- W2023382679 abstract "Experimental glass ionomer cement was prepared for the purpose of this study. Twenty disk specimens (16mm diameter x 10mm height) of test-GIC were prepared for the diametral tensile strength (DTS) test and twenty cylindrical specimens (6 mm diameter x 16mm height) were prepared for the compressive strength (CS) test. Specimens were stored in an artificial saliva at 37º C and (50±10%) of relative humidity in an incubator until testing. Five specimens of each GIC were submitted to CS and DTS test in each period, namely 1 hour, 24 hours, 7 days and 28 days. The specimens were tested in a Universal Testing Machine (Instron 1122, Instron corp., High Wycombe, U.K.) at a crosshead speed of 1.0mm/min for CS and 0.5mm/min for the DTS test until failure occurred. The results have revealed that incorporation of lithium fluoride in the formula of the test GIC might impart an increase in the mechanical properties of the GICs" @default.
- W2023382679 created "2016-06-24" @default.
- W2023382679 creator A5052687138 @default.
- W2023382679 creator A5072142524 @default.
- W2023382679 creator A5088021030 @default.
- W2023382679 date "2011-06-01" @default.
- W2023382679 modified "2023-10-16" @default.
- W2023382679 title "The Effect of Incorporating Lithium Fluoride on the Compressive Strength and Diametric Tensile Strength of Glass Ionomer Cement" @default.
- W2023382679 cites W1982355859 @default.
- W2023382679 cites W2019145433 @default.
- W2023382679 cites W2033055908 @default.
- W2023382679 cites W2044134927 @default.
- W2023382679 cites W2087538383 @default.
- W2023382679 cites W2106526531 @default.
- W2023382679 cites W2135173331 @default.
- W2023382679 cites W2162414259 @default.
- W2023382679 cites W220569438 @default.
- W2023382679 cites W2274360698 @default.
- W2023382679 doi "https://doi.org/10.4028/www.scientific.net/amr.264-265.508" @default.
- W2023382679 hasPublicationYear "2011" @default.
- W2023382679 type Work @default.
- W2023382679 sameAs 2023382679 @default.
- W2023382679 citedByCount "0" @default.
- W2023382679 crossrefType "journal-article" @default.
- W2023382679 hasAuthorship W2023382679A5052687138 @default.
- W2023382679 hasAuthorship W2023382679A5072142524 @default.
- W2023382679 hasAuthorship W2023382679A5088021030 @default.
- W2023382679 hasConcept C112950240 @default.
- W2023382679 hasConcept C159985019 @default.
- W2023382679 hasConcept C178405089 @default.
- W2023382679 hasConcept C180478085 @default.
- W2023382679 hasConcept C183300977 @default.
- W2023382679 hasConcept C192562407 @default.
- W2023382679 hasConcept C30407753 @default.
- W2023382679 hasConcept C51936186 @default.
- W2023382679 hasConcept C523993062 @default.
- W2023382679 hasConceptScore W2023382679C112950240 @default.
- W2023382679 hasConceptScore W2023382679C159985019 @default.
- W2023382679 hasConceptScore W2023382679C178405089 @default.
- W2023382679 hasConceptScore W2023382679C180478085 @default.
- W2023382679 hasConceptScore W2023382679C183300977 @default.
- W2023382679 hasConceptScore W2023382679C192562407 @default.
- W2023382679 hasConceptScore W2023382679C30407753 @default.
- W2023382679 hasConceptScore W2023382679C51936186 @default.
- W2023382679 hasConceptScore W2023382679C523993062 @default.
- W2023382679 hasLocation W20233826791 @default.
- W2023382679 hasOpenAccess W2023382679 @default.
- W2023382679 hasPrimaryLocation W20233826791 @default.
- W2023382679 hasRelatedWork W1834627117 @default.
- W2023382679 hasRelatedWork W2026544389 @default.
- W2023382679 hasRelatedWork W2038597610 @default.
- W2023382679 hasRelatedWork W2162414259 @default.
- W2023382679 hasRelatedWork W2409435685 @default.
- W2023382679 hasRelatedWork W2604340671 @default.
- W2023382679 hasRelatedWork W2992049753 @default.
- W2023382679 hasRelatedWork W4289546066 @default.
- W2023382679 hasRelatedWork W4312365986 @default.
- W2023382679 hasRelatedWork W66509821 @default.
- W2023382679 hasVolume "264-265" @default.
- W2023382679 isParatext "false" @default.
- W2023382679 isRetracted "false" @default.
- W2023382679 magId "2023382679" @default.
- W2023382679 workType "article" @default.