- W2017246552 abstract "Abstract We performed investigations to determine the lifetime of tungsten coatings on carbon under high heat flux with respect to tungsten carbide formation. Tungsten coatings with a molybdenum interlayer were deposited by combined magnetron sputtering and ion implantation. These coatings were heat treated in a vacuum furnace. Subsequently the fraction of the coating thickness which had converted into carbide, was determined by focussed ion beam preparation and electron microscopy. This thickness was found to extend from 10 μm to 18 μm for heat treatments between 2 and 20 h at 1350 °C. Such coatings were then exposed to high heat flux pulses of 16.5 MW/m 2 with pulse durations of 1.5 s. A clear threshold behaviour was found: While after 2 h of heat treatment no coating failure was found, the delaminated surface fraction was up to 5% after treatment for 5 h and up to 25% after treatment for 20 h at 1350 °C." @default.
- W2017246552 created "2016-06-24" @default.
- W2017246552 creator A5011704851 @default.
- W2017246552 creator A5017163345 @default.
- W2017246552 creator A5033321228 @default.
- W2017246552 creator A5037778113 @default.
- W2017246552 creator A5041883295 @default.
- W2017246552 creator A5047899155 @default.
- W2017246552 creator A5052126685 @default.
- W2017246552 creator A5055040713 @default.
- W2017246552 creator A5059007422 @default.
- W2017246552 creator A5077952832 @default.
- W2017246552 date "2011-08-01" @default.
- W2017246552 modified "2023-10-14" @default.
- W2017246552 title "Performance of W coatings on CFC with respect to carbide formation" @default.
- W2017246552 cites W189444653 @default.
- W2017246552 cites W1966707890 @default.
- W2017246552 cites W1967053825 @default.
- W2017246552 cites W1986520278 @default.
- W2017246552 cites W1995357301 @default.
- W2017246552 cites W1995933816 @default.
- W2017246552 cites W1998222915 @default.
- W2017246552 cites W2020919109 @default.
- W2017246552 cites W2038035218 @default.
- W2017246552 cites W2062942697 @default.
- W2017246552 cites W2064389003 @default.
- W2017246552 cites W2066763613 @default.
- W2017246552 cites W2070567150 @default.
- W2017246552 cites W2075334249 @default.
- W2017246552 cites W2076674540 @default.
- W2017246552 cites W2083549902 @default.
- W2017246552 cites W2090110049 @default.
- W2017246552 cites W2098045375 @default.
- W2017246552 cites W2133391167 @default.
- W2017246552 cites W2327844530 @default.
- W2017246552 cites W41992330 @default.
- W2017246552 cites W586329597 @default.
- W2017246552 doi "https://doi.org/10.1016/j.jnucmat.2010.08.049" @default.
- W2017246552 hasPublicationYear "2011" @default.
- W2017246552 type Work @default.
- W2017246552 sameAs 2017246552 @default.
- W2017246552 citedByCount "11" @default.
- W2017246552 countsByYear W20172465522012 @default.
- W2017246552 countsByYear W20172465522013 @default.
- W2017246552 countsByYear W20172465522014 @default.
- W2017246552 countsByYear W20172465522015 @default.
- W2017246552 countsByYear W20172465522016 @default.
- W2017246552 countsByYear W20172465522017 @default.
- W2017246552 countsByYear W20172465522019 @default.
- W2017246552 countsByYear W20172465522021 @default.
- W2017246552 crossrefType "journal-article" @default.
- W2017246552 hasAuthorship W2017246552A5011704851 @default.
- W2017246552 hasAuthorship W2017246552A5017163345 @default.
- W2017246552 hasAuthorship W2017246552A5033321228 @default.
- W2017246552 hasAuthorship W2017246552A5037778113 @default.
- W2017246552 hasAuthorship W2017246552A5041883295 @default.
- W2017246552 hasAuthorship W2017246552A5047899155 @default.
- W2017246552 hasAuthorship W2017246552A5052126685 @default.
- W2017246552 hasAuthorship W2017246552A5055040713 @default.
- W2017246552 hasAuthorship W2017246552A5059007422 @default.
- W2017246552 hasAuthorship W2017246552A5077952832 @default.
- W2017246552 hasConcept C191897082 @default.
- W2017246552 hasConcept C192562407 @default.
- W2017246552 hasConcept C5335593 @default.
- W2017246552 hasConceptScore W2017246552C191897082 @default.
- W2017246552 hasConceptScore W2017246552C192562407 @default.
- W2017246552 hasConceptScore W2017246552C5335593 @default.
- W2017246552 hasIssue "1" @default.
- W2017246552 hasLocation W20172465521 @default.
- W2017246552 hasOpenAccess W2017246552 @default.
- W2017246552 hasPrimaryLocation W20172465521 @default.
- W2017246552 hasRelatedWork W2003538315 @default.
- W2017246552 hasRelatedWork W2022507789 @default.
- W2017246552 hasRelatedWork W2070338356 @default.
- W2017246552 hasRelatedWork W2081303922 @default.
- W2017246552 hasRelatedWork W2138530703 @default.
- W2017246552 hasRelatedWork W2312389078 @default.
- W2017246552 hasRelatedWork W2322722469 @default.
- W2017246552 hasRelatedWork W3046190049 @default.
- W2017246552 hasRelatedWork W3094131129 @default.
- W2017246552 hasRelatedWork W4253328832 @default.
- W2017246552 hasVolume "415" @default.
- W2017246552 isParatext "false" @default.
- W2017246552 isRetracted "false" @default.
- W2017246552 magId "2017246552" @default.
- W2017246552 workType "article" @default.