- W2017013384 endingPage "6505" @default.
- W2017013384 startingPage "6497" @default.
- W2017013384 abstract "The response of poly(ethylene-co-1,9-decadiene) to peroxide treatment was examined and compared with a reference. The polymers were produced in a low-pressure process using a chromium-based catalyst giving a relatively high level of inherent unsaturations through thermal termination of the polymerisation. The copolymerisation with 1,9-decadiene gave an additional 63% vinyl end groups in the polymer. A great improvement in the response to dicumyl peroxide was observed for the decadiene polymers leading to a considerably smaller need for peroxide in order to obtain a certain gel content. The reason for the improved response was previously found to be the overall higher amount of vinyl groups as well as the placement of these groups along the molecular weight distribution. The remaining amount of vinyls after crosslinking was found to be exponentially dependent on the amount of peroxide added. At high peroxide levels almost all vinyl groups were consumed. The peroxide-induced consumption of vinyls was found to increase linearly with the original amount of vinyl unsaturations. At high peroxide levels, approximately the same gel content was obtained in all samples, leading to a considerably higher consumption of vinyls in the decadiene samples as compared to the reference. Mechanical measurements indicate a higher crosslinking density for the materials containing decadiene as compared to the reference. However, at lower gel contents, e.g. 40% and below, the situation is the opposite." @default.
- W2017013384 created "2016-06-24" @default.
- W2017013384 creator A5012519634 @default.
- W2017013384 creator A5077934487 @default.
- W2017013384 date "2000-08-01" @default.
- W2017013384 modified "2023-10-06" @default.
- W2017013384 title "Chemical and mechanical changes in poly(ethylene-co-1,9-decadiene) following crosslinking induced by peroxides" @default.
- W2017013384 cites W1978152681 @default.
- W2017013384 cites W1993761432 @default.
- W2017013384 cites W2017996387 @default.
- W2017013384 cites W2032177832 @default.
- W2017013384 cites W2055217055 @default.
- W2017013384 doi "https://doi.org/10.1016/s0032-3861(99)00881-2" @default.
- W2017013384 hasPublicationYear "2000" @default.
- W2017013384 type Work @default.
- W2017013384 sameAs 2017013384 @default.
- W2017013384 citedByCount "15" @default.
- W2017013384 countsByYear W20170133842013 @default.
- W2017013384 countsByYear W20170133842014 @default.
- W2017013384 countsByYear W20170133842017 @default.
- W2017013384 countsByYear W20170133842021 @default.
- W2017013384 countsByYear W20170133842022 @default.
- W2017013384 crossrefType "journal-article" @default.
- W2017013384 hasAuthorship W2017013384A5012519634 @default.
- W2017013384 hasAuthorship W2017013384A5077934487 @default.
- W2017013384 hasConcept C158117686 @default.
- W2017013384 hasConcept C15920480 @default.
- W2017013384 hasConcept C161790260 @default.
- W2017013384 hasConcept C178790620 @default.
- W2017013384 hasConcept C185592680 @default.
- W2017013384 hasConcept C188027245 @default.
- W2017013384 hasConcept C192562407 @default.
- W2017013384 hasConcept C2778215691 @default.
- W2017013384 hasConcept C2778597550 @default.
- W2017013384 hasConcept C2781048764 @default.
- W2017013384 hasConcept C44228677 @default.
- W2017013384 hasConcept C521977710 @default.
- W2017013384 hasConceptScore W2017013384C158117686 @default.
- W2017013384 hasConceptScore W2017013384C15920480 @default.
- W2017013384 hasConceptScore W2017013384C161790260 @default.
- W2017013384 hasConceptScore W2017013384C178790620 @default.
- W2017013384 hasConceptScore W2017013384C185592680 @default.
- W2017013384 hasConceptScore W2017013384C188027245 @default.
- W2017013384 hasConceptScore W2017013384C192562407 @default.
- W2017013384 hasConceptScore W2017013384C2778215691 @default.
- W2017013384 hasConceptScore W2017013384C2778597550 @default.
- W2017013384 hasConceptScore W2017013384C2781048764 @default.
- W2017013384 hasConceptScore W2017013384C44228677 @default.
- W2017013384 hasConceptScore W2017013384C521977710 @default.
- W2017013384 hasIssue "17" @default.
- W2017013384 hasLocation W20170133841 @default.
- W2017013384 hasOpenAccess W2017013384 @default.
- W2017013384 hasPrimaryLocation W20170133841 @default.
- W2017013384 hasRelatedWork W1504717592 @default.
- W2017013384 hasRelatedWork W1563398166 @default.
- W2017013384 hasRelatedWork W159244847 @default.
- W2017013384 hasRelatedWork W2087835513 @default.
- W2017013384 hasRelatedWork W2291378407 @default.
- W2017013384 hasRelatedWork W2320788267 @default.
- W2017013384 hasRelatedWork W2601355957 @default.
- W2017013384 hasRelatedWork W4211218226 @default.
- W2017013384 hasRelatedWork W4237014638 @default.
- W2017013384 hasRelatedWork W2040691182 @default.
- W2017013384 hasVolume "41" @default.
- W2017013384 isParatext "false" @default.
- W2017013384 isRetracted "false" @default.
- W2017013384 magId "2017013384" @default.
- W2017013384 workType "article" @default.