535A5080611881 @default.
- W2015505535 hasConcept C159985019 @default.
- W2015505535 hasConcept C178790620 @default.
- W2015505535 hasConcept C185592680 @default.
- W2015505535 hasConcept C191897082 @default.
- W2015505535 hasConcept C192562407 @default.
- W2015505535 hasConcept C26771246 @default.
- W2015505535 hasConcept C2780026712 @default.
- W2015505535 hasConcept C44280652 @default.
- W2015505535 hasConcept C77017923 @default.
- W2015505535 hasConcept C77851909 @default.
- W2015505535 hasConcept C87976508 @default.
- W2015505535 hasConceptScore W2015505535C159985019 @default.
- W2015505535 hasConceptScore W2015505535C178790620 @default.
- W2015505535 hasConceptScore W2015505535C185592680 @default.
- W2015505535 hasConceptScore W2015505535C191897082 @default.
- W2015505535 hasConceptScore W2015505535C192562407 @default.
- W2015505535 hasConceptScore W2015505535C26771246 @default.
- W2015505535 hasConceptScore W2015505535C2780026712 @default.
- W2015505535 hasConceptScore W2015505535C44280652 @default.
- W2015505535 hasConceptScore W2015505535C77017923 @default.
- W2015505535 hasConceptScore W2015505535C77851909 @default.
- W2015505535 hasConceptScore W2015505535C87976508 @default.
- W2015505535 hasIssue "3" @default.
- W2015505535 hasLocation W20155055351 @default.
- W2015505535 hasOpenAccess W2015505535 @default.
- W2015505535 hasPrimaryLocation W20155055351 @default.
- W2015505535 hasRelatedWork W2014792072 @default.
- W2015505535 hasRelatedWork W2020485099 @default.
- W2015505535 hasRelatedWork W2090963821 @default.
- W2015505535 hasRelatedWork W2362878368 @default.
- W2015505535 hasRelatedWork W2369435632 @default.
- W2015505535 hasRelatedWork W2375844564 @default.
- W2015505535 hasRelatedWork W2383229841 @default.
- W2015505535 hasRelatedWork W2386864870 @default.
- W2015505535 hasRelatedWork W2509646160 @default.
- W2015505535 hasRelatedWork W2513959326 @default.
- W2015505535 hasVolume "22" @default.
- W2015505535 isParatext "false" @default.
- W2015505535 isRetracted "false" @default.
- W2015505535 magId "2015505535" @default.
- W2015505535 workType "article" @default.