- W2016104561 endingPage "7617" @default.
- W2016104561 startingPage "7611" @default.
- W2016104561 abstract "The structures and electrochemical properties of a series of annealed AB5, La10.5Ce4.3Pr0.5Nd1.4Ni64.3−xCo5.0Mn4.6Al6.0Cu3.2Zr0.2Fex (x = 0.0, 0.5, 1.0, and 1.5), metal hydride alloys were studied for improvement in the low-temperature performance of nickel/metal hydride batteries. As the Fe-content in the alloy increases, the following was observed: lattice constant a first increases and then decreases; lattice constant c and c/a ratio increase; unit cell volume increases monotonically; the main AB5 phase becomes hyper-stoichiometric containing no Zr and its Fe-content is close to the target composition; an additional AB7 phase appears; maximum gaseous hydrogen storage, PCT plateau pressure, and hysteresis first increase and then decrease while the trend of reversible hydrogen storage is the opposite; enthalpy and entropy of hydride formation remain unchanged; electrochemical full capacity decreases while the high-rate dischargeability and surface reaction exchange current increase; and bulk hydrogen diffusion increases first and then decreases by very small amounts. The product of charge-transfer resistance and double-layer capacitance measured at −40 °C indicates an improvement in the surface catalysis with Fe-addition. In the sealed cell, the addition of Fe improves both the specific power and −10 °C low temperature performance, slightly reduces the charge retention, and first marginally improves and then deteriorates the cycle life performance." @default.
- W2016104561 created "2016-06-24" @default.
- W2016104561 creator A5002204604 @default.
- W2016104561 creator A5007215384 @default.
- W2016104561 creator A5013542315 @default.
- W2016104561 creator A5056736167 @default.
- W2016104561 creator A5065337925 @default.
- W2016104561 date "2011-07-01" @default.
- W2016104561 modified "2023-10-16" @default.
- W2016104561 title "Improvement in the low-temperature performance of AB5 metal hydride alloys by Fe-addition" @default.
- W2016104561 cites W1502110682 @default.
- W2016104561 cites W1972739521 @default.
- W2016104561 cites W1972758954 @default.
- W2016104561 cites W1975462370 @default.
- W2016104561 cites W1977976527 @default.
- W2016104561 cites W1980692159 @default.
- W2016104561 cites W1984144086 @default.
- W2016104561 cites W1986257454 @default.
- W2016104561 cites W1987107830 @default.
- W2016104561 cites W1988783707 @default.
- W2016104561 cites W1992768154 @default.
- W2016104561 cites W1993529914 @default.
- W2016104561 cites W1996589507 @default.
- W2016104561 cites W2000035365 @default.
- W2016104561 cites W2000293625 @default.
- W2016104561 cites W2001537301 @default.
- W2016104561 cites W2005998982 @default.
- W2016104561 cites W2007696803 @default.
- W2016104561 cites W2014537558 @default.
- W2016104561 cites W2018016371 @default.
- W2016104561 cites W2019547313 @default.
- W2016104561 cites W2022587816 @default.
- W2016104561 cites W2022990633 @default.
- W2016104561 cites W2023486011 @default.
- W2016104561 cites W2029282884 @default.
- W2016104561 cites W2032865872 @default.
- W2016104561 cites W2033360140 @default.
- W2016104561 cites W2035437968 @default.
- W2016104561 cites W2039149922 @default.
- W2016104561 cites W2039466961 @default.
- W2016104561 cites W2041701617 @default.
- W2016104561 cites W2044682359 @default.
- W2016104561 cites W2050636118 @default.
- W2016104561 cites W2052313790 @default.
- W2016104561 cites W2052953466 @default.
- W2016104561 cites W2056261087 @default.
- W2016104561 cites W2057126532 @default.
- W2016104561 cites W2057546352 @default.
- W2016104561 cites W2059339504 @default.
- W2016104561 cites W2061970295 @default.
- W2016104561 cites W2063388460 @default.
- W2016104561 cites W2068358860 @default.
- W2016104561 cites W2069895379 @default.
- W2016104561 cites W2076219211 @default.
- W2016104561 cites W2076756860 @default.
- W2016104561 cites W2078618051 @default.
- W2016104561 cites W2084893412 @default.
- W2016104561 cites W2086691634 @default.
- W2016104561 cites W2090065358 @default.
- W2016104561 cites W2094610889 @default.
- W2016104561 cites W2094758219 @default.
- W2016104561 cites W2111449191 @default.
- W2016104561 cites W2115245256 @default.
- W2016104561 cites W2159424055 @default.
- W2016104561 cites W2165854031 @default.
- W2016104561 cites W2167383445 @default.
- W2016104561 doi "https://doi.org/10.1016/j.jallcom.2011.04.102" @default.
- W2016104561 hasPublicationYear "2011" @default.
- W2016104561 type Work @default.
- W2016104561 sameAs 2016104561 @default.
- W2016104561 citedByCount "35" @default.
- W2016104561 countsByYear W20161045612012 @default.
- W2016104561 countsByYear W20161045612013 @default.
- W2016104561 countsByYear W20161045612014 @default.
- W2016104561 countsByYear W20161045612015 @default.
- W2016104561 countsByYear W20161045612016 @default.
- W2016104561 countsByYear W20161045612017 @default.
- W2016104561 countsByYear W20161045612018 @default.
- W2016104561 countsByYear W20161045612021 @default.
- W2016104561 crossrefType "journal-article" @default.
- W2016104561 hasAuthorship W2016104561A5002204604 @default.
- W2016104561 hasAuthorship W2016104561A5007215384 @default.
- W2016104561 hasAuthorship W2016104561A5013542315 @default.
- W2016104561 hasAuthorship W2016104561A5056736167 @default.
- W2016104561 hasAuthorship W2016104561A5065337925 @default.
- W2016104561 hasConcept C113196181 @default.
- W2016104561 hasConcept C120665830 @default.
- W2016104561 hasConcept C121332964 @default.
- W2016104561 hasConcept C127413603 @default.
- W2016104561 hasConcept C132612359 @default.
- W2016104561 hasConcept C144082473 @default.
- W2016104561 hasConcept C147789679 @default.
- W2016104561 hasConcept C17525397 @default.
- W2016104561 hasConcept C178790620 @default.
- W2016104561 hasConcept C185592680 @default.
- W2016104561 hasConcept C191897082 @default.
- W2016104561 hasConcept C192562407 @default.
- W2016104561 hasConcept C207114421 @default.