- W2018766835 abstract "The surface oxidation of DSS 2205 duplex stainless steel was studied by X-ray photoelectron spectroscopy (XPS), for two different techniques witch were used to produce thin oxide layers on polished for measuring the concentration of oxide depends on the sputtering profile these duplex stainless steel samples. The experiments were performed in the temperature of 300°C with aging at 7000 hours e with growth of films obtained voltammetric curves (potentiostatically) of the samples in sulfuric acid (H2SO4-0.1M saturated) at low potential. The compositions of the modified oxidized surfaces were determined from the XPS survey scans, and the chemistry of selected elements from the higher-energy-resolution scans of the appropriate peaks. Various Iron/Chromium oxidized layers and various oxide thicknesses were observed and correlated with the temperature. It was found that all the techniques produced oxide layers with various traces of metallic components and with the maximum concentration of chromium oxide and iron oxide in layers close to the oxide layer/metal interface. Therefore this study showed results about the behavior of the DSS 2205 with higher and lower Cr content and that the annealing at 300°C for longer times (7000h) promotes the enrichment of iron oxide, and consequently the decrease in the chromium oxide content, in the oxide surface of both the DSS 2205." @default.
- W2018766835 created "2016-06-24" @default.
- W2018766835 creator A5004985489 @default.
- W2018766835 creator A5044189743 @default.
- W2018766835 date "2014-10-01" @default.
- W2018766835 modified "2023-09-27" @default.
- W2018766835 title "Study of the Variation of Chromium Oxide and Iron in Oxide Layer by XPS in DSS 2205 with Higher and Lower Chromium Content Due to Ageing for 7000 Hours at 300°C" @default.
- W2018766835 cites W1906472459 @default.
- W2018766835 cites W1964548659 @default.
- W2018766835 cites W1979689903 @default.
- W2018766835 cites W2000422813 @default.
- W2018766835 cites W2014882285 @default.
- W2018766835 cites W2104221022 @default.
- W2018766835 cites W2151701394 @default.
- W2018766835 doi "https://doi.org/10.5923/j.materials.20140405.01" @default.
- W2018766835 hasPublicationYear "2014" @default.
- W2018766835 type Work @default.
- W2018766835 sameAs 2018766835 @default.
- W2018766835 citedByCount "1" @default.
- W2018766835 countsByYear W20187668352022 @default.
- W2018766835 crossrefType "journal-article" @default.
- W2018766835 hasAuthorship W2018766835A5004985489 @default.
- W2018766835 hasAuthorship W2018766835A5044189743 @default.
- W2018766835 hasBestOaLocation W20187668351 @default.
- W2018766835 hasConcept C127413603 @default.
- W2018766835 hasConcept C159985019 @default.
- W2018766835 hasConcept C175708663 @default.
- W2018766835 hasConcept C191897082 @default.
- W2018766835 hasConcept C192562407 @default.
- W2018766835 hasConcept C2779227376 @default.
- W2018766835 hasConcept C2779851234 @default.
- W2018766835 hasConcept C2991932455 @default.
- W2018766835 hasConcept C42360764 @default.
- W2018766835 hasConcept C500499127 @default.
- W2018766835 hasConcept C511782168 @default.
- W2018766835 hasConcept C54355233 @default.
- W2018766835 hasConcept C86803240 @default.
- W2018766835 hasConceptScore W2018766835C127413603 @default.
- W2018766835 hasConceptScore W2018766835C159985019 @default.
- W2018766835 hasConceptScore W2018766835C175708663 @default.
- W2018766835 hasConceptScore W2018766835C191897082 @default.
- W2018766835 hasConceptScore W2018766835C192562407 @default.
- W2018766835 hasConceptScore W2018766835C2779227376 @default.
- W2018766835 hasConceptScore W2018766835C2779851234 @default.
- W2018766835 hasConceptScore W2018766835C2991932455 @default.
- W2018766835 hasConceptScore W2018766835C42360764 @default.
- W2018766835 hasConceptScore W2018766835C500499127 @default.
- W2018766835 hasConceptScore W2018766835C511782168 @default.
- W2018766835 hasConceptScore W2018766835C54355233 @default.
- W2018766835 hasConceptScore W2018766835C86803240 @default.
- W2018766835 hasIssue "5" @default.
- W2018766835 hasLocation W20187668351 @default.
- W2018766835 hasOpenAccess W2018766835 @default.
- W2018766835 hasPrimaryLocation W20187668351 @default.
- W2018766835 hasRelatedWork W1983742654 @default.
- W2018766835 hasRelatedWork W2006602464 @default.
- W2018766835 hasRelatedWork W2010741321 @default.
- W2018766835 hasRelatedWork W2017864224 @default.
- W2018766835 hasRelatedWork W2018766835 @default.
- W2018766835 hasRelatedWork W2035763389 @default.
- W2018766835 hasRelatedWork W2038064646 @default.
- W2018766835 hasRelatedWork W2088524340 @default.
- W2018766835 hasRelatedWork W2323937902 @default.
- W2018766835 hasRelatedWork W2620331613 @default.
- W2018766835 hasVolume "4" @default.
- W2018766835 isParatext "false" @default.
- W2018766835 isRetracted "false" @default.
- W2018766835 magId "2018766835" @default.
- W2018766835 workType "article" @default.