- W2016029478 abstract "The Fe 3 Al intermetallics compounds bulks were fabricated by hot-pressing process in this research. The Fe 3 Al intermetallics compounds powders were fabricated by mechanical alloying and heat treatment process. The phase composition and microstructure of the Fe 3 Al intermetallics compounds powders produced by mechanical alloying and heat treatment were investigated. The phase composition and microstructure of the Fe 3 Al intermetallics compounds bulks produced by hot-pressing process were investigated. The XRD patterns results showed that the Fe-Al intermetallics compounds powders were fabricated by mechanical alloying for 60h. Then the Fe 3 Al intermetallics compounds powders were fabricated by heat treatment at 800°C and 1000°C. The microstructure showed that the mean particles sizes of the Fe-Al intermetallics compounds powders produced by mechanical alloying decreased remarkably with the increase of milling time. The microstructure showed that the mean particles size of the Fe 3 Al intermetallics compounds powders produced by mechanical alloying for 60h and heat treatment was rather fine and about 4-5μm. The Fe 3 Al intermetallics compounds bulks were fabricated by hot-pressing process at 1100°C for 2h under the pressure of 35MPa. The XRD patterns results showed that there existed only Fe 3 Al intermetallics compounds phase in the sintered bulks. The Fe 3 Al intermetallics compounds bulks exhibited the homogenous and compact microstructure. The mean particles size of the Fe 3 Al intermetallics compounds was rather fine and about 2-3μm. The relative density of the Fe 3 Al intermetallics compounds sintered bulks was about 99.2%. So the Fe 3 Al intermetallics compounds bulks with the high relative density were fabricated by hot-pressing process." @default.
- W2016029478 created "2016-06-24" @default.
- W2016029478 creator A5075735223 @default.
- W2016029478 date "2011-01-01" @default.
- W2016029478 modified "2023-09-25" @default.
- W2016029478 title "Investigation of Fabrication and Microstructure of the Fe<sub>3</sub>Al Intermetallics Compounds Bulks by Hot-Pressing Process" @default.
- W2016029478 cites W1770138646 @default.
- W2016029478 cites W1964991755 @default.
- W2016029478 cites W1968959538 @default.
- W2016029478 cites W1989719103 @default.
- W2016029478 cites W2002581746 @default.
- W2016029478 cites W2009806387 @default.
- W2016029478 cites W2027774289 @default.
- W2016029478 cites W2030955100 @default.
- W2016029478 cites W2063154939 @default.
- W2016029478 cites W2078751341 @default.
- W2016029478 cites W2081235596 @default.
- W2016029478 cites W2087791385 @default.
- W2016029478 cites W2092501200 @default.
- W2016029478 cites W2094945421 @default.
- W2016029478 cites W4241874697 @default.
- W2016029478 doi "https://doi.org/10.4028/www.scientific.net/amr.183-185.1707" @default.
- W2016029478 hasPublicationYear "2011" @default.
- W2016029478 type Work @default.
- W2016029478 sameAs 2016029478 @default.
- W2016029478 citedByCount "0" @default.
- W2016029478 crossrefType "journal-article" @default.
- W2016029478 hasAuthorship W2016029478A5075735223 @default.
- W2016029478 hasConcept C136525101 @default.
- W2016029478 hasConcept C142724271 @default.
- W2016029478 hasConcept C159985019 @default.
- W2016029478 hasConcept C178790620 @default.
- W2016029478 hasConcept C185592680 @default.
- W2016029478 hasConcept C191897082 @default.
- W2016029478 hasConcept C192562407 @default.
- W2016029478 hasConcept C204787440 @default.
- W2016029478 hasConcept C27501479 @default.
- W2016029478 hasConcept C2776578615 @default.
- W2016029478 hasConcept C2780026712 @default.
- W2016029478 hasConcept C44280652 @default.
- W2016029478 hasConcept C71924100 @default.
- W2016029478 hasConcept C87976508 @default.
- W2016029478 hasConcept C93021684 @default.
- W2016029478 hasConceptScore W2016029478C136525101 @default.
- W2016029478 hasConceptScore W2016029478C142724271 @default.
- W2016029478 hasConceptScore W2016029478C159985019 @default.
- W2016029478 hasConceptScore W2016029478C178790620 @default.
- W2016029478 hasConceptScore W2016029478C185592680 @default.
- W2016029478 hasConceptScore W2016029478C191897082 @default.
- W2016029478 hasConceptScore W2016029478C192562407 @default.
- W2016029478 hasConceptScore W2016029478C204787440 @default.
- W2016029478 hasConceptScore W2016029478C27501479 @default.
- W2016029478 hasConceptScore W2016029478C2776578615 @default.
- W2016029478 hasConceptScore W2016029478C2780026712 @default.
- W2016029478 hasConceptScore W2016029478C44280652 @default.
- W2016029478 hasConceptScore W2016029478C71924100 @default.
- W2016029478 hasConceptScore W2016029478C87976508 @default.
- W2016029478 hasConceptScore W2016029478C93021684 @default.
- W2016029478 hasLocation W20160294781 @default.
- W2016029478 hasOpenAccess W2016029478 @default.
- W2016029478 hasPrimaryLocation W20160294781 @default.
- W2016029478 hasRelatedWork W1559758505 @default.
- W2016029478 hasRelatedWork W2042576283 @default.
- W2016029478 hasRelatedWork W2240913852 @default.
- W2016029478 hasRelatedWork W2331779382 @default.
- W2016029478 hasRelatedWork W2332736103 @default.
- W2016029478 hasRelatedWork W2351626378 @default.
- W2016029478 hasRelatedWork W2743305543 @default.
- W2016029478 hasRelatedWork W2793432596 @default.
- W2016029478 hasRelatedWork W3000072562 @default.
- W2016029478 hasRelatedWork W3156761922 @default.
- W2016029478 hasVolume "183-185" @default.
- W2016029478 isParatext "false" @default.
- W2016029478 isRetracted "false" @default.
- W2016029478 magId "2016029478" @default.
- W2016029478 workType "article" @default.