- W2018653562 abstract "Abstract TiAl specimens measuring 15×10×2 in mm were implanted with Al, Si, Cr or Mo ions of a dose of 1021 or 1.2×1021 (for Cr only) ions m−2 at an acceleration voltage of 50 keV. Their oxidation resistance was assessed by cyclic oxidation tests with temperature varying between room temperature and 1200 K in a flow of purified oxygen under atmospheric pressure. The holding time at temperature was 72 ks (20 h) or 3.6 ks (1 h). Conventional metallographic examinations were performed for implanted specimens and oxidised specimens using glancing angle X-ray diffractometry (XRD), Auger electron spectroscopy (AES), scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). The implantation of Al or Si is effective to decrease the oxidation rate during the first near parabolic period of 130 ks, after which the implantation of Al results in breakaway oxidation, while the implantation of Si gives low oxidation rate for at least up to 800 ks. The implantation of Cr accelerates the oxidation during the initial period and then the partial scale spallation takes place leading to occasional mass losses. The implantation of Mo results in very slow oxidation rate for up to 1500 ks when the experiment was terminated. The same effect was obtained for the implantation of Mo under conditions of 40 keV and 2×1021 ions m−2. The excellent oxidation resistance obtained by the implantation of Si or Mo is attributable to the formation of virtually Al2O3 scales during the initial oxidation periods." @default.
- W2018653562 created "2016-06-24" @default.
- W2018653562 creator A5001984503 @default.
- W2018653562 creator A5007132515 @default.
- W2018653562 creator A5007302285 @default.
- W2018653562 creator A5011619481 @default.
- W2018653562 creator A5037695988 @default.
- W2018653562 date "1999-06-01" @default.
- W2018653562 modified "2023-09-28" @default.
- W2018653562 title "Influence of implantation of Al, Si, Cr or Mo ions on the oxidation behaviour of TiAl under thermal cycle conditions" @default.
- W2018653562 cites W1966743082 @default.
- W2018653562 cites W1977664673 @default.
- W2018653562 cites W2066252231 @default.
- W2018653562 cites W2071611659 @default.
- W2018653562 cites W2082141435 @default.
- W2018653562 cites W2089566254 @default.
- W2018653562 cites W2090278984 @default.
- W2018653562 cites W2092954538 @default.
- W2018653562 cites W4235119262 @default.
- W2018653562 cites W4238207666 @default.
- W2018653562 doi "https://doi.org/10.1016/s0921-5093(99)00042-8" @default.
- W2018653562 hasPublicationYear "1999" @default.
- W2018653562 type Work @default.
- W2018653562 sameAs 2018653562 @default.
- W2018653562 citedByCount "55" @default.
- W2018653562 countsByYear W20186535622012 @default.
- W2018653562 countsByYear W20186535622013 @default.
- W2018653562 countsByYear W20186535622014 @default.
- W2018653562 countsByYear W20186535622016 @default.
- W2018653562 countsByYear W20186535622017 @default.
- W2018653562 countsByYear W20186535622018 @default.
- W2018653562 countsByYear W20186535622019 @default.
- W2018653562 countsByYear W20186535622020 @default.
- W2018653562 countsByYear W20186535622021 @default.
- W2018653562 countsByYear W20186535622022 @default.
- W2018653562 crossrefType "journal-article" @default.
- W2018653562 hasAuthorship W2018653562A5001984503 @default.
- W2018653562 hasAuthorship W2018653562A5007132515 @default.
- W2018653562 hasAuthorship W2018653562A5007302285 @default.
- W2018653562 hasAuthorship W2018653562A5011619481 @default.
- W2018653562 hasAuthorship W2018653562A5037695988 @default.
- W2018653562 hasConcept C121332964 @default.
- W2018653562 hasConcept C145148216 @default.
- W2018653562 hasConcept C178790620 @default.
- W2018653562 hasConcept C185592680 @default.
- W2018653562 hasConcept C191897082 @default.
- W2018653562 hasConcept C192562407 @default.
- W2018653562 hasConcept C204530211 @default.
- W2018653562 hasConcept C41823505 @default.
- W2018653562 hasConcept C97355855 @default.
- W2018653562 hasConceptScore W2018653562C121332964 @default.
- W2018653562 hasConceptScore W2018653562C145148216 @default.
- W2018653562 hasConceptScore W2018653562C178790620 @default.
- W2018653562 hasConceptScore W2018653562C185592680 @default.
- W2018653562 hasConceptScore W2018653562C191897082 @default.
- W2018653562 hasConceptScore W2018653562C192562407 @default.
- W2018653562 hasConceptScore W2018653562C204530211 @default.
- W2018653562 hasConceptScore W2018653562C41823505 @default.
- W2018653562 hasConceptScore W2018653562C97355855 @default.
- W2018653562 hasIssue "1-2" @default.
- W2018653562 hasLocation W20186535621 @default.
- W2018653562 hasOpenAccess W2018653562 @default.
- W2018653562 hasPrimaryLocation W20186535621 @default.
- W2018653562 hasRelatedWork W2003538315 @default.
- W2018653562 hasRelatedWork W2022507789 @default.
- W2018653562 hasRelatedWork W2070338356 @default.
- W2018653562 hasRelatedWork W2312389078 @default.
- W2018653562 hasRelatedWork W2322722469 @default.
- W2018653562 hasRelatedWork W2937808965 @default.
- W2018653562 hasRelatedWork W3046190049 @default.
- W2018653562 hasRelatedWork W3094131129 @default.
- W2018653562 hasRelatedWork W4231413117 @default.
- W2018653562 hasRelatedWork W4253328832 @default.
- W2018653562 hasVolume "266" @default.
- W2018653562 isParatext "false" @default.
- W2018653562 isRetracted "false" @default.
- W2018653562 magId "2018653562" @default.
- W2018653562 workType "article" @default.