• W2016144723 abstract "Effect of 3.4 wt.% C and 5 wt.% SiC doping into the standard in situ (IN) process and mechanically alloyed (MA) MgB2 was studied. Powders of IN and MA process were carried out in air and in argon filled glove box, respectively. Wire samples were prepared by two-axial rolling deformation of IN and MA powders inside the Ti tube. Titanium as sheath material allows to use higher sintering temperatures, we used 700 °C and 800 °C for 30 min in Argon. Critical current densities (Jc) were measured at variable temperatures 4.2 K, 10 K, 15 K and 20 K in the external magnetic fields ranging to 15 T. Critical temperatures, upper critical fields and irreversibility fields of IN and MA with SiC and C additions are compared and discussed. The highest transport properties were observed for wires with MA SiC doped MgB2 in the whole scale of temperatures 4.2–20 K. Upper critical field was rapidly enhanced in the case of carbon doped MA samples at 4.2 K. MA samples have shown decreased Jc values for higher temperatures (15 K, 20 K), in some case even worse than for the not doped reference IN sample. Carbon substitution and grain connectivity of analyzed samples are compared and discussed. Presented results show that for 20 K applications some new ways (additions) have to be found for increasing the Jc substantially." @default.
• W2016144723 created "2016-06-24" @default.
• W2016144723 creator A5014578943 @default.
• W2016144723 creator A5018798134 @default.
• W2016144723 creator A5022049791 @default.
• W2016144723 creator A5024984540 @default.
• W2016144723 creator A5030247217 @default.
• W2016144723 creator A5087845014 @default.
• W2016144723 creator A5088024180 @default.
• W2016144723 date "2009-07-01" @default.
• W2016144723 modified "2023-09-27" @default.
• W2016144723 title "Effect of C and SiC additions into in situ or mechanically alloyed MgB2 deformed in Ti sheath" @default.
• W2016144723 cites W1605431050 @default.
• W2016144723 cites W1969828745 @default.
• W2016144723 cites W1977415058 @default.
• W2016144723 cites W1979106878 @default.
• W2016144723 cites W1988473977 @default.
• W2016144723 cites W2010604741 @default.
• W2016144723 cites W2016277903 @default.
• W2016144723 cites W2021696303 @default.
• W2016144723 cites W2046354596 @default.
• W2016144723 cites W2051596504 @default.
• W2016144723 cites W2052241006 @default.
• W2016144723 cites W2057750780 @default.
• W2016144723 cites W2057928350 @default.
• W2016144723 cites W2059564082 @default.
• W2016144723 cites W2078710135 @default.
• W2016144723 cites W2083824208 @default.
• W2016144723 cites W2085209312 @default.
• W2016144723 cites W2085757252 @default.
• W2016144723 cites W2093306854 @default.
• W2016144723 cites W2093573610 @default.
• W2016144723 cites W2167231063 @default.
• W2016144723 doi "https://doi.org/10.1016/j.physc.2009.05.007" @default.
• W2016144723 hasPublicationYear "2009" @default.
• W2016144723 type Work @default.
• W2016144723 sameAs 2016144723 @default.
• W2016144723 citedByCount "16" @default.
• W2016144723 countsByYear W20161447232012 @default.
• W2016144723 countsByYear W20161447232014 @default.
• W2016144723 countsByYear W20161447232015 @default.
• W2016144723 countsByYear W20161447232016 @default.
• W2016144723 countsByYear W20161447232017 @default.
• W2016144723 countsByYear W20161447232021 @default.
• W2016144723 crossrefType "journal-article" @default.
• W2016144723 hasAuthorship W2016144723A5014578943 @default.
• W2016144723 hasAuthorship W2016144723A5018798134 @default.
• W2016144723 hasAuthorship W2016144723A5022049791 @default.
• W2016144723 hasAuthorship W2016144723A5024984540 @default.
• W2016144723 hasAuthorship W2016144723A5030247217 @default.
• W2016144723 hasAuthorship W2016144723A5087845014 @default.
• W2016144723 hasAuthorship W2016144723A5088024180 @default.
• W2016144723 hasConcept C104779481 @default.
• W2016144723 hasConcept C113196181 @default.
• W2016144723 hasConcept C121332964 @default.
• W2016144723 hasConcept C140205800 @default.
• W2016144723 hasConcept C159985019 @default.
• W2016144723 hasConcept C184779094 @default.
• W2016144723 hasConcept C185592680 @default.
• W2016144723 hasConcept C191897082 @default.
• W2016144723 hasConcept C192562407 @default.
• W2016144723 hasConcept C26873012 @default.
• W2016144723 hasConcept C2777581544 @default.
• W2016144723 hasConcept C2987373456 @default.
• W2016144723 hasConcept C43617362 @default.
• W2016144723 hasConcept C48496998 @default.
• W2016144723 hasConcept C49040817 @default.
• W2016144723 hasConcept C506065880 @default.
• W2016144723 hasConcept C54101563 @default.
• W2016144723 hasConcept C547737533 @default.
• W2016144723 hasConcept C57863236 @default.
• W2016144723 hasConceptScore W2016144723C104779481 @default.
• W2016144723 hasConceptScore W2016144723C113196181 @default.
• W2016144723 hasConceptScore W2016144723C121332964 @default.
• W2016144723 hasConceptScore W2016144723C140205800 @default.
• W2016144723 hasConceptScore W2016144723C159985019 @default.
• W2016144723 hasConceptScore W2016144723C184779094 @default.
• W2016144723 hasConceptScore W2016144723C185592680 @default.
• W2016144723 hasConceptScore W2016144723C191897082 @default.
• W2016144723 hasConceptScore W2016144723C192562407 @default.
• W2016144723 hasConceptScore W2016144723C26873012 @default.
• W2016144723 hasConceptScore W2016144723C2777581544 @default.
• W2016144723 hasConceptScore W2016144723C2987373456 @default.
• W2016144723 hasConceptScore W2016144723C43617362 @default.
• W2016144723 hasConceptScore W2016144723C48496998 @default.
• W2016144723 hasConceptScore W2016144723C49040817 @default.
• W2016144723 hasConceptScore W2016144723C506065880 @default.
• W2016144723 hasConceptScore W2016144723C54101563 @default.
• W2016144723 hasConceptScore W2016144723C547737533 @default.
• W2016144723 hasConceptScore W2016144723C57863236 @default.
• W2016144723 hasIssue "14" @default.
• W2016144723 hasLocation W20161447231 @default.
• W2016144723 hasOpenAccess W2016144723 @default.
• W2016144723 hasPrimaryLocation W20161447231 @default.
• W2016144723 hasRelatedWork W1613913436 @default.
• W2016144723 hasRelatedWork W1967284073 @default.
• W2016144723 hasRelatedWork W1989006700 @default.
• W2016144723 hasRelatedWork W1994172187 @default.

• next