• W2020408087 abstract "Mechanical alloying was carried out to produce CrSi2 thermoelectric compound using a mixture of elemental Cr33Si67 powders. An optimal milling and heat treatment conditions to obtain the single phase of CrSi2 compound with fine microstructure were investigated by X-ray diffraction and differential scanning calorimetry measurement. CrSi2 intermetallic compound with a grain size of 70 nm could be obtained by MA of Cr33Si67 powders for 70 hours and subsequently annealed at 650 o C. Consolidation of the MA powders was performed in a spark plasma sintering (SPS) machine using graphite dies at 600~1000 o C under 60 MPa. The shrinkage of MA samples during SPS consolidation process increased gradually with increasing temperature up to 1000 o C and relatively significant at about 600 o C. We tend to believe that these behaviors are deeply related to form a CrSi2 compound during heating process, as can be realized from the DSC measurement. Electrical conductivity and Seebeck coefficient of sintered bodies were measured up to 900 o C. Seebeck coefficient and power factor of Cr33Si67 compact prepared by MA and SPS at 1000 o C showed the maximum value of 125 µV/K at 400 o C and 4.3 × 10 −4 W/mK 2 at 350 o C, respectively." @default.
• W2020408087 created "2016-06-24" @default.
• W2020408087 creator A5000681694 @default.
• W2020408087 creator A5013542315 @default.
• W2020408087 date "2013-06-30" @default.
• W2020408087 modified "2023-09-24" @default.
• W2020408087 title "Characterization and consolidation of thermoelectric CrSi2compound prepared by mechanical alloying" @default.
• W2020408087 cites W1485283179 @default.
• W2020408087 cites W151886240 @default.
• W2020408087 cites W1585512665 @default.
• W2020408087 cites W1965232023 @default.
• W2020408087 cites W1992949812 @default.
• W2020408087 cites W1995154963 @default.
• W2020408087 cites W1995710183 @default.
• W2020408087 cites W2008075239 @default.
• W2020408087 cites W2011438292 @default.
• W2020408087 cites W2045315503 @default.
• W2020408087 cites W2058592679 @default.
• W2020408087 cites W2060296502 @default.
• W2020408087 cites W2060622147 @default.
• W2020408087 cites W2071392224 @default.
• W2020408087 cites W2171809198 @default.
• W2020408087 cites W2606149633 @default.
• W2020408087 doi "https://doi.org/10.6111/jkcgct.2013.23.3.135" @default.
• W2020408087 hasPublicationYear "2013" @default.
• W2020408087 type Work @default.
• W2020408087 sameAs 2020408087 @default.
• W2020408087 citedByCount "0" @default.
• W2020408087 crossrefType "journal-article" @default.
• W2020408087 hasAuthorship W2020408087A5000681694 @default.
• W2020408087 hasAuthorship W2020408087A5013542315 @default.
• W2020408087 hasBestOaLocation W20204080871 @default.
• W2020408087 hasConcept C112625512 @default.
• W2020408087 hasConcept C113196181 @default.
• W2020408087 hasConcept C119599485 @default.
• W2020408087 hasConcept C121332964 @default.
• W2020408087 hasConcept C127413603 @default.
• W2020408087 hasConcept C159985019 @default.
• W2020408087 hasConcept C185592680 @default.
• W2020408087 hasConcept C191897082 @default.
• W2020408087 hasConcept C192562407 @default.
• W2020408087 hasConcept C207365445 @default.
• W2020408087 hasConcept C27501479 @default.
• W2020408087 hasConcept C2776014600 @default.
• W2020408087 hasConcept C2777581544 @default.
• W2020408087 hasConcept C2779698641 @default.
• W2020408087 hasConcept C2780026712 @default.
• W2020408087 hasConcept C39519442 @default.
• W2020408087 hasConcept C43617362 @default.
• W2020408087 hasConcept C63024428 @default.
• W2020408087 hasConcept C69990965 @default.
• W2020408087 hasConcept C87976508 @default.
• W2020408087 hasConcept C97346530 @default.
• W2020408087 hasConcept C97355855 @default.
• W2020408087 hasConceptScore W2020408087C112625512 @default.
• W2020408087 hasConceptScore W2020408087C113196181 @default.
• W2020408087 hasConceptScore W2020408087C119599485 @default.
• W2020408087 hasConceptScore W2020408087C121332964 @default.
• W2020408087 hasConceptScore W2020408087C127413603 @default.
• W2020408087 hasConceptScore W2020408087C159985019 @default.
• W2020408087 hasConceptScore W2020408087C185592680 @default.
• W2020408087 hasConceptScore W2020408087C191897082 @default.
• W2020408087 hasConceptScore W2020408087C192562407 @default.
• W2020408087 hasConceptScore W2020408087C207365445 @default.
• W2020408087 hasConceptScore W2020408087C27501479 @default.
• W2020408087 hasConceptScore W2020408087C2776014600 @default.
• W2020408087 hasConceptScore W2020408087C2777581544 @default.
• W2020408087 hasConceptScore W2020408087C2779698641 @default.
• W2020408087 hasConceptScore W2020408087C2780026712 @default.
• W2020408087 hasConceptScore W2020408087C39519442 @default.
• W2020408087 hasConceptScore W2020408087C43617362 @default.
• W2020408087 hasConceptScore W2020408087C63024428 @default.
• W2020408087 hasConceptScore W2020408087C69990965 @default.
• W2020408087 hasConceptScore W2020408087C87976508 @default.
• W2020408087 hasConceptScore W2020408087C97346530 @default.
• W2020408087 hasConceptScore W2020408087C97355855 @default.
• W2020408087 hasLocation W20204080871 @default.
• W2020408087 hasOpenAccess W2020408087 @default.
• W2020408087 hasPrimaryLocation W20204080871 @default.
• W2020408087 hasRelatedWork W1986591367 @default.
• W2020408087 hasRelatedWork W1998389765 @default.
• W2020408087 hasRelatedWork W2018464676 @default.
• W2020408087 hasRelatedWork W2025381851 @default.
• W2020408087 hasRelatedWork W2043376813 @default.
• W2020408087 hasRelatedWork W2054398789 @default.
• W2020408087 hasRelatedWork W2064747089 @default.
• W2020408087 hasRelatedWork W2079403093 @default.
• W2020408087 hasRelatedWork W2089456423 @default.
• W2020408087 hasRelatedWork W2089655020 @default.
• W2020408087 hasRelatedWork W2154370633 @default.
• W2020408087 hasRelatedWork W2351080399 @default.
• W2020408087 hasRelatedWork W2355544132 @default.
• W2020408087 hasRelatedWork W2376881436 @default.
• W2020408087 hasRelatedWork W2386618379 @default.
• W2020408087 hasRelatedWork W2395122325 @default.
• W2020408087 hasRelatedWork W2965099370 @default.
• W2020408087 hasRelatedWork W2979100778 @default.
• W2020408087 hasRelatedWork W3119865542 @default.
• W2020408087 hasRelatedWork W3120659163 @default.
• W2020408087 isParatext "false" @default.

• next