- W2024097118 abstract "Electrical and optical activation studies of AlxGa1−xN (x = 0.11 and 0.21) implanted with silicon were made as a function of ion dose and anneal temperature. Silicon ions were implanted at 200 keV with doses ranging from 1 × 1014 to 1 × 1015 cm−2 at room temperature. The implanted samples were subsequently annealed from 1100 to 1300 °C for 20 min in a nitrogen environment. A maximum electrical activation efficiency of 91% was obtained for the Al0.11Ga0.89N implanted with the highest dose of 1 × 1015 cm−2 even after annealing at 1150 °C. 100% activation efficiencies were successfully obtained for the Al0.21Ga0.79N samples after annealing at 1300 °C for both doses of 5 × 1014 and 1 × 1015 cm−2. The mobility of the Si-implanted AlxGa1−xN increases with annealing temperature, and the highest mobilities are 109 and 98 cm2/V·s for Al0.11Ga0.89N and Al0.21Ga0.79N, respectively. The cathodoluminescence (CL) spectra for all the samples exhibited a sharp neutral-donor-bound exciton peak, and the CL intensity increases with annealing temperature, indicating successive improved implantation damage recovery as the annealing temperature is increased. These results provide the optimum annealing conditions for activation of implanted Si ions in AlxGa1−xN." @default.
- W2024097118 created "2016-06-24" @default.
- W2024097118 creator A5011297444 @default.
- W2024097118 creator A5079648521 @default.
- W2024097118 creator A5079719778 @default.
- W2024097118 date "2012-01-01" @default.
- W2024097118 modified "2023-09-27" @default.
- W2024097118 title "Ion dose and anneal temperature dependent studies of silicon implanted AlxGa1−xN" @default.
- W2024097118 cites W1538171360 @default.
- W2024097118 cites W1964495850 @default.
- W2024097118 cites W1964716706 @default.
- W2024097118 cites W1965455292 @default.
- W2024097118 cites W1986774761 @default.
- W2024097118 cites W2000606566 @default.
- W2024097118 cites W2011483233 @default.
- W2024097118 cites W2032944145 @default.
- W2024097118 cites W2038936151 @default.
- W2024097118 cites W2052843275 @default.
- W2024097118 cites W2066926441 @default.
- W2024097118 cites W2069363052 @default.
- W2024097118 cites W2078026392 @default.
- W2024097118 cites W2081002835 @default.
- W2024097118 cites W2082032560 @default.
- W2024097118 cites W2083742862 @default.
- W2024097118 cites W2142435489 @default.
- W2024097118 cites W2162857337 @default.
- W2024097118 cites W1669846460 @default.
- W2024097118 doi "https://doi.org/10.1016/j.cap.2011.05.007" @default.
- W2024097118 hasPublicationYear "2012" @default.
- W2024097118 type Work @default.
- W2024097118 sameAs 2024097118 @default.
- W2024097118 citedByCount "3" @default.
- W2024097118 countsByYear W20240971182016 @default.
- W2024097118 countsByYear W20240971182020 @default.
- W2024097118 countsByYear W20240971182023 @default.
- W2024097118 crossrefType "journal-article" @default.
- W2024097118 hasAuthorship W2024097118A5011297444 @default.
- W2024097118 hasAuthorship W2024097118A5079648521 @default.
- W2024097118 hasAuthorship W2024097118A5079719778 @default.
- W2024097118 hasConcept C113196181 @default.
- W2024097118 hasConcept C139861200 @default.
- W2024097118 hasConcept C145148216 @default.
- W2024097118 hasConcept C148869448 @default.
- W2024097118 hasConcept C177322064 @default.
- W2024097118 hasConcept C178790620 @default.
- W2024097118 hasConcept C185592680 @default.
- W2024097118 hasConcept C191897082 @default.
- W2024097118 hasConcept C192562407 @default.
- W2024097118 hasConcept C2777855556 @default.
- W2024097118 hasConcept C41823505 @default.
- W2024097118 hasConcept C43617362 @default.
- W2024097118 hasConcept C49040817 @default.
- W2024097118 hasConcept C544956773 @default.
- W2024097118 hasConceptScore W2024097118C113196181 @default.
- W2024097118 hasConceptScore W2024097118C139861200 @default.
- W2024097118 hasConceptScore W2024097118C145148216 @default.
- W2024097118 hasConceptScore W2024097118C148869448 @default.
- W2024097118 hasConceptScore W2024097118C177322064 @default.
- W2024097118 hasConceptScore W2024097118C178790620 @default.
- W2024097118 hasConceptScore W2024097118C185592680 @default.
- W2024097118 hasConceptScore W2024097118C191897082 @default.
- W2024097118 hasConceptScore W2024097118C192562407 @default.
- W2024097118 hasConceptScore W2024097118C2777855556 @default.
- W2024097118 hasConceptScore W2024097118C41823505 @default.
- W2024097118 hasConceptScore W2024097118C43617362 @default.
- W2024097118 hasConceptScore W2024097118C49040817 @default.
- W2024097118 hasConceptScore W2024097118C544956773 @default.
- W2024097118 hasFunder F4320322120 @default.
- W2024097118 hasFunder F4320322349 @default.
- W2024097118 hasFunder F4320338279 @default.
- W2024097118 hasIssue "1" @default.
- W2024097118 hasLocation W20240971181 @default.
- W2024097118 hasOpenAccess W2024097118 @default.
- W2024097118 hasPrimaryLocation W20240971181 @default.
- W2024097118 hasRelatedWork W1616992653 @default.
- W2024097118 hasRelatedWork W2024097118 @default.
- W2024097118 hasRelatedWork W2042925312 @default.
- W2024097118 hasRelatedWork W2053243913 @default.
- W2024097118 hasRelatedWork W2060214064 @default.
- W2024097118 hasRelatedWork W2065669148 @default.
- W2024097118 hasRelatedWork W2071047578 @default.
- W2024097118 hasRelatedWork W2088081281 @default.
- W2024097118 hasRelatedWork W2094221410 @default.
- W2024097118 hasRelatedWork W2977855466 @default.
- W2024097118 hasVolume "12" @default.
- W2024097118 isParatext "false" @default.
- W2024097118 isRetracted "false" @default.
- W2024097118 magId "2024097118" @default.
- W2024097118 workType "article" @default.