- W2017013268 abstract "Abstract Turbine blades made of Ni-base superalloy IN738 in stationary gas turbine had been removed during routine maintenance procedures after 10,000–20,000 h of operation. Crack growth in this material was studied by performing lab tests with specimens directly cut from the hot area of these blades with testing temperatures of 20 °C and 700 °C. The crack paths in these tests were analyzed and compared to those of service cracks. It was found that even though intergranular crack growth was dominant at elevated temperatures there was still a certain amount of transgranular crack propagation in all cases. Transgranular crack growth under operating conditions led to local recrystallization in the plastic zone ahead of the crack tip. The implications of the recrystallization process on the crack growth rate are discussed in the paper." @default.
- W2017013268 created "2016-06-24" @default.
- W2017013268 creator A5003623013 @default.
- W2017013268 creator A5075996735 @default.
- W2017013268 creator A5079578311 @default.
- W2017013268 date "2014-08-01" @default.
- W2017013268 modified "2023-09-26" @default.
- W2017013268 title "Crack growth mechanisms in an aged superalloy at high temperature" @default.
- W2017013268 cites W1996566820 @default.
- W2017013268 cites W1998721235 @default.
- W2017013268 cites W2010982133 @default.
- W2017013268 cites W2013333935 @default.
- W2017013268 cites W2013941145 @default.
- W2017013268 cites W2038607050 @default.
- W2017013268 cites W2056499764 @default.
- W2017013268 cites W2084950541 @default.
- W2017013268 cites W2108623911 @default.
- W2017013268 cites W2153334739 @default.
- W2017013268 cites W4246642522 @default.
- W2017013268 doi "https://doi.org/10.1016/j.ijfatigue.2013.05.014" @default.
- W2017013268 hasPublicationYear "2014" @default.
- W2017013268 type Work @default.
- W2017013268 sameAs 2017013268 @default.
- W2017013268 citedByCount "6" @default.
- W2017013268 countsByYear W20170132682016 @default.
- W2017013268 countsByYear W20170132682018 @default.
- W2017013268 countsByYear W20170132682020 @default.
- W2017013268 countsByYear W20170132682022 @default.
- W2017013268 crossrefType "journal-article" @default.
- W2017013268 hasAuthorship W2017013268A5003623013 @default.
- W2017013268 hasAuthorship W2017013268A5075996735 @default.
- W2017013268 hasAuthorship W2017013268A5079578311 @default.
- W2017013268 hasConcept C159985019 @default.
- W2017013268 hasConcept C191897082 @default.
- W2017013268 hasConcept C192562407 @default.
- W2017013268 hasConcept C207055975 @default.
- W2017013268 hasConcept C87976508 @default.
- W2017013268 hasConceptScore W2017013268C159985019 @default.
- W2017013268 hasConceptScore W2017013268C191897082 @default.
- W2017013268 hasConceptScore W2017013268C192562407 @default.
- W2017013268 hasConceptScore W2017013268C207055975 @default.
- W2017013268 hasConceptScore W2017013268C87976508 @default.
- W2017013268 hasLocation W20170132681 @default.
- W2017013268 hasOpenAccess W2017013268 @default.
- W2017013268 hasPrimaryLocation W20170132681 @default.
- W2017013268 hasRelatedWork W1984838914 @default.
- W2017013268 hasRelatedWork W2020660716 @default.
- W2017013268 hasRelatedWork W2031582942 @default.
- W2017013268 hasRelatedWork W2070704769 @default.
- W2017013268 hasRelatedWork W2077617097 @default.
- W2017013268 hasRelatedWork W2080679998 @default.
- W2017013268 hasRelatedWork W2589584934 @default.
- W2017013268 hasRelatedWork W2959042971 @default.
- W2017013268 hasRelatedWork W4230613107 @default.
- W2017013268 hasRelatedWork W4250486179 @default.
- W2017013268 hasVolume "65" @default.
- W2017013268 isParatext "false" @default.
- W2017013268 isRetracted "false" @default.
- W2017013268 magId "2017013268" @default.
- W2017013268 workType "article" @default.