- W2020165897 abstract "Ni films were deposited on anodic aluminum oxide (AAO) and SiO2/Si(100) substrates at 300 K by direct current magnetron sputtering with the oblique target. The film thickness was 80 nm, 160 nm and 260 nm. The films grown on AAO substrates have a network structure while those deposited on SiO2/Si(100) substrates are continuous. The network film consists of granules and is formed by granule connection. The granule consists of many fine grains. The granule size increases with increasing film thickness. The 80 nm-thick network film has a honeycomb-like structure. The continuous films grow with a columnar structure and the transverse size of columnar grains increases with increasing film thickness. All the network films show a Ni(111) diffraction peak while the 160 nm- and 260 nm-thick continuous films exhibit the Ni(111) and Ni(200) diffraction peaks. The network films have higher coercivity and residual magnetization ratio compared with the continuous films. The coercivity and the residual magnetization ratio increase with increasing film thickness for the network films while they are almost independent of the film thickness for the continuous films. A temperature dependence of the resistance within 5–200 K reveals that the 80 nm-thick network Ni film exhibits markedly a minimal resistance at about 40 K. A logarithmic temperature dependence of the conductance is verified at temperatures below 40 K. The temperature coefficient of resistance is smallest for the 80 nm-thick network film and is largest for the 260 nm-thick continuous film." @default.
- W2020165897 created "2016-06-24" @default.
- W2020165897 creator A5004202702 @default.
- W2020165897 creator A5051248516 @default.
- W2020165897 creator A5085426795 @default.
- W2020165897 creator A5085598914 @default.
- W2020165897 creator A5091249837 @default.
- W2020165897 date "2012-07-01" @default.
- W2020165897 modified "2023-10-08" @default.
- W2020165897 title "Comparative study on the characteristics of network and continuous Ni films" @default.
- W2020165897 cites W1969483911 @default.
- W2020165897 cites W1976555209 @default.
- W2020165897 cites W1979206081 @default.
- W2020165897 cites W1982878399 @default.
- W2020165897 cites W1987620189 @default.
- W2020165897 cites W1990242711 @default.
- W2020165897 cites W1993915743 @default.
- W2020165897 cites W1998823728 @default.
- W2020165897 cites W2000641017 @default.
- W2020165897 cites W2001984154 @default.
- W2020165897 cites W2007985745 @default.
- W2020165897 cites W2014251327 @default.
- W2020165897 cites W2015079311 @default.
- W2020165897 cites W2016148532 @default.
- W2020165897 cites W2025413814 @default.
- W2020165897 cites W2030046525 @default.
- W2020165897 cites W2031049225 @default.
- W2020165897 cites W2042647320 @default.
- W2020165897 cites W2043388388 @default.
- W2020165897 cites W2051119943 @default.
- W2020165897 cites W2068867003 @default.
- W2020165897 cites W2076513456 @default.
- W2020165897 cites W2079297208 @default.
- W2020165897 cites W2087747186 @default.
- W2020165897 doi "https://doi.org/10.1016/j.tsf.2012.04.085" @default.
- W2020165897 hasPublicationYear "2012" @default.
- W2020165897 type Work @default.
- W2020165897 sameAs 2020165897 @default.
- W2020165897 citedByCount "8" @default.
- W2020165897 countsByYear W20201658972013 @default.
- W2020165897 countsByYear W20201658972014 @default.
- W2020165897 countsByYear W20201658972015 @default.
- W2020165897 countsByYear W20201658972016 @default.
- W2020165897 countsByYear W20201658972019 @default.
- W2020165897 crossrefType "journal-article" @default.
- W2020165897 hasAuthorship W2020165897A5004202702 @default.
- W2020165897 hasAuthorship W2020165897A5051248516 @default.
- W2020165897 hasAuthorship W2020165897A5085426795 @default.
- W2020165897 hasAuthorship W2020165897A5085598914 @default.
- W2020165897 hasAuthorship W2020165897A5091249837 @default.
- W2020165897 hasConcept C121332964 @default.
- W2020165897 hasConcept C126530901 @default.
- W2020165897 hasConcept C159985019 @default.
- W2020165897 hasConcept C171250308 @default.
- W2020165897 hasConcept C19067145 @default.
- W2020165897 hasConcept C192562407 @default.
- W2020165897 hasConcept C26873012 @default.
- W2020165897 hasConceptScore W2020165897C121332964 @default.
- W2020165897 hasConceptScore W2020165897C126530901 @default.
- W2020165897 hasConceptScore W2020165897C159985019 @default.
- W2020165897 hasConceptScore W2020165897C171250308 @default.
- W2020165897 hasConceptScore W2020165897C19067145 @default.
- W2020165897 hasConceptScore W2020165897C192562407 @default.
- W2020165897 hasConceptScore W2020165897C26873012 @default.
- W2020165897 hasIssue "18" @default.
- W2020165897 hasLocation W20201658971 @default.
- W2020165897 hasOpenAccess W2020165897 @default.
- W2020165897 hasPrimaryLocation W20201658971 @default.
- W2020165897 hasRelatedWork W1996409043 @default.
- W2020165897 hasRelatedWork W2005415654 @default.
- W2020165897 hasRelatedWork W2082293200 @default.
- W2020165897 hasRelatedWork W2090673143 @default.
- W2020165897 hasRelatedWork W2126584361 @default.
- W2020165897 hasRelatedWork W2137307547 @default.
- W2020165897 hasRelatedWork W2156998367 @default.
- W2020165897 hasRelatedWork W2380293314 @default.
- W2020165897 hasRelatedWork W2943188944 @default.
- W2020165897 hasRelatedWork W4285802202 @default.
- W2020165897 hasVolume "520" @default.
- W2020165897 isParatext "false" @default.
- W2020165897 isRetracted "false" @default.
- W2020165897 magId "2020165897" @default.
- W2020165897 workType "article" @default.