• W2015904920 abstract "Single fibre pushout testing has been used to measure the load needed to displace a fibre, as a function of its aspect ratio. This has been done for SiC monofilaments, having duplex carbon/TiB2 coatings, embedded in a matrix of Ti6Al4V. Wedge-shaped specimens have been used, allowing pushout of fibres with a range of aspect ratios from a single specimen. Partially pushed-out fibres have also been pushed back into the matrix. Specimens have been examined in the as-fabricated form and also after subsequent heat treatments. Analysis of the results indicates that in all cases it was the resistance to the onset of frictional sliding which was determining the pushout load. Values of the interfacial shear stress necessary for frictional sliding, τfr, have been established, although it was not possible to measure separately the coefficient of static friction or the residual radial compressive stress. The value of τfr was found to increase progressively on heat treating the composite. Preliminary chemical analysis work suggests that this results from an interfacial reaction, possibly one which causes the carbon layer to become reduced in thickness. On utilise des essais d'arrachage sur une fibre isolée pour mesurer la charge nécessaire pour déplacer une fibre en fonction de son rapport d'aspect. Ce travail a été fait pour des monofilaments de SiC ayant un revêtement double carbone/TiB2, enchassés dans une matrice de Ti6 Al4V. Des échantillons en forme de coin sont utilisés, ce qui permet l'arrachage de fibres présentant une gamme de rapports d'aspect à partir d'un seul échantillon. Des fibres partiellement arrachées ont aussi été renfoncées dans la matrice. Les échantillons sont examinés sous leur forme brute de fabrication ainsi qu'aprés des traitements thermiques. L'analyse des résultats indique que dans tous les cas c'est la résistance à l'établissement du glissement par friction qui détermine la charge d'arrachage. Les valeurs de la contrainte de cisaillement interfaciale nécessaire pour le glissement par friction, τfr, sont établies, quoiqu'il ne soit pas possible de mesurer séparément le coefficient de friction statique ou la contrainte de compression radiale résiduelle. On trouve que la valeur de τfr croît progressivement si l'on traite thermiquement le composite. Un travail d'analyse chimique préliminaire suggère que ceci provient d'une réaction interfaciale, par exemple celle qui réduit l'épaisseur de la couche de carbone. Mit Versuchen zum Herausziehen einzelner Fasern wird die zur Verschiebung einer Faser benötigte Last in Abhängigkeit von deren Aspektverhältnis gemessen. Das Material besteht aus SiC-Fasern mit Kohlenstoff-TiB2-Doppelüberzug, die in einer Matrix aus Ti6 Al4V eingebettet sind. Keilförmige Proben werden benutzt; diese ermöglichen das Herausziehen von Fasern mit unterschiedlichem Aspektverhältnis. Auch werden teilweise herausgezogene Fasern in die Matrix zurückgestoßen. Die Proben werden wie hergestellt untersucht, außerdem nach verschiedenen Wärmebehandlungen. Die Analyse der Ergebnisse weist darauf hin, daß in allen Fällen der Widerstand gegen den Einsatz de Reibungsgleitung die Ausziehlast bestimmt. Werte für die Grenzflächenscherkraft τfr, die für diese Reibungsgleitung nötig ist, werden bestimmt, wenn es auch nicht möglich war, den Koeffizienten der statischen Reibung oder die radiale Rest-Kompressionsspannung getrennt zu bestimmen. Der Wert für τfr nimmt progressiv mit der Wärmebehandlung zu. Vorläufige chemische Untersuchungen legen nahe, daß dieses Verhalten von einer Grenzflächenreaktion herrührt, möglicherweise von einer, die die Dicke der Kohlenstoffschicht reduziert." @default.
• W2015904920 created "2016-06-24" @default.
• W2015904920 creator A5018285975 @default.
• W2015904920 creator A5032208095 @default.
• W2015904920 date "1992-01-01" @default.
• W2015904920 modified "2023-10-16" @default.
• W2015904920 title "The use of single fibre pushout testing to explore interfacial mechanics in SiC monofilament-reinforced Ti—II. Application of the test to composite material" @default.
• W2015904920 cites W1970820608 @default.
• W2015904920 cites W1986267349 @default.
• W2015904920 cites W1995491268 @default.
• W2015904920 cites W1997533319 @default.
• W2015904920 cites W1999079726 @default.
• W2015904920 cites W1999810704 @default.
• W2015904920 cites W2008377735 @default.
• W2015904920 cites W2009405194 @default.
• W2015904920 cites W2023370962 @default.
• W2015904920 cites W2029675666 @default.
• W2015904920 cites W2073795626 @default.
• W2015904920 cites W2084857292 @default.
• W2015904920 doi "https://doi.org/10.1016/0956-7151(92)90207-u" @default.
• W2015904920 hasPublicationYear "1992" @default.
• W2015904920 type Work @default.
• W2015904920 sameAs 2015904920 @default.
• W2015904920 citedByCount "54" @default.
• W2015904920 countsByYear W20159049202016 @default.
• W2015904920 countsByYear W20159049202018 @default.
• W2015904920 countsByYear W20159049202020 @default.
• W2015904920 crossrefType "journal-article" @default.
• W2015904920 hasAuthorship W2015904920A5018285975 @default.
• W2015904920 hasAuthorship W2015904920A5032208095 @default.
• W2015904920 hasConcept C104779481 @default.
• W2015904920 hasConcept C159985019 @default.
• W2015904920 hasConcept C192562407 @default.
• W2015904920 hasConcept C2524010 @default.
• W2015904920 hasConcept C33923547 @default.
• W2015904920 hasConcept C47422493 @default.
• W2015904920 hasConceptScore W2015904920C104779481 @default.
• W2015904920 hasConceptScore W2015904920C159985019 @default.
• W2015904920 hasConceptScore W2015904920C192562407 @default.
• W2015904920 hasConceptScore W2015904920C2524010 @default.
• W2015904920 hasConceptScore W2015904920C33923547 @default.
• W2015904920 hasConceptScore W2015904920C47422493 @default.
• W2015904920 hasIssue "1" @default.
• W2015904920 hasLocation W20159049201 @default.
• W2015904920 hasOpenAccess W2015904920 @default.
• W2015904920 hasPrimaryLocation W20159049201 @default.
• W2015904920 hasRelatedWork W2005496670 @default.
• W2015904920 hasRelatedWork W2053517630 @default.
• W2015904920 hasRelatedWork W2075449049 @default.
• W2015904920 hasRelatedWork W2380293314 @default.
• W2015904920 hasRelatedWork W2900524175 @default.
• W2015904920 hasRelatedWork W3043268847 @default.
• W2015904920 hasRelatedWork W3048672776 @default.
• W2015904920 hasRelatedWork W3082440218 @default.
• W2015904920 hasRelatedWork W4285010844 @default.
• W2015904920 hasRelatedWork W2463824739 @default.
• W2015904920 hasVolume "40" @default.
• W2015904920 isParatext "false" @default.
• W2015904920 isRetracted "false" @default.
• W2015904920 magId "2015904920" @default.
• W2015904920 workType "article" @default.