- W2022683558 abstract "Abstract New transparent conductive films that had a sandwich structure composed of ITO/Cu/ITO multilayer films were prepared by a conventional RF and DC magnetron sputtering process on a polycarbonate substrate without intentional substrate heating. The thickness of each layer in the ITO/Cu/ITO films was kept constant at 50 nm/5 nm/45 nm. The optoelectrical and structural properties of the films were compared with conventional ITO single-layer films and ITO/Cu/ITO multilayered films. Although both films had identical thickness, 100 nm, the ITO/Cu/ITO films showed a lower resistivity, 3.5 × 10 −4 Ω cm. In optical transmittance measurements, however, the ITO single-layer films showed a higher transmittance of 74% in the wavelength range of 300–800 nm. XRD spectra showed that both the ITO and ITO/Cu/ITO films were amorphous. The figure of merit, φ TC , reached a maximum of 5.2 × 10 −4 Ω −1 for the ITO/Cu/ITO films, which was higher than the φ TC of the ITO films (1.6 × 10 −4 Ω −1 ). The φ TC results suggested that ITO/Cu/ITO films had better optoelectrical properties than conventional ITO single-layer films." @default.
- W2022683558 created "2016-06-24" @default.
- W2022683558 creator A5024917162 @default.
- W2022683558 creator A5031924143 @default.
- W2022683558 creator A5057122889 @default.
- W2022683558 creator A5059092534 @default.
- W2022683558 creator A5064549873 @default.
- W2022683558 creator A5089582868 @default.
- W2022683558 date "2008-09-01" @default.
- W2022683558 modified "2023-09-24" @default.
- W2022683558 title "Fabrication of transparent conductive films with a sandwich structure composed of ITO/Cu/ITO" @default.
- W2022683558 cites W1965073035 @default.
- W2022683558 cites W1970834286 @default.
- W2022683558 cites W1975872348 @default.
- W2022683558 cites W1992142373 @default.
- W2022683558 cites W2000575887 @default.
- W2022683558 cites W2008304625 @default.
- W2022683558 cites W2016802554 @default.
- W2022683558 cites W2032561628 @default.
- W2022683558 cites W2033685500 @default.
- W2022683558 cites W2075157799 @default.
- W2022683558 cites W2075330480 @default.
- W2022683558 cites W2098748802 @default.
- W2022683558 doi "https://doi.org/10.1016/j.vacuum.2008.04.061" @default.
- W2022683558 hasPublicationYear "2008" @default.
- W2022683558 type Work @default.
- W2022683558 sameAs 2022683558 @default.
- W2022683558 citedByCount "23" @default.
- W2022683558 countsByYear W20226835582012 @default.
- W2022683558 countsByYear W20226835582013 @default.
- W2022683558 countsByYear W20226835582014 @default.
- W2022683558 countsByYear W20226835582016 @default.
- W2022683558 countsByYear W20226835582017 @default.
- W2022683558 countsByYear W20226835582020 @default.
- W2022683558 countsByYear W20226835582021 @default.
- W2022683558 countsByYear W20226835582022 @default.
- W2022683558 crossrefType "journal-article" @default.
- W2022683558 hasAuthorship W2022683558A5024917162 @default.
- W2022683558 hasAuthorship W2022683558A5031924143 @default.
- W2022683558 hasAuthorship W2022683558A5057122889 @default.
- W2022683558 hasAuthorship W2022683558A5059092534 @default.
- W2022683558 hasAuthorship W2022683558A5064549873 @default.
- W2022683558 hasAuthorship W2022683558A5089582868 @default.
- W2022683558 hasConcept C136525101 @default.
- W2022683558 hasConcept C142724271 @default.
- W2022683558 hasConcept C159985019 @default.
- W2022683558 hasConcept C171250308 @default.
- W2022683558 hasConcept C17470697 @default.
- W2022683558 hasConcept C192562407 @default.
- W2022683558 hasConcept C202374169 @default.
- W2022683558 hasConcept C204787440 @default.
- W2022683558 hasConcept C49040817 @default.
- W2022683558 hasConcept C71924100 @default.
- W2022683558 hasConceptScore W2022683558C136525101 @default.
- W2022683558 hasConceptScore W2022683558C142724271 @default.
- W2022683558 hasConceptScore W2022683558C159985019 @default.
- W2022683558 hasConceptScore W2022683558C171250308 @default.
- W2022683558 hasConceptScore W2022683558C17470697 @default.
- W2022683558 hasConceptScore W2022683558C192562407 @default.
- W2022683558 hasConceptScore W2022683558C202374169 @default.
- W2022683558 hasConceptScore W2022683558C204787440 @default.
- W2022683558 hasConceptScore W2022683558C49040817 @default.
- W2022683558 hasConceptScore W2022683558C71924100 @default.
- W2022683558 hasIssue "2" @default.
- W2022683558 hasLocation W20226835581 @default.
- W2022683558 hasOpenAccess W2022683558 @default.
- W2022683558 hasPrimaryLocation W20226835581 @default.
- W2022683558 hasRelatedWork W1503050415 @default.
- W2022683558 hasRelatedWork W1966617170 @default.
- W2022683558 hasRelatedWork W2045918486 @default.
- W2022683558 hasRelatedWork W2266365827 @default.
- W2022683558 hasRelatedWork W2290945384 @default.
- W2022683558 hasRelatedWork W2566969933 @default.
- W2022683558 hasRelatedWork W2614766546 @default.
- W2022683558 hasRelatedWork W2997324931 @default.
- W2022683558 hasRelatedWork W3000789669 @default.
- W2022683558 hasRelatedWork W3189842726 @default.
- W2022683558 hasVolume "83" @default.
- W2022683558 isParatext "false" @default.
- W2022683558 isRetracted "false" @default.
- W2022683558 magId "2022683558" @default.
- W2022683558 workType "article" @default.