- W2022810503 abstract "The paper contains strength tests results of joints soldered using lead and leadless soft solders. For tests lead solders types Pb60Sn40 and Sn60Pb40 and leadless soft solders types Sn95.5Ag3.8Cu0.7 and Sn96Ag4 were used. As basic materials steel sheet, zinc-coated steel sheet, copper sheet and brass sheet 100 x 20 x 1 mm was the test samples size. Always two sheets were cleaned and jointed together. For heating the propane-butane + air flame was used. Then the tested assemblies were loaded using the universal tensile-strength testing machine till to failure. At the tests the force needed for assemblies failure and failure type (in soldered joint, in basic material) were recorded. From measured data the solder strength was calculated. From the experiment results it follows that from the point of view of the soldered joints strength as well of the solder strength relatively small differences were found. At the same time it is evident that the joint strength and solder strength depend on soldered material type and on soldered joint lapping length. On the basis of carried out experiments it can be stated that the substitution of lead solders by leadless solders is possible without risk of soldered joints strength decrease." @default.
- W2022810503 created "2016-06-24" @default.
- W2022810503 creator A5006639248 @default.
- W2022810503 date "2013-11-24" @default.
- W2022810503 modified "2023-09-27" @default.
- W2022810503 title "Soldering sheets using soft solders" @default.
- W2022810503 cites W1975068766 @default.
- W2022810503 cites W1989686992 @default.
- W2022810503 cites W1989737343 @default.
- W2022810503 cites W1993806214 @default.
- W2022810503 cites W2052468482 @default.
- W2022810503 cites W2064314848 @default.
- W2022810503 cites W2065260025 @default.
- W2022810503 cites W212447503 @default.
- W2022810503 cites W3033324657 @default.
- W2022810503 doi "https://doi.org/10.11118/actaun201361061597" @default.
- W2022810503 hasPublicationYear "2013" @default.
- W2022810503 type Work @default.
- W2022810503 sameAs 2022810503 @default.
- W2022810503 citedByCount "12" @default.
- W2022810503 countsByYear W20228105032013 @default.
- W2022810503 countsByYear W20228105032014 @default.
- W2022810503 countsByYear W20228105032015 @default.
- W2022810503 countsByYear W20228105032016 @default.
- W2022810503 countsByYear W20228105032017 @default.
- W2022810503 countsByYear W20228105032018 @default.
- W2022810503 crossrefType "journal-article" @default.
- W2022810503 hasAuthorship W2022810503A5006639248 @default.
- W2022810503 hasBestOaLocation W20228105031 @default.
- W2022810503 hasConcept C191897082 @default.
- W2022810503 hasConcept C192562407 @default.
- W2022810503 hasConcept C50296614 @default.
- W2022810503 hasConceptScore W2022810503C191897082 @default.
- W2022810503 hasConceptScore W2022810503C192562407 @default.
- W2022810503 hasConceptScore W2022810503C50296614 @default.
- W2022810503 hasIssue "6" @default.
- W2022810503 hasLocation W20228105031 @default.
- W2022810503 hasOpenAccess W2022810503 @default.
- W2022810503 hasPrimaryLocation W20228105031 @default.
- W2022810503 hasRelatedWork W2022507789 @default.
- W2022810503 hasRelatedWork W2072503384 @default.
- W2022810503 hasRelatedWork W2128047618 @default.
- W2022810503 hasRelatedWork W3149753647 @default.
- W2022810503 hasRelatedWork W4252751901 @default.
- W2022810503 hasRelatedWork W4281746734 @default.
- W2022810503 hasRelatedWork W4310063626 @default.
- W2022810503 hasRelatedWork W4322766080 @default.
- W2022810503 hasRelatedWork W4381325326 @default.
- W2022810503 hasRelatedWork W4386002993 @default.
- W2022810503 hasVolume "61" @default.
- W2022810503 isParatext "false" @default.
- W2022810503 isRetracted "false" @default.
- W2022810503 magId "2022810503" @default.
- W2022810503 workType "article" @default.