- W2023554212 abstract "Thermal cycle resistance of Ni-20Cr, Ni-50Cr and CoNiCrAlY coatings produced by air plasma spraying was investigated according to Japanese Industrial Standard Testing method for thermal cycle resistance of oxidation resistant metallic coatings (JIS H 8452 : 2008) . The specimens were exposed to a cyclic heating and cooling regimen comprised of up to 100 cycles of 10 hours heating to 1000 °C or 1093 °C in air followed by cooling. The thermal cycle resistance of oxidation-resistant metallic coatings was found to depend strongly on testing temperature and on the chemical composition of the coating materials. In thermal cycle testing at 1000 °C, no remarkable failure was observed in any specimen. However, in thermal cycle testing at 1093 °C, spalling was observed over the entire surface of the Ni-20Cr coating, although the Ni-50Cr and the CoNiCrAlY coatings exhibited excellent thermal cycle resistance even upon exposure to 100 thermal cycles. The CoNiCrAlY coating showed mass gain with increasing number of thermal cycles due to preferential oxidation between thermal spray particle splats. Furthermore, the failure behavior of specimens was investigated in detail by SEM, XRD, EPMA, etc." @default.
- W2023554212 created "2016-06-24" @default.
- W2023554212 creator A5005892180 @default.
- W2023554212 creator A5056869298 @default.
- W2023554212 creator A5066636464 @default.
- W2023554212 creator A5075162103 @default.
- W2023554212 creator A5075413955 @default.
- W2023554212 creator A5091439639 @default.
- W2023554212 date "2011-09-01" @default.
- W2023554212 modified "2023-09-25" @default.
- W2023554212 title "Thermal Cycle Properties of Plasma Sprayed Oxidation-Resistant Metallic Coatings" @default.
- W2023554212 cites W1986308974 @default.
- W2023554212 cites W2011238821 @default.
- W2023554212 cites W2022125619 @default.
- W2023554212 cites W2033363923 @default.
- W2023554212 cites W2081220697 @default.
- W2023554212 doi "https://doi.org/10.4028/www.scientific.net/msf.696.296" @default.
- W2023554212 hasPublicationYear "2011" @default.
- W2023554212 type Work @default.
- W2023554212 sameAs 2023554212 @default.
- W2023554212 citedByCount "0" @default.
- W2023554212 crossrefType "journal-article" @default.
- W2023554212 hasAuthorship W2023554212A5005892180 @default.
- W2023554212 hasAuthorship W2023554212A5056869298 @default.
- W2023554212 hasAuthorship W2023554212A5066636464 @default.
- W2023554212 hasAuthorship W2023554212A5075162103 @default.
- W2023554212 hasAuthorship W2023554212A5075413955 @default.
- W2023554212 hasAuthorship W2023554212A5091439639 @default.
- W2023554212 hasConcept C121332964 @default.
- W2023554212 hasConcept C137693562 @default.
- W2023554212 hasConcept C149669645 @default.
- W2023554212 hasConcept C159985019 @default.
- W2023554212 hasConcept C176711861 @default.
- W2023554212 hasConcept C191897082 @default.
- W2023554212 hasConcept C192562407 @default.
- W2023554212 hasConcept C204530211 @default.
- W2023554212 hasConcept C2781448156 @default.
- W2023554212 hasConcept C544153396 @default.
- W2023554212 hasConcept C62520636 @default.
- W2023554212 hasConcept C82706917 @default.
- W2023554212 hasConcept C97355855 @default.
- W2023554212 hasConceptScore W2023554212C121332964 @default.
- W2023554212 hasConceptScore W2023554212C137693562 @default.
- W2023554212 hasConceptScore W2023554212C149669645 @default.
- W2023554212 hasConceptScore W2023554212C159985019 @default.
- W2023554212 hasConceptScore W2023554212C176711861 @default.
- W2023554212 hasConceptScore W2023554212C191897082 @default.
- W2023554212 hasConceptScore W2023554212C192562407 @default.
- W2023554212 hasConceptScore W2023554212C204530211 @default.
- W2023554212 hasConceptScore W2023554212C2781448156 @default.
- W2023554212 hasConceptScore W2023554212C544153396 @default.
- W2023554212 hasConceptScore W2023554212C62520636 @default.
- W2023554212 hasConceptScore W2023554212C82706917 @default.
- W2023554212 hasConceptScore W2023554212C97355855 @default.
- W2023554212 hasLocation W20235542121 @default.
- W2023554212 hasOpenAccess W2023554212 @default.
- W2023554212 hasPrimaryLocation W20235542121 @default.
- W2023554212 hasRelatedWork W1572483098 @default.
- W2023554212 hasRelatedWork W1590606937 @default.
- W2023554212 hasRelatedWork W1967259796 @default.
- W2023554212 hasRelatedWork W1968044470 @default.
- W2023554212 hasRelatedWork W1992690972 @default.
- W2023554212 hasRelatedWork W2034574826 @default.
- W2023554212 hasRelatedWork W2044122069 @default.
- W2023554212 hasRelatedWork W2052805457 @default.
- W2023554212 hasRelatedWork W2054461631 @default.
- W2023554212 hasRelatedWork W2064415287 @default.
- W2023554212 hasRelatedWork W2094207832 @default.
- W2023554212 hasRelatedWork W2165363138 @default.
- W2023554212 hasRelatedWork W2171311740 @default.
- W2023554212 hasRelatedWork W2287540705 @default.
- W2023554212 hasRelatedWork W2378959514 @default.
- W2023554212 hasRelatedWork W2584135263 @default.
- W2023554212 hasRelatedWork W2969253862 @default.
- W2023554212 hasRelatedWork W3206505414 @default.
- W2023554212 hasRelatedWork W364317979 @default.
- W2023554212 hasRelatedWork W757770755 @default.
- W2023554212 isParatext "false" @default.
- W2023554212 isRetracted "false" @default.
- W2023554212 magId "2023554212" @default.
- W2023554212 workType "article" @default.