- W2016074189 abstract "The effects of crack size, stress ratio and absorbed hydrogen on the fatigue crack propagation characteristics of high strength steel were studied near threshold regime. The test material was SCM440H low alloy steel. The material was quenched in vacuum and tempered at low temperature to achieve high strength and to lower the initial content of hydrogen of the material. The effects of crack size and stress ratio on the fatigue crack propagation rate and threshold stress intensity factor were investigated in air at first. These data offered a baseline as a reference. The effect of absorbed hydrogen was examined using a material in which hydrogen was introduced by cathodic charging. It was verified that the absorbed hydrogen in high strength steel affected the high cycle fatigue crack propagation characteristics. The fatigue crack propagation rate near threshold region was accelerated and ΔKth was lowered. The concentration of about 1ppm hydrogen caused 20% reduction of ΔKth. Since absorbed hydrogen has an influence even on high cycle fatigue crack propagation, it should be taken into account in the evaluation of defect of hydrogen utilization machine." @default.
- W2016074189 created "2016-06-24" @default.
- W2016074189 creator A5045695131 @default.
- W2016074189 creator A5066135217 @default.
- W2016074189 creator A5073212860 @default.
- W2016074189 creator A5082779723 @default.
- W2016074189 creator A5086838889 @default.
- W2016074189 date "2005-01-01" @default.
- W2016074189 modified "2023-09-24" @default.
- W2016074189 title "Effects of Crack Size, Stress Ratio and Hydrogen on the Near Threshold Fatigue Crack Propagation of High Strength Steel" @default.
- W2016074189 cites W2317799699 @default.
- W2016074189 cites W2322691876 @default.
- W2016074189 cites W2323949685 @default.
- W2016074189 cites W250113792 @default.
- W2016074189 doi "https://doi.org/10.2472/jsms.54.1237" @default.
- W2016074189 hasPublicationYear "2005" @default.
- W2016074189 type Work @default.
- W2016074189 sameAs 2016074189 @default.
- W2016074189 citedByCount "9" @default.
- W2016074189 countsByYear W20160741892021 @default.
- W2016074189 countsByYear W20160741892022 @default.
- W2016074189 crossrefType "journal-article" @default.
- W2016074189 hasAuthorship W2016074189A5045695131 @default.
- W2016074189 hasAuthorship W2016074189A5066135217 @default.
- W2016074189 hasAuthorship W2016074189A5073212860 @default.
- W2016074189 hasAuthorship W2016074189A5082779723 @default.
- W2016074189 hasAuthorship W2016074189A5086838889 @default.
- W2016074189 hasBestOaLocation W20160741891 @default.
- W2016074189 hasConcept C127413603 @default.
- W2016074189 hasConcept C131850400 @default.
- W2016074189 hasConcept C138885662 @default.
- W2016074189 hasConcept C147789679 @default.
- W2016074189 hasConcept C159985019 @default.
- W2016074189 hasConcept C17525397 @default.
- W2016074189 hasConcept C178790620 @default.
- W2016074189 hasConcept C185592680 @default.
- W2016074189 hasConcept C191897082 @default.
- W2016074189 hasConcept C192562407 @default.
- W2016074189 hasConcept C205871581 @default.
- W2016074189 hasConcept C21036866 @default.
- W2016074189 hasConcept C2780026712 @default.
- W2016074189 hasConcept C28539199 @default.
- W2016074189 hasConcept C41895202 @default.
- W2016074189 hasConcept C512968161 @default.
- W2016074189 hasConcept C54303661 @default.
- W2016074189 hasConcept C59085676 @default.
- W2016074189 hasConcept C66938386 @default.
- W2016074189 hasConcept C69809600 @default.
- W2016074189 hasConcept C75512024 @default.
- W2016074189 hasConcept C89395315 @default.
- W2016074189 hasConceptScore W2016074189C127413603 @default.
- W2016074189 hasConceptScore W2016074189C131850400 @default.
- W2016074189 hasConceptScore W2016074189C138885662 @default.
- W2016074189 hasConceptScore W2016074189C147789679 @default.
- W2016074189 hasConceptScore W2016074189C159985019 @default.
- W2016074189 hasConceptScore W2016074189C17525397 @default.
- W2016074189 hasConceptScore W2016074189C178790620 @default.
- W2016074189 hasConceptScore W2016074189C185592680 @default.
- W2016074189 hasConceptScore W2016074189C191897082 @default.
- W2016074189 hasConceptScore W2016074189C192562407 @default.
- W2016074189 hasConceptScore W2016074189C205871581 @default.
- W2016074189 hasConceptScore W2016074189C21036866 @default.
- W2016074189 hasConceptScore W2016074189C2780026712 @default.
- W2016074189 hasConceptScore W2016074189C28539199 @default.
- W2016074189 hasConceptScore W2016074189C41895202 @default.
- W2016074189 hasConceptScore W2016074189C512968161 @default.
- W2016074189 hasConceptScore W2016074189C54303661 @default.
- W2016074189 hasConceptScore W2016074189C59085676 @default.
- W2016074189 hasConceptScore W2016074189C66938386 @default.
- W2016074189 hasConceptScore W2016074189C69809600 @default.
- W2016074189 hasConceptScore W2016074189C75512024 @default.
- W2016074189 hasConceptScore W2016074189C89395315 @default.
- W2016074189 hasIssue "12" @default.
- W2016074189 hasLocation W20160741891 @default.
- W2016074189 hasOpenAccess W2016074189 @default.
- W2016074189 hasPrimaryLocation W20160741891 @default.
- W2016074189 hasRelatedWork W1485836223 @default.
- W2016074189 hasRelatedWork W2016074189 @default.
- W2016074189 hasRelatedWork W2019649257 @default.
- W2016074189 hasRelatedWork W2021639701 @default.
- W2016074189 hasRelatedWork W2051520959 @default.
- W2016074189 hasRelatedWork W2055638518 @default.
- W2016074189 hasRelatedWork W2074617172 @default.
- W2016074189 hasRelatedWork W2609714811 @default.
- W2016074189 hasRelatedWork W2901912464 @default.
- W2016074189 hasRelatedWork W579541462 @default.
- W2016074189 hasVolume "54" @default.
- W2016074189 isParatext "false" @default.
- W2016074189 isRetracted "false" @default.
- W2016074189 magId "2016074189" @default.
- W2016074189 workType "article" @default.