- W2023682404 abstract "The interfacial microstructures characteristics of alumina ceramic body reinforced with yttria stabilized zirconia (YSZ) was evaluated after friction welding to 6061 aluminum alloy using optical and electron microscopy. Alumina rods containing 25 and 50 wt% yttria stabilized zirconia were fabricated by slip casting in plaster of Paris (POP) molds and subsequently sintered at 1600 °C. On the other hand, aluminum rods were machine down to the required dimension using a lathe machine. The diameter of the ceramic and the metal rods was 16 mm. Rotational speeds for the friction welding were varied between 900 and 1800 rpm. The friction pressure was maintained at 7 MPa for a friction time of 30 s. Optical and scanning electron microscopy was used to analyze the microstructure of the resultant joints, particularly at the interface. The joints were also examined with EDX line (energy dispersive X-ray) in order to determine the phases formed during the welding. The mechanical properties of the friction welded YSZ–Al2O3 composite to 6061 alloy were determined with a four-point bend test and Vickers microhardness. The experimental results showed the degree of deformation varied significantly for the 6061 Al alloy than the ceramic composite part. The mechanical strength of friction-welded ceramic composite/6061 Al alloy components were obviously affected by joining rotational speed selected which decreases in strength with increasing rotational speed." @default.
- W2023682404 created "2016-06-24" @default.
- W2023682404 creator A5025621549 @default.
- W2023682404 creator A5030422863 @default.
- W2023682404 creator A5037268423 @default.
- W2023682404 creator A5043042122 @default.
- W2023682404 date "2011-01-01" @default.
- W2023682404 modified "2023-10-14" @default.
- W2023682404 title "Evaluation of interfacial bonding in dissimilar materials of YSZ–alumina composites to 6061 aluminium alloy using friction welding" @default.
- W2023682404 cites W1976244151 @default.
- W2023682404 cites W1981519203 @default.
- W2023682404 cites W1991960991 @default.
- W2023682404 cites W1995225386 @default.
- W2023682404 cites W2000648936 @default.
- W2023682404 cites W2004838763 @default.
- W2023682404 cites W2009393444 @default.
- W2023682404 cites W2014652708 @default.
- W2023682404 cites W2017441614 @default.
- W2023682404 cites W2048574673 @default.
- W2023682404 cites W2049195899 @default.
- W2023682404 cites W2049368133 @default.
- W2023682404 cites W2058834591 @default.
- W2023682404 cites W2066910041 @default.
- W2023682404 cites W2086854022 @default.
- W2023682404 cites W2102061140 @default.
- W2023682404 cites W2126855515 @default.
- W2023682404 doi "https://doi.org/10.1016/j.msea.2010.10.060" @default.
- W2023682404 hasPublicationYear "2011" @default.
- W2023682404 type Work @default.
- W2023682404 sameAs 2023682404 @default.
- W2023682404 citedByCount "18" @default.
- W2023682404 countsByYear W20236824042012 @default.
- W2023682404 countsByYear W20236824042013 @default.
- W2023682404 countsByYear W20236824042014 @default.
- W2023682404 countsByYear W20236824042015 @default.
- W2023682404 countsByYear W20236824042017 @default.
- W2023682404 countsByYear W20236824042018 @default.
- W2023682404 countsByYear W20236824042019 @default.
- W2023682404 countsByYear W20236824042020 @default.
- W2023682404 countsByYear W20236824042021 @default.
- W2023682404 crossrefType "journal-article" @default.
- W2023682404 hasAuthorship W2023682404A5025621549 @default.
- W2023682404 hasAuthorship W2023682404A5030422863 @default.
- W2023682404 hasAuthorship W2023682404A5037268423 @default.
- W2023682404 hasAuthorship W2023682404A5043042122 @default.
- W2023682404 hasConcept C104779481 @default.
- W2023682404 hasConcept C123609680 @default.
- W2023682404 hasConcept C133392424 @default.
- W2023682404 hasConcept C134132462 @default.
- W2023682404 hasConcept C159985019 @default.
- W2023682404 hasConcept C165720898 @default.
- W2023682404 hasConcept C191897082 @default.
- W2023682404 hasConcept C192562407 @default.
- W2023682404 hasConcept C19474535 @default.
- W2023682404 hasConcept C26771246 @default.
- W2023682404 hasConcept C2780026712 @default.
- W2023682404 hasConcept C87976508 @default.
- W2023682404 hasConcept C96410337 @default.
- W2023682404 hasConceptScore W2023682404C104779481 @default.
- W2023682404 hasConceptScore W2023682404C123609680 @default.
- W2023682404 hasConceptScore W2023682404C133392424 @default.
- W2023682404 hasConceptScore W2023682404C134132462 @default.
- W2023682404 hasConceptScore W2023682404C159985019 @default.
- W2023682404 hasConceptScore W2023682404C165720898 @default.
- W2023682404 hasConceptScore W2023682404C191897082 @default.
- W2023682404 hasConceptScore W2023682404C192562407 @default.
- W2023682404 hasConceptScore W2023682404C19474535 @default.
- W2023682404 hasConceptScore W2023682404C26771246 @default.
- W2023682404 hasConceptScore W2023682404C2780026712 @default.
- W2023682404 hasConceptScore W2023682404C87976508 @default.
- W2023682404 hasConceptScore W2023682404C96410337 @default.
- W2023682404 hasIssue "3" @default.
- W2023682404 hasLocation W20236824041 @default.
- W2023682404 hasOpenAccess W2023682404 @default.
- W2023682404 hasPrimaryLocation W20236824041 @default.
- W2023682404 hasRelatedWork W1984931024 @default.
- W2023682404 hasRelatedWork W1990574691 @default.
- W2023682404 hasRelatedWork W2001108138 @default.
- W2023682404 hasRelatedWork W2038621919 @default.
- W2023682404 hasRelatedWork W2068113961 @default.
- W2023682404 hasRelatedWork W2076087596 @default.
- W2023682404 hasRelatedWork W2378060932 @default.
- W2023682404 hasRelatedWork W2379855728 @default.
- W2023682404 hasRelatedWork W2980884952 @default.
- W2023682404 hasRelatedWork W3033525047 @default.
- W2023682404 hasVolume "528" @default.
- W2023682404 isParatext "false" @default.
- W2023682404 isRetracted "false" @default.
- W2023682404 magId "2023682404" @default.
- W2023682404 workType "article" @default.