- W2016698658 abstract "Fracture toughness tests were performed at 93, 205, 316, and 427°C using electropotential techniques on HT-9 weld material irradiated to a fluence of 2.35 × 1022 n/cm2 (E>0.1 MeV) at 390°C. Testing of welds irradiated at 450, 500, and 550°C was performed at 205°C. Test results were analyzed using the J-integral approach. It was found that the initiation fracture toughness of these HT-9 welds increased slightly, while the tearing modulus decreased significantly after irradiation to a fluence of 2.35 × 1022 n/cm2. In addition, results showed that irradiation temperature had little effect on the initiation fracture toughness of HT-9 weld metal. The specimens were examined by scanning electron microscopy after the test in order to understand the fracture process in this weld material." @default.
- W2016698658 created "2016-06-24" @default.
- W2016698658 creator A5024071911 @default.
- W2016698658 creator A5039827663 @default.
- W2016698658 date "1985-10-01" @default.
- W2016698658 modified "2023-09-23" @default.
- W2016698658 title "Fracture Toughness of Irradiated HT-9 Weld Metal" @default.
- W2016698658 doi "https://doi.org/10.1115/1.3225827" @default.
- W2016698658 hasPublicationYear "1985" @default.
- W2016698658 type Work @default.
- W2016698658 sameAs 2016698658 @default.
- W2016698658 citedByCount "3" @default.
- W2016698658 crossrefType "journal-article" @default.
- W2016698658 hasAuthorship W2016698658A5024071911 @default.
- W2016698658 hasAuthorship W2016698658A5039827663 @default.
- W2016698658 hasConcept C111337013 @default.
- W2016698658 hasConcept C121332964 @default.
- W2016698658 hasConcept C159985019 @default.
- W2016698658 hasConcept C185544564 @default.
- W2016698658 hasConcept C191897082 @default.
- W2016698658 hasConcept C192562407 @default.
- W2016698658 hasConcept C43369102 @default.
- W2016698658 hasConcept C544153396 @default.
- W2016698658 hasConcept C97549433 @default.
- W2016698658 hasConceptScore W2016698658C111337013 @default.
- W2016698658 hasConceptScore W2016698658C121332964 @default.
- W2016698658 hasConceptScore W2016698658C159985019 @default.
- W2016698658 hasConceptScore W2016698658C185544564 @default.
- W2016698658 hasConceptScore W2016698658C191897082 @default.
- W2016698658 hasConceptScore W2016698658C192562407 @default.
- W2016698658 hasConceptScore W2016698658C43369102 @default.
- W2016698658 hasConceptScore W2016698658C544153396 @default.
- W2016698658 hasConceptScore W2016698658C97549433 @default.
- W2016698658 hasLocation W20166986581 @default.
- W2016698658 hasOpenAccess W2016698658 @default.
- W2016698658 hasPrimaryLocation W20166986581 @default.
- W2016698658 hasRelatedWork W160643839 @default.
- W2016698658 hasRelatedWork W1706966180 @default.
- W2016698658 hasRelatedWork W1975466182 @default.
- W2016698658 hasRelatedWork W2005829071 @default.
- W2016698658 hasRelatedWork W2008188297 @default.
- W2016698658 hasRelatedWork W2028750761 @default.
- W2016698658 hasRelatedWork W2033319458 @default.
- W2016698658 hasRelatedWork W2075427355 @default.
- W2016698658 hasRelatedWork W210893765 @default.
- W2016698658 hasRelatedWork W2158047966 @default.
- W2016698658 hasRelatedWork W2159219675 @default.
- W2016698658 hasRelatedWork W2366288667 @default.
- W2016698658 hasRelatedWork W2480027366 @default.
- W2016698658 hasRelatedWork W2559575164 @default.
- W2016698658 hasRelatedWork W2571196338 @default.
- W2016698658 hasRelatedWork W3009750354 @default.
- W2016698658 hasRelatedWork W3096363185 @default.
- W2016698658 hasRelatedWork W3096545256 @default.
- W2016698658 hasRelatedWork W3096712828 @default.
- W2016698658 hasRelatedWork W3207318761 @default.
- W2016698658 isParatext "false" @default.
- W2016698658 isRetracted "false" @default.
- W2016698658 magId "2016698658" @default.
- W2016698658 workType "article" @default.